Taishan jade porcelain and preparation method thereof
The invention discloses Taishan jade porcelain. A formula of the Taishan jade porcelain comprises the following components: 28%-35% of Taishan jade powder, 8%-15% of kaolin, 5%-10% of potassium feldspar, 7%-12% of quartz, 2%-5% of magnesium oxide, 3%-6% of lithium fluoride, 5%-9% of zinc sulfide nano powder and the balance being yttrium oxide. The invention also discloses a preparation method of the Taishan jade porcelain. The preparation method comprises the following steps: quantitatively weighing, preparing blank slurry, preheating the blank slurry, preparing a plain blank, demolding, calcining and carrying out surface treatment. The Taishan jade porcelain has the beneficial effects that the national jade porcelain is produced by utilizing the characteristics of Taishan jade, the firingtemperature range is wide, and the firing operation is easy; the sintered porcelain body is jade and has good transparency, high mechanical strength and good thermal stability; the invention also provides the preparation method of the Taishan jade porcelain, wherein the preparation method is scientific, reasonable and easy to implement, ensures the product quality and qualification rate, reducesthe potential safety hazard caused by cracking, severe deformation and the like in the subsequent use, and enhances the use safety and reliability.
本发明公开了泰山玉瓷，该泰山玉瓷的配方包括以下组份：泰山玉石粉28％—35％、高岭土8％—15％、钾长石5％—10％、石英7％—12％、氧化镁2％—5％、氟化锂3％—6％，硫化锌纳米粉末5％—9％，其余为氧化钇；本发明还公开了泰山玉瓷的制备方法，该制备方法包括以下步骤：定量称取，制备坯浆，坯浆预热，制备素胚，脱模，煅烧，表面处理；本发明的有益效果是：本发明的目的在于利用泰山玉的特性，生产一种国玉瓷，烧成温度范围宽，容易烧成操作；烧结后瓷胎呈一种玉质，透明度好，机械强度高、热稳定性好；本发明同时提供了其制备方法，科学合理，容易实施，保证了产品质量和合格率，降低了后续使用中因开裂、变形剧烈等造成的安全隐患，提高了使用的安全性及可靠性。
Taishan jade porcelain and preparation method thereof
The invention discloses Taishan jade porcelain. A formula of the Taishan jade porcelain comprises the following components: 28%-35% of Taishan jade powder, 8%-15% of kaolin, 5%-10% of potassium feldspar, 7%-12% of quartz, 2%-5% of magnesium oxide, 3%-6% of lithium fluoride, 5%-9% of zinc sulfide nano powder and the balance being yttrium oxide. The invention also discloses a preparation method of the Taishan jade porcelain. The preparation method comprises the following steps: quantitatively weighing, preparing blank slurry, preheating the blank slurry, preparing a plain blank, demolding, calcining and carrying out surface treatment. The Taishan jade porcelain has the beneficial effects that the national jade porcelain is produced by utilizing the characteristics of Taishan jade, the firingtemperature range is wide, and the firing operation is easy; the sintered porcelain body is jade and has good transparency, high mechanical strength and good thermal stability; the invention also provides the preparation method of the Taishan jade porcelain, wherein the preparation method is scientific, reasonable and easy to implement, ensures the product quality and qualification rate, reducesthe potential safety hazard caused by cracking, severe deformation and the like in the subsequent use, and enhances the use safety and reliability.
本发明公开了泰山玉瓷，该泰山玉瓷的配方包括以下组份：泰山玉石粉28％—35％、高岭土8％—15％、钾长石5％—10％、石英7％—12％、氧化镁2％—5％、氟化锂3％—6％，硫化锌纳米粉末5％—9％，其余为氧化钇；本发明还公开了泰山玉瓷的制备方法，该制备方法包括以下步骤：定量称取，制备坯浆，坯浆预热，制备素胚，脱模，煅烧，表面处理；本发明的有益效果是：本发明的目的在于利用泰山玉的特性，生产一种国玉瓷，烧成温度范围宽，容易烧成操作；烧结后瓷胎呈一种玉质，透明度好，机械强度高、热稳定性好；本发明同时提供了其制备方法，科学合理，容易实施，保证了产品质量和合格率，降低了后续使用中因开裂、变形剧烈等造成的安全隐患，提高了使用的安全性及可靠性。
Taishan jade porcelain and preparation method thereof
泰山玉瓷及其制备方法
LU DEGUO (author) / ZHANG GUANGWEN (author)
2020-08-07
Patent
Electronic Resource
Chinese