The invention belongs to the technical field of Taishan jade preparation processes, and relates to a Taishan jade pottery manufacturing method. The Taishan jade is ground into powder, the powder is mixed with argil according to the proportion of 15: 85-35: 65, glazing is not carried out, and firing is carried out at the low temperature of 900 DEG C. According to the teacup and teapot manufactured through the technology, the problem that the Taishan jade cracks is solved, and due to the fact that original mineral components of the Taishan jade are kept to the maximum degree through the technology, a human body can absorb beneficial microelements easily. The cracking problem is avoided by utilizing the viscosity of the pottery clay, mineral substances of the Taishan jade can be retained, the processing difficulty is reduced, the yield is improved, and the practical safety is ensured.
本发明属于泰山玉制备工艺技术领域，涉及一种泰山玉陶器制作方法。将泰山玉石打磨成粉末，按15:85‑35:65的比例与陶土混合，不上釉，900度低温烧制，采用该工艺制成的茶杯、茶壶，解决了上述泰山玉石开裂问题，且因工艺最大程度保持了泰山玉石的原有矿物成分，有利于人体吸收有益微量元素。本发明利用陶土的黏性来规避开裂问题，又能够保留泰山玉石的矿物质，降低加工难度，提高成品率，保证了实用的安全。
The invention belongs to the technical field of Taishan jade preparation processes, and relates to a Taishan jade pottery manufacturing method. The Taishan jade is ground into powder, the powder is mixed with argil according to the proportion of 15: 85-35: 65, glazing is not carried out, and firing is carried out at the low temperature of 900 DEG C. According to the teacup and teapot manufactured through the technology, the problem that the Taishan jade cracks is solved, and due to the fact that original mineral components of the Taishan jade are kept to the maximum degree through the technology, a human body can absorb beneficial microelements easily. The cracking problem is avoided by utilizing the viscosity of the pottery clay, mineral substances of the Taishan jade can be retained, the processing difficulty is reduced, the yield is improved, and the practical safety is ensured.
本发明属于泰山玉制备工艺技术领域，涉及一种泰山玉陶器制作方法。将泰山玉石打磨成粉末，按15:85‑35:65的比例与陶土混合，不上釉，900度低温烧制，采用该工艺制成的茶杯、茶壶，解决了上述泰山玉石开裂问题，且因工艺最大程度保持了泰山玉石的原有矿物成分，有利于人体吸收有益微量元素。本发明利用陶土的黏性来规避开裂问题，又能够保留泰山玉石的矿物质，降低加工难度，提高成品率，保证了实用的安全。