The invention relates to the field of ceramic glaze and the field of ceramic processes, in particular to a wood grain glaze, a wood grain glaze ceramic and a preparation method thereof. The wood grainglaze is prepared from the following components by weight: 18-30 parts of albite, 10-18 parts of quartz, 12-25 parts of calcite, 8-15 parts of zinc oxide, 8-15 parts of aluminum oxide, 5-12 parts oftitanium dioxide, 10-20 parts of wollastonite and 1-5 parts of ferrozirconium red. The wollastonite, ferrozirconium red, titanium dioxide and other raw materials are mutually matched according to a certain proportion, by means of specific tool operation, firing is conducted under specific conditions to present the characteristics of a plain wood grain board, colored and diversified ceramics can beobtained, and unique artistry is achieved, meanwhile, the ceramic glaze surface has good wear resistance and stain resistance, and the dissolution rates of lead and cadmium can both reach the international standard.
本发明涉及陶瓷釉料领域及陶瓷工艺领域，具体涉及一种木纹釉、木纹釉陶瓷及其制备方法。所述木纹釉的釉料组分及各组分的重量分数为：钠长石18‑30份，石英10‑18份，方解石12‑25份，氧化锌8‑15份，氧化铝8‑15份，二氧化钛5‑12份，硅灰石10‑20份，锆铁红1‑5份。本申请通过硅灰石、锆铁红、二氧化钛等原料按照一定比例互配，通过特定的工具操作，并在特定的条件下进行烧制呈现素色木纹板的特性，获得了色彩多样化的陶瓷，具有独特的艺术性，同时陶瓷釉面具有良好的耐磨性、耐污性，且铅镉溶出度均可达到国际标准。
The invention relates to the field of ceramic glaze and the field of ceramic processes, in particular to a wood grain glaze, a wood grain glaze ceramic and a preparation method thereof. The wood grainglaze is prepared from the following components by weight: 18-30 parts of albite, 10-18 parts of quartz, 12-25 parts of calcite, 8-15 parts of zinc oxide, 8-15 parts of aluminum oxide, 5-12 parts oftitanium dioxide, 10-20 parts of wollastonite and 1-5 parts of ferrozirconium red. The wollastonite, ferrozirconium red, titanium dioxide and other raw materials are mutually matched according to a certain proportion, by means of specific tool operation, firing is conducted under specific conditions to present the characteristics of a plain wood grain board, colored and diversified ceramics can beobtained, and unique artistry is achieved, meanwhile, the ceramic glaze surface has good wear resistance and stain resistance, and the dissolution rates of lead and cadmium can both reach the international standard.
本发明涉及陶瓷釉料领域及陶瓷工艺领域，具体涉及一种木纹釉、木纹釉陶瓷及其制备方法。所述木纹釉的釉料组分及各组分的重量分数为：钠长石18‑30份，石英10‑18份，方解石12‑25份，氧化锌8‑15份，氧化铝8‑15份，二氧化钛5‑12份，硅灰石10‑20份，锆铁红1‑5份。本申请通过硅灰石、锆铁红、二氧化钛等原料按照一定比例互配，通过特定的工具操作，并在特定的条件下进行烧制呈现素色木纹板的特性，获得了色彩多样化的陶瓷，具有独特的艺术性，同时陶瓷釉面具有良好的耐磨性、耐污性，且铅镉溶出度均可达到国际标准。
Wood grain glaze, wood grain glaze ceramic and preparation method thereof
木纹釉、木纹釉陶瓷及其制备方法
LING MING (author)
2020-09-08
Patent
Electronic Resource
Chinese
| European Patent Office | 2021
| European Patent Office | 2023
Natural-imitated glaze-filled wood grain brick and preparation process thereof
| European Patent Office | 2023