Refractory material for ladle slag entrapment prevention, ladle slag entrapment prevention product and preparation method of ladle slag entrapment prevention product
The invention discloses a refractory material for ladle slag entrapment prevention. The refractory material comprises the following chemical components in percentage by mass: 30-40% of corundum, 30%-40% of alumina, 3%-8% of fused magnesia, 10%-20% of magnesium aluminate spinel, 5%-10% of andalusite, 1.5%-4% of alpha-Al2O3 micro powder, 0.25%-2.5% of SiO2 micro powder, 5%-10% of beta-sialon, 1%-3%of desilicated zirconium fine powder, and 1%-3% of aluminate cement. The invention further discloses a steel ladle slag entrapment prevention product and a preparation method thereof. The steel ladleslag entrapment prevention product is good in slag corrosion resistance, the high-temperature breaking strength is high, the breaking strength of the refractory brick is 10MPa-15MPa at 110 DEG C after24h, the breaking strength of the refractory brick is 25MPa-50MPa after 1550 DEG C*3h high-temperature firing, the breaking strength of the refractory brick is 6MPa-10MPa at a high temperature of 1400 DEG C, the refractoriness of the refractory brick is greater than 1700 DEG C, and the actual service life of the refractory brick is greater than 30 furnaces.
本发明公开了一种钢包防卷渣用耐火材料,化学成分质量分数包括:刚玉30%~40%;矾土30%~40%;电熔镁砂3%~8%;镁铝尖晶石10%~20%;红柱石5%~10%;α‑AlO微粉1.5%~4%;SiO微粉0.25%~2.5%;β‑sialon 5%~10%;脱硅锆细粉1%~3%;铝酸盐水泥1%~3%。本发明还公开了钢包防卷渣制品及其制备方法,抗熔渣侵蚀性能好;高温抗折强度高:其110℃×24h抗折强度为10MPa~15MPa,1550℃×3h高温烧制后抗折强度为25MPa~50MPa,1400℃高温抗折强度为6MPa~10MPa,耐火度大于1700℃,实际使用寿命大于30炉。
Refractory material for ladle slag entrapment prevention, ladle slag entrapment prevention product and preparation method of ladle slag entrapment prevention product
The invention discloses a refractory material for ladle slag entrapment prevention. The refractory material comprises the following chemical components in percentage by mass: 30-40% of corundum, 30%-40% of alumina, 3%-8% of fused magnesia, 10%-20% of magnesium aluminate spinel, 5%-10% of andalusite, 1.5%-4% of alpha-Al2O3 micro powder, 0.25%-2.5% of SiO2 micro powder, 5%-10% of beta-sialon, 1%-3%of desilicated zirconium fine powder, and 1%-3% of aluminate cement. The invention further discloses a steel ladle slag entrapment prevention product and a preparation method thereof. The steel ladleslag entrapment prevention product is good in slag corrosion resistance, the high-temperature breaking strength is high, the breaking strength of the refractory brick is 10MPa-15MPa at 110 DEG C after24h, the breaking strength of the refractory brick is 25MPa-50MPa after 1550 DEG C*3h high-temperature firing, the breaking strength of the refractory brick is 6MPa-10MPa at a high temperature of 1400 DEG C, the refractoriness of the refractory brick is greater than 1700 DEG C, and the actual service life of the refractory brick is greater than 30 furnaces.
本发明公开了一种钢包防卷渣用耐火材料,化学成分质量分数包括:刚玉30%~40%;矾土30%~40%;电熔镁砂3%~8%;镁铝尖晶石10%~20%;红柱石5%~10%;α‑AlO微粉1.5%~4%;SiO微粉0.25%~2.5%;β‑sialon 5%~10%;脱硅锆细粉1%~3%;铝酸盐水泥1%~3%。本发明还公开了钢包防卷渣制品及其制备方法,抗熔渣侵蚀性能好;高温抗折强度高:其110℃×24h抗折强度为10MPa~15MPa,1550℃×3h高温烧制后抗折强度为25MPa~50MPa,1400℃高温抗折强度为6MPa~10MPa,耐火度大于1700℃,实际使用寿命大于30炉。
Refractory material for ladle slag entrapment prevention, ladle slag entrapment prevention product and preparation method of ladle slag entrapment prevention product
一种钢包防卷渣用耐火材料、钢包防卷渣制品及其制备方法
LIU MENG (author) / YE TUMING (author) / TANG SHUPING (author) / ZOU LONG (author) / ZHOU WANGZHI (author)
2020-09-08
Patent
Electronic Resource
Chinese