Preparation method of high-temperature manganese red ceramic glaze and application of glaze
The invention discloses a manufacturing method of high-temperature manganese red ceramic glaze and application of the glaze, and relates to the technical field of ceramic product manufacturing glazes,and the method comprises the following steps: finely grinding 5-15 parts by weight of aluminum hydroxide and 3-8 parts by weight of manganese carbonate into dry powder by using a dry grinder in advance; then adding 1-5 parts by weight of diammonium hydrogen phosphate into the dry powder, uniformly mixing to prepare a mixed material, loading the mixed material into refractory saggers, stacking therefractory saggers on a kiln car, and pushing the kiln car into a shuttle kiln for calcining; classifying and screening rare earth tailings, feldspar, quartz, talc, dolomite, marble and kaolin, removing impurities and crushing for later use; taking the impurity-removed and crushed raw materials obtained in the step 2 according to the following parts by weight for burdening; finely grinding the prepared materials through a wet ball milling process, sieving, and aging to obtain the product. During high-temperature calcination in a reducing atmosphere, the glaze of the ceramic product is brightand smooth and is pink, light red or purple red, and the ceramic product is dark and pink during high-temperature calcination in a weak reducing atmosphere.
一种高温锰红陶瓷釉料的制作方法及该釉料的应用，本发明涉及陶瓷制品制造釉料技术领域，预先用干式粉碎机将5‑15重量份的氢氧化铝和3‑8重量份的碳酸锰细磨加工制成干粉料；然后将1‑5重量份的磷酸氢二安加入干粉料中混合均匀制成混合物料，装入耐火匣钵，码放在窑车上，推入梭式窑锻烧；将稀土尾矿、长石、石英、滑石、白云石、大理石、高岭土分类筛选，除去杂质并粉碎备用；按照如下重量份取步骤二中得到的去除杂质并粉碎后的原料进行配料；将配好的料通过湿法球磨工艺细磨、过筛、陈腐工序后即得。在还原气氛高温煅烧时，陶瓷制品釉面鲜艳润滑、颜色呈粉红色、淡红色或紫红色，弱还原气氛高温烧成时颜色较深、呈桃红色。
Preparation method of high-temperature manganese red ceramic glaze and application of glaze
The invention discloses a manufacturing method of high-temperature manganese red ceramic glaze and application of the glaze, and relates to the technical field of ceramic product manufacturing glazes,and the method comprises the following steps: finely grinding 5-15 parts by weight of aluminum hydroxide and 3-8 parts by weight of manganese carbonate into dry powder by using a dry grinder in advance; then adding 1-5 parts by weight of diammonium hydrogen phosphate into the dry powder, uniformly mixing to prepare a mixed material, loading the mixed material into refractory saggers, stacking therefractory saggers on a kiln car, and pushing the kiln car into a shuttle kiln for calcining; classifying and screening rare earth tailings, feldspar, quartz, talc, dolomite, marble and kaolin, removing impurities and crushing for later use; taking the impurity-removed and crushed raw materials obtained in the step 2 according to the following parts by weight for burdening; finely grinding the prepared materials through a wet ball milling process, sieving, and aging to obtain the product. During high-temperature calcination in a reducing atmosphere, the glaze of the ceramic product is brightand smooth and is pink, light red or purple red, and the ceramic product is dark and pink during high-temperature calcination in a weak reducing atmosphere.
一种高温锰红陶瓷釉料的制作方法及该釉料的应用，本发明涉及陶瓷制品制造釉料技术领域，预先用干式粉碎机将5‑15重量份的氢氧化铝和3‑8重量份的碳酸锰细磨加工制成干粉料；然后将1‑5重量份的磷酸氢二安加入干粉料中混合均匀制成混合物料，装入耐火匣钵，码放在窑车上，推入梭式窑锻烧；将稀土尾矿、长石、石英、滑石、白云石、大理石、高岭土分类筛选，除去杂质并粉碎备用；按照如下重量份取步骤二中得到的去除杂质并粉碎后的原料进行配料；将配好的料通过湿法球磨工艺细磨、过筛、陈腐工序后即得。在还原气氛高温煅烧时，陶瓷制品釉面鲜艳润滑、颜色呈粉红色、淡红色或紫红色，弱还原气氛高温烧成时颜色较深、呈桃红色。
Preparation method of high-temperature manganese red ceramic glaze and application of glaze
一种高温锰红陶瓷釉料的制作方法及该釉料的应用
GUO ZHISHAN (author) / GUO ZHIFENG (author) / HUANG LIJUN (author) / YANG YUNSHAN (author) / GUO ZHIPENG (author)
2020-09-11
Patent
Electronic Resource
Chinese
Glaze used for medium-temperature ceramic product and ceramic preparation method applying glaze
| European Patent Office | 2015
| European Patent Office | 2023
| European Patent Office | 2023