Anti-cracking ceramic glaze water and preparation method thereof
The invention discloses anti-cracking ceramic glaze water and a preparation method thereof, the anti-cracking ceramic glaze water comprises the following raw materials by weight: 15 parts of albite, 8parts of potassium feldspar, 3 parts of kaolin, 6 parts of quartz sand, 4 parts of zinc white, 3 parts of high alumina clay, 2 parts of boron carbide, 3 parts of niobium pentoxide, 2 parts of zinc oxide, and 12 parts of frit, and the preparation method comprises the following steps: S1, thoroughly crushing the raw materials through crushing equipment, and screening the crushed raw materials through a 250-mesh standard sieve to obtain a granular raw material A meeting requirements, so that the anti-cracking effect and hardness of the ceramic prepared from the ceramic glaze water provided by the invention can be greatly improved, the market requirements of higher hardness and anti-cracking property are met, a large number of bubbles are not generated on the glaze surface during firing, theproduct is high in antifouling capacity after being polished and relatively high in glossiness, meanwhile, the raw materials in the glaze are all common raw materials on the market. Therefore, the purchasing and processing cost can be greatly reduced, and the market prospect is good.
本发明公开了一种防裂陶瓷釉水及其制备方法，包括以下按照重量份计的原料：钠长石15份、钾长石8份、高岭土3份、石英砂6份、锌白4份、高铝粘土3份、碳化硼2份、五氧化二铌3份、氧化锌2份、熔块12份，包括以下步骤：S1、获取原材料，称取配方量的上述原料，然后将原料通过粉碎设备进行彻底粉碎，然后经过250目的标准筛，得到符合要求的颗粒原料A。本发明提供的陶瓷釉水制成的陶瓷防裂效果和硬度都能够大幅度提高，满足了更高硬度和防裂性的市场需求，釉面在烧制时不会产生大量的气泡，产品抛后防污能力强，其光泽度也较高，同时，釉料中的原料均为市面上常见的原料，因此能够极大降低采购及加工成本，具有良好的市场前景。
Anti-cracking ceramic glaze water and preparation method thereof
The invention discloses anti-cracking ceramic glaze water and a preparation method thereof, the anti-cracking ceramic glaze water comprises the following raw materials by weight: 15 parts of albite, 8parts of potassium feldspar, 3 parts of kaolin, 6 parts of quartz sand, 4 parts of zinc white, 3 parts of high alumina clay, 2 parts of boron carbide, 3 parts of niobium pentoxide, 2 parts of zinc oxide, and 12 parts of frit, and the preparation method comprises the following steps: S1, thoroughly crushing the raw materials through crushing equipment, and screening the crushed raw materials through a 250-mesh standard sieve to obtain a granular raw material A meeting requirements, so that the anti-cracking effect and hardness of the ceramic prepared from the ceramic glaze water provided by the invention can be greatly improved, the market requirements of higher hardness and anti-cracking property are met, a large number of bubbles are not generated on the glaze surface during firing, theproduct is high in antifouling capacity after being polished and relatively high in glossiness, meanwhile, the raw materials in the glaze are all common raw materials on the market. Therefore, the purchasing and processing cost can be greatly reduced, and the market prospect is good.
本发明公开了一种防裂陶瓷釉水及其制备方法，包括以下按照重量份计的原料：钠长石15份、钾长石8份、高岭土3份、石英砂6份、锌白4份、高铝粘土3份、碳化硼2份、五氧化二铌3份、氧化锌2份、熔块12份，包括以下步骤：S1、获取原材料，称取配方量的上述原料，然后将原料通过粉碎设备进行彻底粉碎，然后经过250目的标准筛，得到符合要求的颗粒原料A。本发明提供的陶瓷釉水制成的陶瓷防裂效果和硬度都能够大幅度提高，满足了更高硬度和防裂性的市场需求，釉面在烧制时不会产生大量的气泡，产品抛后防污能力强，其光泽度也较高，同时，釉料中的原料均为市面上常见的原料，因此能够极大降低采购及加工成本，具有良好的市场前景。
Anti-cracking ceramic glaze water and preparation method thereof
一种防裂陶瓷釉水及其制备方法
ZENG XINYU (author)
2021-01-12
Patent
Electronic Resource
Chinese
Ceramic glaze with non-cracking glaze surface and glazing method thereof
| European Patent Office | 2020
High-permeability anti-cracking celadon glaze formula and preparation method thereof
| European Patent Office | 2024
| European Patent Office | 2024
Cracked glaze, preparation method thereof and sanitary ceramic containing cracked glaze
| European Patent Office | 2024
Transmutation glaze, transmutation glaze laterite ceramic product and preparation method thereof
| European Patent Office | 2022