Method for preparing artificial white marble building material from refined manganese slag
The invention discloses a method for preparing an artificial white marble building material from refined manganese slag, and belongs to the field of building materials. The artificial white marble isprepared from the following raw materials in percentage by weight: 10-15% of refining slag powder, 40-45% of dolomite powder, 15-25% of quartz sand powder, 10-20% of stone powder, 5-15% of an adhesive, 1-2% of a curing agent, 0.03-0.07% of a toner and 0.01-0.03% of a compacting agent, and an artificial white marble product is formed after mold forming and curing. The method can effectively use theexisting manganese slag raw materials, reduce environmental pollution, and improve the use value of manganese slag. The building material with long service life and high additional value is provided,waste is turned into wealth, and the society is benefited.
一种利用精炼锰渣制备人造汉白玉建材的方法，属于建材领域。所述人造汉白玉各原料配比为，精炼渣粉10‑15%、白云石粉40‑45%、石英砂粉15‑25%、石粉10‑20%、粘合剂5‑15%、固化剂1‑2%、调色剂0.03‑0.07%、密实剂0.01‑0.03%，经模具成型、固化后，形成人造汉白玉产品，本发明可有效利用现存的锰渣原料，减少对环境的污染，提高锰渣的使用价值，提供寿命长且具有高附加值的建筑材料，变废为宝，造福社会。
Method for preparing artificial white marble building material from refined manganese slag
The invention discloses a method for preparing an artificial white marble building material from refined manganese slag, and belongs to the field of building materials. The artificial white marble isprepared from the following raw materials in percentage by weight: 10-15% of refining slag powder, 40-45% of dolomite powder, 15-25% of quartz sand powder, 10-20% of stone powder, 5-15% of an adhesive, 1-2% of a curing agent, 0.03-0.07% of a toner and 0.01-0.03% of a compacting agent, and an artificial white marble product is formed after mold forming and curing. The method can effectively use theexisting manganese slag raw materials, reduce environmental pollution, and improve the use value of manganese slag. The building material with long service life and high additional value is provided,waste is turned into wealth, and the society is benefited.
一种利用精炼锰渣制备人造汉白玉建材的方法，属于建材领域。所述人造汉白玉各原料配比为，精炼渣粉10‑15%、白云石粉40‑45%、石英砂粉15‑25%、石粉10‑20%、粘合剂5‑15%、固化剂1‑2%、调色剂0.03‑0.07%、密实剂0.01‑0.03%，经模具成型、固化后，形成人造汉白玉产品，本发明可有效利用现存的锰渣原料，减少对环境的污染，提高锰渣的使用价值，提供寿命长且具有高附加值的建筑材料，变废为宝，造福社会。
Method for preparing artificial white marble building material from refined manganese slag
一种利用精炼锰渣制备人造汉白玉建材的方法
ZHANG WANBING (author) / NING JIESUAN (author) / ZHANG LIQING (author)
2021-01-22
Patent
Electronic Resource
Chinese
| European Patent Office | 2021
Artificial Marble Chip Artificial Marble Using Same and Method for Preparing thereof
European Patent Office | 2015
Method for preparing artificial marble by using coal gangue and steel slag as aggregate
| European Patent Office | 2023
MOLDING MATERIAL FOR ARTIFICIAL MARBLE, AND THE ARTIFICIAL MARBLE
| European Patent Office | 2017
Artificial marble chip, method of preparing the same and artificial marble including the same
| European Patent Office | 2020