Cement-based capillary crystalline waterproof material based on graphene oxide modification and preparation method of cement-based capillary crystalline waterproof material
The invention discloses a cement-based capillary crystalline waterproof material based on graphene oxide modification and relates to the technical field of building waterproof materials. The material comprises the following components in parts by weight: 50-200 parts of cement, 20-60 parts of quartz sand, 1-10 parts of a retarder, 1-10 parts of a water reducing agent, 1-10 parts of a dispersing agent, 0.1-0.5 part of graphene oxide, 4-10 parts of capillary crystalline master batch, 1-10 parts of a crystalline precipitant, 0.5-5 parts of a surfactant, 0.5-2 part of a complexing agent, 1-5 parts of a calcium ion compensating agent, 0.1-1 part of cellulose ether, 1-2 parts of redispersible latex powder and 0.1-1 part of a defoaming agent, wherein the above components are weighed in proportion, and are stirred and mixed in a three-dimensional motion mixer, and the mixture is put in a ball mill for ball milling to obtain the graphene oxide modified cement-based capillary crystalline waterproof material.
一种基于氧化石墨烯改性的水泥基渗透结晶型防水材料，涉及建筑防水材料技术领域，包括以下重量份数的组分：水泥50‑200份，石英砂20‑60份，缓凝剂1‑10份，减水剂1‑10份，分散剂1‑10份，氧化石墨烯0.1‑0.5份，渗透结晶母料4‑10份，结晶沉淀剂1‑10份，表面活性剂0.5‑5份，络合剂0.5‑2份，钙离子补偿剂1‑5份，纤维素醚0.1‑1份，可再分散乳胶粉1‑2份，消泡剂0.1‑1份,将上述按比例称取，放入三维运动混合机中搅拌混合，然后放入球磨机中球磨得到氧化石墨烯改性的水泥基渗透结晶型防水材料。
Cement-based capillary crystalline waterproof material based on graphene oxide modification and preparation method of cement-based capillary crystalline waterproof material
The invention discloses a cement-based capillary crystalline waterproof material based on graphene oxide modification and relates to the technical field of building waterproof materials. The material comprises the following components in parts by weight: 50-200 parts of cement, 20-60 parts of quartz sand, 1-10 parts of a retarder, 1-10 parts of a water reducing agent, 1-10 parts of a dispersing agent, 0.1-0.5 part of graphene oxide, 4-10 parts of capillary crystalline master batch, 1-10 parts of a crystalline precipitant, 0.5-5 parts of a surfactant, 0.5-2 part of a complexing agent, 1-5 parts of a calcium ion compensating agent, 0.1-1 part of cellulose ether, 1-2 parts of redispersible latex powder and 0.1-1 part of a defoaming agent, wherein the above components are weighed in proportion, and are stirred and mixed in a three-dimensional motion mixer, and the mixture is put in a ball mill for ball milling to obtain the graphene oxide modified cement-based capillary crystalline waterproof material.
一种基于氧化石墨烯改性的水泥基渗透结晶型防水材料，涉及建筑防水材料技术领域，包括以下重量份数的组分：水泥50‑200份，石英砂20‑60份，缓凝剂1‑10份，减水剂1‑10份，分散剂1‑10份，氧化石墨烯0.1‑0.5份，渗透结晶母料4‑10份，结晶沉淀剂1‑10份，表面活性剂0.5‑5份，络合剂0.5‑2份，钙离子补偿剂1‑5份，纤维素醚0.1‑1份，可再分散乳胶粉1‑2份，消泡剂0.1‑1份,将上述按比例称取，放入三维运动混合机中搅拌混合，然后放入球磨机中球磨得到氧化石墨烯改性的水泥基渗透结晶型防水材料。
Cement-based capillary crystalline waterproof material based on graphene oxide modification and preparation method of cement-based capillary crystalline waterproof material
一种基于氧化石墨烯改性的水泥基渗透结晶型防水材料及其制备方法
YUAN XIAOYA (author) / LIU TAO (author) / WANG LIANG (author) / HOU KANG (author) / LIN SHANWU (author) / QI MENG (author)
2021-04-06
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Cement-based capillary crystalline waterproof agent and waterproof material
| European Patent Office | 2024
Cement-based capillary crystalline waterproof material and preparation method thereof
| European Patent Office | 2024
Cement-based capillary crystalline waterproof material and preparation method thereof
| European Patent Office | 2024