The invention relates to a manufacturing process of a void-free embossment wall, which comprises the following steps: 1) making a mold, 2) pouring a surface material, 3) pouring a structural material, 4) performing film covering and curing: after the pouring of the structural material is completed, covering the structural material with a plastic film to prevent the water from evaporating too fast to generate cracks; and (5) demolding and curing are conducted, specifically, demolding is conducted after the covering film is cured for 20-24 h, curing continues to be conducted for 24 h after demolding, then surface treatment is conducted, and manufacturing of the void-free embossment wall is completed. The invention has the beneficial effects that the embossed wall manufactured by the process is fine in surface, clear in line outline, more attractive in structure, free of obvious holes in the surface, high in compressive strength and not easy to break.
本发明涉及一种无孔洞浮雕壁的制作工艺，包括以下步骤：1)制定模具2)浇筑面料3)浇筑结构料4)覆膜养护在完成浇筑结构料后，用塑料薄膜覆盖，防止水分蒸发过快产生裂纹；5)脱模及养护在覆膜养护20‑24h后脱模，在脱模后继续养护24小时再进行表面处理，即，完成无孔洞浮雕壁的制作。有益效果是：通过上述工艺制作的浮雕壁表面细腻、线条轮廓清晰，结构更加美观，表面无明显孔洞，而且抗压强度大，不易碎。
The invention relates to a manufacturing process of a void-free embossment wall, which comprises the following steps: 1) making a mold, 2) pouring a surface material, 3) pouring a structural material, 4) performing film covering and curing: after the pouring of the structural material is completed, covering the structural material with a plastic film to prevent the water from evaporating too fast to generate cracks; and (5) demolding and curing are conducted, specifically, demolding is conducted after the covering film is cured for 20-24 h, curing continues to be conducted for 24 h after demolding, then surface treatment is conducted, and manufacturing of the void-free embossment wall is completed. The invention has the beneficial effects that the embossed wall manufactured by the process is fine in surface, clear in line outline, more attractive in structure, free of obvious holes in the surface, high in compressive strength and not easy to break.
本发明涉及一种无孔洞浮雕壁的制作工艺，包括以下步骤：1)制定模具2)浇筑面料3)浇筑结构料4)覆膜养护在完成浇筑结构料后，用塑料薄膜覆盖，防止水分蒸发过快产生裂纹；5)脱模及养护在覆膜养护20‑24h后脱模，在脱模后继续养护24小时再进行表面处理，即，完成无孔洞浮雕壁的制作。有益效果是：通过上述工艺制作的浮雕壁表面细腻、线条轮廓清晰，结构更加美观，表面无明显孔洞，而且抗压强度大，不易碎。
Manufacturing process of void-free embossment wall
一种无孔洞浮雕壁的制作工艺
LIU HUI (author)
2022-04-29
Patent
Electronic Resource
Chinese
IPC:
B44C
Verfahren zum Herstellen von Verzierungen
,
PRODUCING DECORATIVE EFFECTS
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
C04B
Kalk
,
LIME
Method for forming embossment style wall surface and embossment style wall surface
| European Patent Office | 2022
| European Patent Office | 2020