The invention provides a hexagonal ferrite with high coercive force and high density and a preparation method thereof. The M-type hexagonal ferrite material is prepared by doping 2.5% of Bi2O3, 2.0% of CuO and 0.1-1.0% of V2O5 to improve the density of M-type barium ferrite while ensuring the coercive force of the material, preparing a green body by combining a wet magnetic field forming process and then combining an optimized sintering process. The method is characterized in that the coercive force is greater than 2200Oe, and the density reaches 5.14 g/cm < 3 >.
本发明提供了一种具有高矫顽力和高密度的六角铁氧体及制备方法。在保证材料矫顽力的同时，通过掺杂2.5％Bi2O3、2.0％CuO和0.1％～1.0％V2O5来提高M型钡铁氧体密度，结合湿法磁场成型工艺制备生坯，再结合优化的烧结工艺，最终制备的M型六角铁氧体材料。其特征在于，矫顽力大于2200Oe，密度达到5.14g/cm3。
High-coercivity M-type barium ferrite densification technology for self-biased circulator
The invention provides a hexagonal ferrite with high coercive force and high density and a preparation method thereof. The M-type hexagonal ferrite material is prepared by doping 2.5% of Bi2O3, 2.0% of CuO and 0.1-1.0% of V2O5 to improve the density of M-type barium ferrite while ensuring the coercive force of the material, preparing a green body by combining a wet magnetic field forming process and then combining an optimized sintering process. The method is characterized in that the coercive force is greater than 2200Oe, and the density reaches 5.14 g/cm < 3 >.
本发明提供了一种具有高矫顽力和高密度的六角铁氧体及制备方法。在保证材料矫顽力的同时，通过掺杂2.5％Bi2O3、2.0％CuO和0.1％～1.0％V2O5来提高M型钡铁氧体密度，结合湿法磁场成型工艺制备生坯，再结合优化的烧结工艺，最终制备的M型六角铁氧体材料。其特征在于，矫顽力大于2200Oe，密度达到5.14g/cm3。
High-coercivity M-type barium ferrite densification technology for self-biased circulator
自偏置环行器用高矫顽力M型钡铁氧体致密化技术
ZHANG TAO (author) / JIANG XIAONA (author) / YU ZHONG (author) / WU CHUANJIAN (author) / SUN KE (author) / LAN ZHONGWEN (author)
2022-05-31
Patent
Electronic Resource
Chinese
Preparation technology of high-remanence M-type barium ferrite for self-biased circulator
| European Patent Office | 2022
Preparation method of high-coercivity permanent magnet barium ferrite
| European Patent Office | 2023
Development of millimeter wave integrated circulator based on barium ferrite
| British Library Online Contents | 2008
Preparation method of high-coercivity strontium-barium ferrite magnetic material
| European Patent Office | 2015
| British Library Online Contents | 2002