Manufacturing method of high-temperature-resistant ceramic fiber board
The invention provides a manufacturing method of a high-temperature-resistant ceramic fiber board, and the method mainly comprises six steps of preparation material mixing, dispersing agent preheating, flocculation and scattering, blank making, drying and firing, a novel binding agent using mode is adopted, high-density combination of ceramic fibers and powder is achieved, and the high-temperature-resistant ceramic fiber board is obtained. According to the ceramic fiber board prepared by adding the solution heated by the organic binding agent into the mixed preparation material, the use amount of the binding agent can be effectively reduced, the binding degree of the ceramic fiber and the filler is further improved, the uniformity of the fiber board is good, and meanwhile, the use amount of the binding agent is reduced, so that the production cost is reduced, and the environmental pollution is reduced; and the economic benefit is improved.
本发明提供一种耐高温陶瓷纤维板制作方法，该方法主要包括混制预备料、预热分散剂、絮凝打散、制坯、烘干、烧成等六个步骤，本发明采用一种新型结合剂使用方式，实现了陶瓷纤维和粉料的高密度结合，利用有机结合剂加热后的溶液再加入到混制预备料中制成的陶瓷纤维板可以有效减少结合剂的使用量，进一步提高陶瓷纤维和填充料的结合程度，纤维板的均一度好，同时减少了结合剂的使用，从而降低了生产成本，减少了环境污染，提高了经济效益。
Manufacturing method of high-temperature-resistant ceramic fiber board
The invention provides a manufacturing method of a high-temperature-resistant ceramic fiber board, and the method mainly comprises six steps of preparation material mixing, dispersing agent preheating, flocculation and scattering, blank making, drying and firing, a novel binding agent using mode is adopted, high-density combination of ceramic fibers and powder is achieved, and the high-temperature-resistant ceramic fiber board is obtained. According to the ceramic fiber board prepared by adding the solution heated by the organic binding agent into the mixed preparation material, the use amount of the binding agent can be effectively reduced, the binding degree of the ceramic fiber and the filler is further improved, the uniformity of the fiber board is good, and meanwhile, the use amount of the binding agent is reduced, so that the production cost is reduced, and the environmental pollution is reduced; and the economic benefit is improved.
本发明提供一种耐高温陶瓷纤维板制作方法，该方法主要包括混制预备料、预热分散剂、絮凝打散、制坯、烘干、烧成等六个步骤，本发明采用一种新型结合剂使用方式，实现了陶瓷纤维和粉料的高密度结合，利用有机结合剂加热后的溶液再加入到混制预备料中制成的陶瓷纤维板可以有效减少结合剂的使用量，进一步提高陶瓷纤维和填充料的结合程度，纤维板的均一度好，同时减少了结合剂的使用，从而降低了生产成本，减少了环境污染，提高了经济效益。
Manufacturing method of high-temperature-resistant ceramic fiber board
一种耐高温陶瓷纤维板制作方法
WANG GUOQING (author)
2023-01-17
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Preparation process of high-temperature-resistant ceramic fiber board
| European Patent Office | 2024
Manufacturing method of high-temperature-resistant ceramic
| European Patent Office | 2021
| European Patent Office | 2022