Black golden flower ceramic tile surface treatment glaze and method
The invention relates to the technical field of ceramic tile surface treatment, in particular to a black golden flower ceramic tile surface treatment glaze and method. Comprising 92% of black eurotium cristatum polishing glaze and 8% of mineral glaze, and the black eurotium cristatum polishing glaze comprises the following components in parts by weight: 48-54 parts of SiO2, 10-16 parts of Al2O3, 4-10 parts of CaO, 1.5-2.1 parts of MgO, 3-9 parts of ZnO, 3.5-9.5 parts of BaO, 3.5-4.1 parts of K2O and 2.8-3.4 parts of Na2O; the mineral glaze is prepared from the following components in parts by weight: 1.2 to 1.6 parts of B2O3, 1.2 to 1.8 parts of TiO2, 1.4 to 1.6 parts of LiO2, 1.2 to 1.8 parts of PbO and 1.2 to 1.9 parts of SrO. When the glaze for treating the surface of the black golden flower ceramic tile is used for treating the surface of a ceramic tile blank, the glaze is used for treating the ceramic tile, the sintering time is prolonged by 78.5%, and the temperature is reduced by 15%.
本发明涉及瓷砖表面处理技术领域，具体是一种黑金花瓷砖表面处理釉料及方法。包括92％的黑金花抛釉料和8％矿物质釉料，所述黑金花抛釉料包括：SiO248‑54份、Al2O310‑16份、CaO4‑10份、MgO 1.5‑2.1份、ZnO 3‑9份、BaO 3.5‑9.5份、K2O3.5‑4.1份、Na2O2.8‑3.4份；矿物质釉料包括：B2O31.2‑1.6份、TiO21.2‑1.8份、LiO21.4‑1.6份、PbO1.2‑1.8份、SrO1.2‑1.9份。利用本发明的黑金花瓷砖表面处理釉料对瓷砖胚体表面进行处理时，采用本发明的釉料对瓷砖进行处理，其烧结时间提高了78.5％，温度降低了15％。
Black golden flower ceramic tile surface treatment glaze and method
The invention relates to the technical field of ceramic tile surface treatment, in particular to a black golden flower ceramic tile surface treatment glaze and method. Comprising 92% of black eurotium cristatum polishing glaze and 8% of mineral glaze, and the black eurotium cristatum polishing glaze comprises the following components in parts by weight: 48-54 parts of SiO2, 10-16 parts of Al2O3, 4-10 parts of CaO, 1.5-2.1 parts of MgO, 3-9 parts of ZnO, 3.5-9.5 parts of BaO, 3.5-4.1 parts of K2O and 2.8-3.4 parts of Na2O; the mineral glaze is prepared from the following components in parts by weight: 1.2 to 1.6 parts of B2O3, 1.2 to 1.8 parts of TiO2, 1.4 to 1.6 parts of LiO2, 1.2 to 1.8 parts of PbO and 1.2 to 1.9 parts of SrO. When the glaze for treating the surface of the black golden flower ceramic tile is used for treating the surface of a ceramic tile blank, the glaze is used for treating the ceramic tile, the sintering time is prolonged by 78.5%, and the temperature is reduced by 15%.
本发明涉及瓷砖表面处理技术领域，具体是一种黑金花瓷砖表面处理釉料及方法。包括92％的黑金花抛釉料和8％矿物质釉料，所述黑金花抛釉料包括：SiO248‑54份、Al2O310‑16份、CaO4‑10份、MgO 1.5‑2.1份、ZnO 3‑9份、BaO 3.5‑9.5份、K2O3.5‑4.1份、Na2O2.8‑3.4份；矿物质釉料包括：B2O31.2‑1.6份、TiO21.2‑1.8份、LiO21.4‑1.6份、PbO1.2‑1.8份、SrO1.2‑1.9份。利用本发明的黑金花瓷砖表面处理釉料对瓷砖胚体表面进行处理时，采用本发明的釉料对瓷砖进行处理，其烧结时间提高了78.5％，温度降低了15％。
Black golden flower ceramic tile surface treatment glaze and method
一种黑金花瓷砖表面处理釉料及方法
ZHENG JUZHANG (author)
2023-03-28
Patent
Electronic Resource
Chinese
Glaze material of jade glaze, ceramic tile and preparation method of ceramic tile
| European Patent Office | 2023
Transmutation glaze suitable for ceramic tile production and transmutation glaze ceramic tile
| European Patent Office | 2015
| European Patent Office | 2024
White glaze, ceramic tile and ceramic tile preparation method
| European Patent Office | 2020