Glaze of noctilucent artware and production method of artware
The invention relates to a glaze material of a night luminous artware and a production method of the artware, the glaze material is composed of the following components in percentage by weight: 35-45% of feldspar, 25-35% of quartz, 5-8% of talc, 7-12% of kaolin, 7-12% of medium-temperature frit, 10-15% of transparent glaze, 10-15% of fluorescent powder and 10-15% of fluorite. The weight ratio of the medium-temperature frit is 7-12%, the weight ratio of the transparent glaze is 10-15%, the weight ratio of the fluorescent powder is 4-7%, and the weight ratio of the fluorite is 1-4%. By means of the production method of the luminous glaze, luminous artware capable of emitting light continuously can be obtained, and therefore the ornamental value of the artware can be greatly improved; and compared with the traditional luminous porcelain, the situation that the light disappears late at night is avoided.
本发明涉及夜间发光工艺品的釉料及该工艺品的生产方法，所述釉料由长石、石英、滑石、高岭土、中温熔块、透明釉、荧光粉和氟石组成，所述长石的重量占比为35‑45%，所述石英的重量占比为25‑35%，所述滑石的重量占比为5‑8%，所述高岭土的重量占比为7‑12%，所述中温熔块的重量占比为7‑12%，所述透明釉的重量占比为10‑15%，所述荧光粉的重量占比为4‑7%，所述氟石的重量占比为1‑4%，通过本发明提供的发光釉料生产方法能够得到持续发光的发光工艺品，因此能够极大的提高工艺品的观赏性，相较于传统的发光瓷器，不会出现深夜光亮消失的情况。
Glaze of noctilucent artware and production method of artware
The invention relates to a glaze material of a night luminous artware and a production method of the artware, the glaze material is composed of the following components in percentage by weight: 35-45% of feldspar, 25-35% of quartz, 5-8% of talc, 7-12% of kaolin, 7-12% of medium-temperature frit, 10-15% of transparent glaze, 10-15% of fluorescent powder and 10-15% of fluorite. The weight ratio of the medium-temperature frit is 7-12%, the weight ratio of the transparent glaze is 10-15%, the weight ratio of the fluorescent powder is 4-7%, and the weight ratio of the fluorite is 1-4%. By means of the production method of the luminous glaze, luminous artware capable of emitting light continuously can be obtained, and therefore the ornamental value of the artware can be greatly improved; and compared with the traditional luminous porcelain, the situation that the light disappears late at night is avoided.
本发明涉及夜间发光工艺品的釉料及该工艺品的生产方法，所述釉料由长石、石英、滑石、高岭土、中温熔块、透明釉、荧光粉和氟石组成，所述长石的重量占比为35‑45%，所述石英的重量占比为25‑35%，所述滑石的重量占比为5‑8%，所述高岭土的重量占比为7‑12%，所述中温熔块的重量占比为7‑12%，所述透明釉的重量占比为10‑15%，所述荧光粉的重量占比为4‑7%，所述氟石的重量占比为1‑4%，通过本发明提供的发光釉料生产方法能够得到持续发光的发光工艺品，因此能够极大的提高工艺品的观赏性，相较于传统的发光瓷器，不会出现深夜光亮消失的情况。
Glaze of noctilucent artware and production method of artware
夜间发光工艺品的釉料及该工艺品的生产方法
CHEN HUAZHANG (author) / SU LIFEN (author)
2023-03-28
Patent
Electronic Resource
Chinese
Artware in conchoidal shape and manufacturing method of artware
| European Patent Office | 2015
Manufacturing process of ice cracked glaze jun porcelain artware
| European Patent Office | 2021