Marble crystal glaze, marble tile using same and preparation process
The invention relates to the technical field of tiles, in particular to marble crystal glaze, a marble tile using the same and a preparation process. The marble crystal glaze is prepared by uniformly mixing and ball-milling the following raw materials: 25-30 parts of albite, 10-25 parts of lithium feldspar, 6-8 parts of wollastonite, 5-10 parts of kaolin, 6-11 parts of zinc oxide, 2-7 parts of barium carbonate, 5-15 parts of barium lithium aluminum crystal dry particle frit, 2-5 parts of fluorite, 5-10 parts of quartz, 1-5 parts of corundum, 1-2 parts of lithium carbonate, 40-60 parts of a suspending agent, 5-10 parts of stamp-pad ink and 1-8 parts of water. The barium lithium aluminum crystal dry particle frit is prepared by uniformly mixing and ball-milling the following raw materials: 20-30 parts of barium carbonate, 1-2 parts of ball clay, 6-10 parts of diopside, 1-5 parts of limestone, 5-13 parts of lithium carbonate, 10-15 parts of aluminum oxide, 1-5 parts of corundum, 1-5 parts of boric acid, 3-5 parts of sodium carbonate, 3-5 parts of strontium carbonate, 7-15 parts of albite and 2-6 parts of quartz. The marble ceramic tile has good anti-skid performance, hardness and antifouling property, and due to the ultrathin marble crystal glaze layer, the marble ceramic tile is flat in glaze surface, clear in texture and bright in color.
本发明涉及瓷砖技术领域,尤其涉及一种大理石结晶釉、使用其的大理石瓷砖及制备工艺。大理石结晶釉包括如下原料混匀后球磨制得:钠长石25‑30份、锂长石10‑25份、硅灰石6‑8份、高岭土5‑10份、氧化锌6‑11份、碳酸钡2‑7份、钡锂铝结晶干粒熔块5‑15份、萤石2‑5份、石英5‑10份、刚玉1‑5份、碳酸锂1‑2份、悬浮剂40‑60份、印油5‑10份和水1‑8份;钡锂铝结晶干粒熔块包括如下原料混匀后球磨制得:碳酸钡20‑30份、球土1‑2份、透辉石6‑10份、石灰石1‑5份、碳酸锂5‑13份、氧化铝10‑15份、刚玉1‑5份、硼酸1‑5份、碳酸钠3‑5份、碳酸锶3‑5份、钠长石7‑15份和石英2‑6份。大理石瓷砖具有较好的防滑性能、硬度和防污性,由于具有超薄的大理石结晶釉层,大理石瓷砖的釉面平整、纹理清晰、色彩艳丽。
Marble crystal glaze, marble tile using same and preparation process
The invention relates to the technical field of tiles, in particular to marble crystal glaze, a marble tile using the same and a preparation process. The marble crystal glaze is prepared by uniformly mixing and ball-milling the following raw materials: 25-30 parts of albite, 10-25 parts of lithium feldspar, 6-8 parts of wollastonite, 5-10 parts of kaolin, 6-11 parts of zinc oxide, 2-7 parts of barium carbonate, 5-15 parts of barium lithium aluminum crystal dry particle frit, 2-5 parts of fluorite, 5-10 parts of quartz, 1-5 parts of corundum, 1-2 parts of lithium carbonate, 40-60 parts of a suspending agent, 5-10 parts of stamp-pad ink and 1-8 parts of water. The barium lithium aluminum crystal dry particle frit is prepared by uniformly mixing and ball-milling the following raw materials: 20-30 parts of barium carbonate, 1-2 parts of ball clay, 6-10 parts of diopside, 1-5 parts of limestone, 5-13 parts of lithium carbonate, 10-15 parts of aluminum oxide, 1-5 parts of corundum, 1-5 parts of boric acid, 3-5 parts of sodium carbonate, 3-5 parts of strontium carbonate, 7-15 parts of albite and 2-6 parts of quartz. The marble ceramic tile has good anti-skid performance, hardness and antifouling property, and due to the ultrathin marble crystal glaze layer, the marble ceramic tile is flat in glaze surface, clear in texture and bright in color.
本发明涉及瓷砖技术领域,尤其涉及一种大理石结晶釉、使用其的大理石瓷砖及制备工艺。大理石结晶釉包括如下原料混匀后球磨制得:钠长石25‑30份、锂长石10‑25份、硅灰石6‑8份、高岭土5‑10份、氧化锌6‑11份、碳酸钡2‑7份、钡锂铝结晶干粒熔块5‑15份、萤石2‑5份、石英5‑10份、刚玉1‑5份、碳酸锂1‑2份、悬浮剂40‑60份、印油5‑10份和水1‑8份;钡锂铝结晶干粒熔块包括如下原料混匀后球磨制得:碳酸钡20‑30份、球土1‑2份、透辉石6‑10份、石灰石1‑5份、碳酸锂5‑13份、氧化铝10‑15份、刚玉1‑5份、硼酸1‑5份、碳酸钠3‑5份、碳酸锶3‑5份、钠长石7‑15份和石英2‑6份。大理石瓷砖具有较好的防滑性能、硬度和防污性,由于具有超薄的大理石结晶釉层,大理石瓷砖的釉面平整、纹理清晰、色彩艳丽。
Marble crystal glaze, marble tile using same and preparation process
一种大理石结晶釉、使用其的大理石瓷砖及制备工艺
ZHAN SHUNWANG (author) / LI LIN (author) / ZHU LIANFENG (author)
2023-05-23
Patent
Electronic Resource
Chinese
IPC:
C03C
Chemische Zusammensetzungen für Gläser, Glasuren oder Emails
,
CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
C04B
Kalk
,
LIME
/
E04F
FINISHING WORK ON BUILDINGS, e.g. STAIRS, FLOORS
,
Ausbau von Bauwerken, z.B. Treppen, Fußböden
Gold mica marble glaze, marble tile using same and preparation method of marble tile
European Patent Office | 2023
|Permeable marble glaze, marble tile using same and preparation method thereof
European Patent Office | 2024
|Diamond glittering glaze, glittering marble tile and preparation process of glittering marble tile
European Patent Office | 2023
|Ultrafine soft light marble glaze, preparation method thereof and marble tile
European Patent Office | 2024
|European Patent Office | 2023
|