Permeable marble glaze, marble tile using same and preparation method thereof
The invention relates to the technical field of tiles, in particular to permeable marble glaze, a marble tile using the same and a preparation method of the marble tile. The ceramic tile is prepared by uniformly mixing and ball-milling the following raw materials in parts by weight: 25-35 parts of nepheline, 12-16 parts of wollastonite, 6-10 parts of modified barium titanate frit, 6-13 parts of ball clay, 8-12 parts of zinc oxide, 3-6 parts of barium sulfate, 15-20 parts of quartz, 8-13 parts of dolomite, 1-2 parts of talc, 2-8 parts of barium carbonate, 10-20 parts of a penetrant, 5-10 parts of a binder and 10-15 parts of deionized water. Porous rough glaze and permeable marble glaze are sequentially applied to a ground glaze layer, barium sulfate and modified barium carbonate frits are added to the permeable marble glaze layer, wollastonite and zinc oxide can be combined into barium zinc titanate crystals, the glaze layer has the characteristics of being porous, rough and easy to permeate, meanwhile, the performance of glaze slip of the permeable marble glaze is easier to control, and the service life of the glaze slip is prolonged. The marble ceramic tile prepared after firing has good skid resistance, erosion resistance and texture feeling.
本发明涉及瓷砖技术领域，尤其涉及一种渗透大理石釉、使用其的大理石瓷砖及其制备方法。以重量份数计，包括如下原料混匀后球磨制得：霞石25‑35份、硅灰石12‑16份、改性钛酸钡熔块6‑10份、球土6‑13份、氧化锌8‑12份、硫酸钡3‑6份、石英15‑20份、白云石8‑13份、滑石1‑2份、碳酸钡2‑8份、渗透剂10‑20份、粘结剂5‑10份和去离子水10‑15份。通过在底釉层上依次施加多孔粗糙釉和渗透大理石釉，其中，渗透大理石釉层中加入了硫酸钡和改性碳酸钡熔块，有助于硅灰石、氧化锌结合成锌钛酸钡晶体，使釉层具有多孔粗糙、易渗透的特性，同时更易控制渗透大理石釉釉浆的性能，烧成后制备得到的大理石瓷砖具有较好的防滑性、耐侵蚀性和纹理感。
Permeable marble glaze, marble tile using same and preparation method thereof
The invention relates to the technical field of tiles, in particular to permeable marble glaze, a marble tile using the same and a preparation method of the marble tile. The ceramic tile is prepared by uniformly mixing and ball-milling the following raw materials in parts by weight: 25-35 parts of nepheline, 12-16 parts of wollastonite, 6-10 parts of modified barium titanate frit, 6-13 parts of ball clay, 8-12 parts of zinc oxide, 3-6 parts of barium sulfate, 15-20 parts of quartz, 8-13 parts of dolomite, 1-2 parts of talc, 2-8 parts of barium carbonate, 10-20 parts of a penetrant, 5-10 parts of a binder and 10-15 parts of deionized water. Porous rough glaze and permeable marble glaze are sequentially applied to a ground glaze layer, barium sulfate and modified barium carbonate frits are added to the permeable marble glaze layer, wollastonite and zinc oxide can be combined into barium zinc titanate crystals, the glaze layer has the characteristics of being porous, rough and easy to permeate, meanwhile, the performance of glaze slip of the permeable marble glaze is easier to control, and the service life of the glaze slip is prolonged. The marble ceramic tile prepared after firing has good skid resistance, erosion resistance and texture feeling.
本发明涉及瓷砖技术领域，尤其涉及一种渗透大理石釉、使用其的大理石瓷砖及其制备方法。以重量份数计，包括如下原料混匀后球磨制得：霞石25‑35份、硅灰石12‑16份、改性钛酸钡熔块6‑10份、球土6‑13份、氧化锌8‑12份、硫酸钡3‑6份、石英15‑20份、白云石8‑13份、滑石1‑2份、碳酸钡2‑8份、渗透剂10‑20份、粘结剂5‑10份和去离子水10‑15份。通过在底釉层上依次施加多孔粗糙釉和渗透大理石釉，其中，渗透大理石釉层中加入了硫酸钡和改性碳酸钡熔块，有助于硅灰石、氧化锌结合成锌钛酸钡晶体，使釉层具有多孔粗糙、易渗透的特性，同时更易控制渗透大理石釉釉浆的性能，烧成后制备得到的大理石瓷砖具有较好的防滑性、耐侵蚀性和纹理感。
Permeable marble glaze, marble tile using same and preparation method thereof
一种渗透大理石釉、使用其的大理石瓷砖及其制备方法
SHEN XIAOLI (author) / DENG BO (author) / HUANG SHAOQING (author) / ZHANG WEIYE (author) / ZHU WEIJIAN (author) / BI BO (author) / ZHU LIANFENG (author) / HUANG WENFENG (author) / HUANG HAIFA (author)
2024-01-12
Patent
Electronic Resource
Chinese
IPC:
C03C
Chemische Zusammensetzungen für Gläser, Glasuren oder Emails
,
CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
C04B
Kalk
,
LIME
Gold mica marble glaze, marble tile using same and preparation method of marble tile
| European Patent Office | 2023
Marble crystal glaze, marble tile using same and preparation process
| European Patent Office | 2023
Ultrafine soft light marble glaze, preparation method thereof and marble tile
| European Patent Office | 2024
Diamond glittering glaze, glittering marble tile and preparation process of glittering marble tile
| European Patent Office | 2023
| European Patent Office | 2023