Quickly-solidified ceramic tile adhesive
The invention provides a rapidly-solidified ceramic tile adhesive. The rapidly-solidified ceramic tile adhesive is prepared from the following raw materials in parts by weight: 40-80 parts of Portland cement, 25-35 parts of polymer resin, 11-25 parts of a film-forming agent, 10-15 parts of filler, 7-9 parts of an adhesive, 2-5 parts of a catalyst and 1-3 parts of a preservative, according to the ceramic tile adhesive, the raw materials are selected, scientifically proportioned, combined and used, the performance of the raw materials is synergistically exerted, so that high adhesion strength and solidification speed are achieved, the initial setting time of the ceramic tile adhesive is 12-15 min, the final setting time of the ceramic tile adhesive is 21-28 h, the gel is completely dried, completely cured, completely loses plasticity and begins to generate strength within the shortest 21 h, and the ceramic tile adhesive is not prone to falling off during rapid solidification. The adhesive has the advantages that the adhesive strength is high, the adhesive tensile strength is kept between 1.7 Mpa and 2.2 Mpa, displacement does not occur, the transverse deformation is 1.0 mm to 1.5 mm, and the adhesion between the ceramic tile and a base layer is realized in the standard range of JC/T547-2005 ceramic wall and floor tile adhesives; the ceramic tile paving construction period is greatly shortened, the requirements of emergency engineering are met, and the performance of the ceramic tile paving agent can meet the technical requirements.
本发明提供一种快速凝固的瓷砖胶黏剂，包括以下重量份原料：硅酸盐水泥40‑80份、聚合物树脂25‑35份、成膜剂11‑25份、填料10‑15份、粘合剂7‑9份、催化剂2‑5份、防腐剂1‑3份；本发明的瓷砖胶黏剂经各原料选择，科学配比组合使用，协同发挥其性能，以达到较高的黏附强度和凝固速度，本发明中实施例组的初凝为12‑15min，终凝时间为21‑28h，最短21h凝胶剂完全干透，完全固化，完全失去塑性并开始产生强度，在快速凝固的同时，胶粘拉伸强度保持较高，在1.7‑2.2Mpa之间，其未发生位移，横向形变为1.0‑1.5mm，在JC/T547‑2005《陶瓷墙地砖胶粘剂》标准范围内，实现瓷砖与基层之间的粘合；又能快速凝结，极大程度缩短瓷砖铺贴工期，满足紧急工程的需求，其性能又能达到技术要求。
Quickly-solidified ceramic tile adhesive
The invention provides a rapidly-solidified ceramic tile adhesive. The rapidly-solidified ceramic tile adhesive is prepared from the following raw materials in parts by weight: 40-80 parts of Portland cement, 25-35 parts of polymer resin, 11-25 parts of a film-forming agent, 10-15 parts of filler, 7-9 parts of an adhesive, 2-5 parts of a catalyst and 1-3 parts of a preservative, according to the ceramic tile adhesive, the raw materials are selected, scientifically proportioned, combined and used, the performance of the raw materials is synergistically exerted, so that high adhesion strength and solidification speed are achieved, the initial setting time of the ceramic tile adhesive is 12-15 min, the final setting time of the ceramic tile adhesive is 21-28 h, the gel is completely dried, completely cured, completely loses plasticity and begins to generate strength within the shortest 21 h, and the ceramic tile adhesive is not prone to falling off during rapid solidification. The adhesive has the advantages that the adhesive strength is high, the adhesive tensile strength is kept between 1.7 Mpa and 2.2 Mpa, displacement does not occur, the transverse deformation is 1.0 mm to 1.5 mm, and the adhesion between the ceramic tile and a base layer is realized in the standard range of JC/T547-2005 ceramic wall and floor tile adhesives; the ceramic tile paving construction period is greatly shortened, the requirements of emergency engineering are met, and the performance of the ceramic tile paving agent can meet the technical requirements.
本发明提供一种快速凝固的瓷砖胶黏剂，包括以下重量份原料：硅酸盐水泥40‑80份、聚合物树脂25‑35份、成膜剂11‑25份、填料10‑15份、粘合剂7‑9份、催化剂2‑5份、防腐剂1‑3份；本发明的瓷砖胶黏剂经各原料选择，科学配比组合使用，协同发挥其性能，以达到较高的黏附强度和凝固速度，本发明中实施例组的初凝为12‑15min，终凝时间为21‑28h，最短21h凝胶剂完全干透，完全固化，完全失去塑性并开始产生强度，在快速凝固的同时，胶粘拉伸强度保持较高，在1.7‑2.2Mpa之间，其未发生位移，横向形变为1.0‑1.5mm，在JC/T547‑2005《陶瓷墙地砖胶粘剂》标准范围内，实现瓷砖与基层之间的粘合；又能快速凝结，极大程度缩短瓷砖铺贴工期，满足紧急工程的需求，其性能又能达到技术要求。
Quickly-solidified ceramic tile adhesive
一种快速凝固的瓷砖胶黏剂
XIE YAKUN (author) / XIE ZHOUSHUAI (author) / WANG FANGLING (author)
2023-08-22
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME