Wear-resistant glaze and preparation method thereof
The invention discloses a wear-resistant glaze material and a preparation method thereof, and relates to the field of ceramic glaze materials, the wear-resistant glaze material comprises a cover glaze layer and a fully polished glaze layer, the cover glaze layer is prepared from the following raw materials by weight: 20-40 parts of potassium feldspar; 25 to 35 parts of albite; 5 to 15 parts of kaolin; 5 to 15 parts of calcined kaolin; 20 to 25 parts of calcined alumina; 1-5 parts of dolomite; 2 to 8 parts of nepheline; 2 to 6 parts of quartz; the fully polished glaze layer is prepared from the following raw materials in parts by weight: 50-60 parts of albite; 5 to 15 parts of kaolin; 2-7 parts of calcined kaolin; 1-3 parts of calcined alumina; 10 to 20 parts of dolomite; 0.5 to 1.5 parts of quartz; 2-6 parts of calcined zinc oxide; 2 to 10 parts of strontium carbonate; 1-5 parts of calcined talc; 1 to 5 parts of wollastonite; and 0.5 to 1.5 parts of corundum. The wear-resistant ceramic tile has the effect of improving the wear resistance of the ceramic tile.
本发明公开了一种耐磨釉料及其制备方法，涉及陶瓷釉料领域，包括面釉层和全抛釉层，所述面釉层包括以下重量份原料制成：钾长石：20‑40份；钠长石：25‑35份；高岭土：5‑15份；煅烧高岭土：5‑15份；煅烧氧化铝：20‑25份；白云石：1‑5份；霞石：2‑8份；石英：2‑6份；所述全抛釉层包括以下重量份原料制成：钠长石：50‑60份；高岭土：5‑15份；煅烧高岭土：2‑7份；煅烧氧化铝：1‑3份；白云石：10‑20份；石英：0.5‑1.5份；煅烧氧化锌：2‑6份；碳酸锶：2‑10份；煅烧滑石：1‑5份；硅灰石：1‑5份；刚玉0.5‑1.5份。本申请具有提高陶瓷瓷砖的耐磨的效果。
Wear-resistant glaze and preparation method thereof
The invention discloses a wear-resistant glaze material and a preparation method thereof, and relates to the field of ceramic glaze materials, the wear-resistant glaze material comprises a cover glaze layer and a fully polished glaze layer, the cover glaze layer is prepared from the following raw materials by weight: 20-40 parts of potassium feldspar; 25 to 35 parts of albite; 5 to 15 parts of kaolin; 5 to 15 parts of calcined kaolin; 20 to 25 parts of calcined alumina; 1-5 parts of dolomite; 2 to 8 parts of nepheline; 2 to 6 parts of quartz; the fully polished glaze layer is prepared from the following raw materials in parts by weight: 50-60 parts of albite; 5 to 15 parts of kaolin; 2-7 parts of calcined kaolin; 1-3 parts of calcined alumina; 10 to 20 parts of dolomite; 0.5 to 1.5 parts of quartz; 2-6 parts of calcined zinc oxide; 2 to 10 parts of strontium carbonate; 1-5 parts of calcined talc; 1 to 5 parts of wollastonite; and 0.5 to 1.5 parts of corundum. The wear-resistant ceramic tile has the effect of improving the wear resistance of the ceramic tile.
本发明公开了一种耐磨釉料及其制备方法，涉及陶瓷釉料领域，包括面釉层和全抛釉层，所述面釉层包括以下重量份原料制成：钾长石：20‑40份；钠长石：25‑35份；高岭土：5‑15份；煅烧高岭土：5‑15份；煅烧氧化铝：20‑25份；白云石：1‑5份；霞石：2‑8份；石英：2‑6份；所述全抛釉层包括以下重量份原料制成：钠长石：50‑60份；高岭土：5‑15份；煅烧高岭土：2‑7份；煅烧氧化铝：1‑3份；白云石：10‑20份；石英：0.5‑1.5份；煅烧氧化锌：2‑6份；碳酸锶：2‑10份；煅烧滑石：1‑5份；硅灰石：1‑5份；刚玉0.5‑1.5份。本申请具有提高陶瓷瓷砖的耐磨的效果。
Wear-resistant glaze and preparation method thereof
一种耐磨釉料及其制备方法
PENG XIANGHUI (author) / PENG BINHUI (author) / MAO YUANXIN (author)
2023-09-22
Patent
Electronic Resource
Chinese
Antibacterial wear-resistant glaze and preparation method thereof
| European Patent Office | 2021
Preparation method of wear-resistant glaze daily porcelain glaze
| European Patent Office | 2020
| European Patent Office | 2020
| European Patent Office | 2022