Preparation method of high-temperature ablation-resistant chopped carbon fiber reinforced SiBCN-MAS composite material
The invention discloses a preparation method of a high-temperature ablation-resistant chopped carbon fiber reinforced SiBCN-MAS composite material, and relates to a preparation method of a SiBCN ceramic matrix composite material. The invention aims to solve the problems of poor contact surface binding force and limited improvement degree of high-temperature ablation resistance of the existing carbon fiber or cracked carbon coating carbon fiber reinforced SiBCN ceramic matrix composite. The method comprises the following steps: 1, preparing cracked carbon coating chopped carbon fibers; 2, preparing SiBCN amorphous ceramic powder; 3, mixing the raw materials; and 4, sintering. The preparation method is used for preparing the high-temperature ablation-resistant short carbon fiber reinforced SiBCN-MAS composite material.
一种高温耐烧蚀的短切碳纤维增强SiBCN‑MAS复合材料的制备方法，它涉及SiBCN陶瓷基复合材料的制备方法。本发明要解决现有碳纤维或裂解碳涂层碳纤维增强SiBCN陶瓷基复合材料存在触面结合力差，且高温耐烧蚀性提升程度有限的问题。方法：一、制备裂解碳涂层短切碳纤维；二、制备SiBCN非晶陶瓷粉末；三、混合原料；四、烧结。本发明用于高温耐烧蚀的短切碳纤维增强SiBCN‑MAS复合材料的制备。
Preparation method of high-temperature ablation-resistant chopped carbon fiber reinforced SiBCN-MAS composite material
The invention discloses a preparation method of a high-temperature ablation-resistant chopped carbon fiber reinforced SiBCN-MAS composite material, and relates to a preparation method of a SiBCN ceramic matrix composite material. The invention aims to solve the problems of poor contact surface binding force and limited improvement degree of high-temperature ablation resistance of the existing carbon fiber or cracked carbon coating carbon fiber reinforced SiBCN ceramic matrix composite. The method comprises the following steps: 1, preparing cracked carbon coating chopped carbon fibers; 2, preparing SiBCN amorphous ceramic powder; 3, mixing the raw materials; and 4, sintering. The preparation method is used for preparing the high-temperature ablation-resistant short carbon fiber reinforced SiBCN-MAS composite material.
一种高温耐烧蚀的短切碳纤维增强SiBCN‑MAS复合材料的制备方法，它涉及SiBCN陶瓷基复合材料的制备方法。本发明要解决现有碳纤维或裂解碳涂层碳纤维增强SiBCN陶瓷基复合材料存在触面结合力差，且高温耐烧蚀性提升程度有限的问题。方法：一、制备裂解碳涂层短切碳纤维；二、制备SiBCN非晶陶瓷粉末；三、混合原料；四、烧结。本发明用于高温耐烧蚀的短切碳纤维增强SiBCN‑MAS复合材料的制备。
Preparation method of high-temperature ablation-resistant chopped carbon fiber reinforced SiBCN-MAS composite material
一种高温耐烧蚀的短切碳纤维增强SiBCN-MAS复合材料的制备方法
LI DAXIN (author) / WANG YAN (author) / ZHOU TANGJU'ER (author) / LIN KUNPENG (author) / XIAO JUNZE (author) / YANG ZHIHUA (author) / JIA DECHANG (author) / ZHOU YU (author)
2023-10-31
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Method for chopped KD-SA type SiC fiber reinforced SiBCN-MAS ceramic
| European Patent Office | 2024
High-density fiber-reinforced SiBCN ceramic-based composite material and preparation method thereof
| European Patent Office | 2024
Chopped carbon fiber reinforced carbon-ceramic composite material and preparation method thereof
| European Patent Office | 2024
Preparation method of chopped carbon fiber composite material
| European Patent Office | 2023
Preparation method of chopped carbon fiber composite material
| European Patent Office | 2022