The invention discloses transmutation purplish red glaze, which belongs to the technical field of transmutation glaze and comprises ground glaze and cover glaze. The ground glaze is prepared from the following raw materials in parts by weight: 18 to 25 parts of potassium feldspar, 15 to 20 parts of albite, 20 to 25 parts of quartz, 10 to 15 parts of calcite, 4 to 5 parts of Jiepai mud, 1 to 2 parts of Guizhou soil, 9 to 11 parts of frit, 9 to 10 parts of iron oxide red and 9 to 10 parts of manganese carbonate; the cover glaze comprises the following raw materials in parts by weight: 5-10 parts of modified diatomite, 60-80 parts of silicon carbide, 8-12 parts of talcum powder, 6-9 parts of aluminum oxide and 1.5-2.5 parts of sodium carboxymethyl cellulose.The natural raw materials and the chemical raw materials are mixed according to a specific proportion, under the action of high-temperature melting, the unique effect of amaranth transmutation is obtained through firing, and the glaze has the advantages that the glaze is bright in color, bright in color and good in color and luster; the color generation effect of the formula has extremely high artistic value and wide practical market prospects, and has good wear resistance, antibacterial performance and easy-to-clean performance.
本发明公开了一种窑变紫红釉，属于窑变釉技术领域，包括底釉和面釉；所述底釉包括以下重量份原料：钾长石18‑25份，钠长石15‑20份，石英20‑25份，方解石10‑15份，界牌泥4‑5份，贵州土1‑2份，熔块9‑11份，氧化铁红9‑10份，碳酸锰9‑10份；所述面釉包括以下重量份原料：改性硅藻土5‑10份，碳化硅60‑80份，滑石粉8‑12份，氧化铝6‑9份，羧甲基纤维素钠1.5‑2.5份，本发明将自然原料与化学原料，按特定分量的配比混合，在高温熔融作用下，烧制出紫红色窑变的独特效果，该配方的呈色效果具有极高的艺术价值和广泛的实用市场前景，且具有良好耐磨、抗菌以及易清洁性能。
Furnace transmutation purplish red glaze
The invention discloses transmutation purplish red glaze, which belongs to the technical field of transmutation glaze and comprises ground glaze and cover glaze. The ground glaze is prepared from the following raw materials in parts by weight: 18 to 25 parts of potassium feldspar, 15 to 20 parts of albite, 20 to 25 parts of quartz, 10 to 15 parts of calcite, 4 to 5 parts of Jiepai mud, 1 to 2 parts of Guizhou soil, 9 to 11 parts of frit, 9 to 10 parts of iron oxide red and 9 to 10 parts of manganese carbonate; the cover glaze comprises the following raw materials in parts by weight: 5-10 parts of modified diatomite, 60-80 parts of silicon carbide, 8-12 parts of talcum powder, 6-9 parts of aluminum oxide and 1.5-2.5 parts of sodium carboxymethyl cellulose.The natural raw materials and the chemical raw materials are mixed according to a specific proportion, under the action of high-temperature melting, the unique effect of amaranth transmutation is obtained through firing, and the glaze has the advantages that the glaze is bright in color, bright in color and good in color and luster; the color generation effect of the formula has extremely high artistic value and wide practical market prospects, and has good wear resistance, antibacterial performance and easy-to-clean performance.
本发明公开了一种窑变紫红釉，属于窑变釉技术领域，包括底釉和面釉；所述底釉包括以下重量份原料：钾长石18‑25份，钠长石15‑20份，石英20‑25份，方解石10‑15份，界牌泥4‑5份，贵州土1‑2份，熔块9‑11份，氧化铁红9‑10份，碳酸锰9‑10份；所述面釉包括以下重量份原料：改性硅藻土5‑10份，碳化硅60‑80份，滑石粉8‑12份，氧化铝6‑9份，羧甲基纤维素钠1.5‑2.5份，本发明将自然原料与化学原料，按特定分量的配比混合，在高温熔融作用下，烧制出紫红色窑变的独特效果，该配方的呈色效果具有极高的艺术价值和广泛的实用市场前景，且具有良好耐磨、抗菌以及易清洁性能。
Furnace transmutation purplish red glaze
一种窑变紫红釉
ZHOU HENG (author) / LI ZHIXING (author) / LI HANG (author) / XIE ZHILAI (author) / LI XUE (author)
2023-11-10
Patent
Electronic Resource
Chinese
| European Patent Office | 2024
| European Patent Office | 2022
| European Patent Office | 2024
Purplish red oxidation Grignard metal glaze and processing technology thereof
| European Patent Office | 2021