Integrated cementing material for high-performance low-carbon concrete
The invention discloses an integrated cementing material for high-performance low-carbon concrete. The integrated cementing material is prepared by uniformly dry-mixing the following raw materials in parts by weight: 35-40 parts of Portland cement clinker powder; 5 to 6 parts of high-calcium high-iron belite sulphoaluminate cement clinker powder; 5-10 parts of fine limestone powder; 14 to 20 parts of ground fly ash; 10 to 15 parts of superfine slag powder; 10 to 15 parts of steel slag micro powder; and 5-10 parts of coarse limestone powder. The preparation parameters of the high-calcium, high-iron and high-belite sulphoaluminate cement clinker are as follows: the alkalinity coefficient Cm value is 1.60-1.65, the fCaO is 0.5-1.0%, and the fSO3 is 0.5-1.0%; the mineral composition is as follows: 50%-60% of C2S, 20%-25% of C4A3S, 10%-15% of C6AF2 and 5%-10% of C12A7. According to the integrated cementing material disclosed by the invention, the dosage of the cement clinker is as low as 33-38%, and the 28d strength can reach 41.0-42.0 MPa.
本发明公开了一种高性能低碳混凝土用一体化胶凝材料，由如下重量份的原料干混均匀得到：硅酸盐水泥熟料粉35‑40份；高钙高铁贝利特硫铝酸盐水泥熟料粉5‑6份；细石灰石粉5‑10份；磨细粉煤灰14‑20份；矿渣微粉10‑15份；钢渣微粉10‑15份；粗石灰石粉5‑10份。高钙高铁高贝利特硫铝酸盐水泥熟料的配料参数：碱度系数Cm值1.60～1.65，fCaO0.5～1.0％，fSO30.5～1.0％；矿物组成：C2S 50～60％，C4A3S 20～25％，C6AF210‑15％，C12A75‑10％。本发明一体化胶凝材料，水泥熟料用量低至33‑38％，28d强度可达到41.0‑42.0MPa。
Integrated cementing material for high-performance low-carbon concrete
The invention discloses an integrated cementing material for high-performance low-carbon concrete. The integrated cementing material is prepared by uniformly dry-mixing the following raw materials in parts by weight: 35-40 parts of Portland cement clinker powder; 5 to 6 parts of high-calcium high-iron belite sulphoaluminate cement clinker powder; 5-10 parts of fine limestone powder; 14 to 20 parts of ground fly ash; 10 to 15 parts of superfine slag powder; 10 to 15 parts of steel slag micro powder; and 5-10 parts of coarse limestone powder. The preparation parameters of the high-calcium, high-iron and high-belite sulphoaluminate cement clinker are as follows: the alkalinity coefficient Cm value is 1.60-1.65, the fCaO is 0.5-1.0%, and the fSO3 is 0.5-1.0%; the mineral composition is as follows: 50%-60% of C2S, 20%-25% of C4A3S, 10%-15% of C6AF2 and 5%-10% of C12A7. According to the integrated cementing material disclosed by the invention, the dosage of the cement clinker is as low as 33-38%, and the 28d strength can reach 41.0-42.0 MPa.
本发明公开了一种高性能低碳混凝土用一体化胶凝材料，由如下重量份的原料干混均匀得到：硅酸盐水泥熟料粉35‑40份；高钙高铁贝利特硫铝酸盐水泥熟料粉5‑6份；细石灰石粉5‑10份；磨细粉煤灰14‑20份；矿渣微粉10‑15份；钢渣微粉10‑15份；粗石灰石粉5‑10份。高钙高铁高贝利特硫铝酸盐水泥熟料的配料参数：碱度系数Cm值1.60～1.65，fCaO0.5～1.0％，fSO30.5～1.0％；矿物组成：C2S 50～60％，C4A3S 20～25％，C6AF210‑15％，C12A75‑10％。本发明一体化胶凝材料，水泥熟料用量低至33‑38％，28d强度可达到41.0‑42.0MPa。
Integrated cementing material for high-performance low-carbon concrete
一种高性能低碳混凝土用一体化胶凝材料
YAO PIQIANG (author) / HUANG XIONG (author) / LIU MINGHAO (author)
2023-12-05
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2024
| European Patent Office | 2022
Ultra-high performance concrete based on composite cementing material system
| European Patent Office | 2022