Ceramic glaze, ceramic product and preparation method thereof
The invention relates to a ceramic glaze, a ceramic product and a preparation method thereof, the ceramic glaze comprises the following components by weight: 76-89 parts of opaque glaze, 10-21 parts of a liquid phase regulator, and 1-3 parts of rare earth oxide; the opaque glaze is prepared from the following chemical components in percentage by weight: 57.2 percent to 60.5 percent of SiO2, 9 percent to 12.8 percent of Al2O3, 8 percent to 12.5 percent of CaO, 5.5 percent to 9.0 percent of MgO, 2.2 percent to 4.2 percent of K2O, 1.5 percent to 3.0 percent of Na2O, 6 percent to 11.0 percent of ZrO2, 1.6 percent to 4.5 percent of SrO and 2.1 percent to 4.3 percent of BaO. The glaze surface of a ceramic product prepared from the ceramic glaze has lasting wear resistance, the effect is stable for a long time, the process of the product is simple, and the ceramic glaze can be used for large-scale production in factories.
一种陶瓷釉料、陶瓷产品及其制备方法，其中，所述陶瓷釉料，按重量计，包括如下组分：乳浊釉76份‑89份，液相调节剂10份‑21份，稀土氧化物1份‑3份；所述乳浊釉的化学组成，按重量百分比计，为：SiO2 57.2％‑60.5％、Al2O3 9％‑12.8％、CaO 8％‑12.5％、MgO 5.5％‑9.0％、K2O 2.2％‑4.2％、Na2O 1.5％‑3.0％、ZrO2 6％‑11.0％、SrO 1.6％‑4.5％、BaO 2.1％‑4.3％。采用所述陶瓷釉料制备的陶瓷产品的釉面具有持久耐磨性，并且该效果长期稳定，产品的工艺简单、可供工厂规模生产。
Ceramic glaze, ceramic product and preparation method thereof
The invention relates to a ceramic glaze, a ceramic product and a preparation method thereof, the ceramic glaze comprises the following components by weight: 76-89 parts of opaque glaze, 10-21 parts of a liquid phase regulator, and 1-3 parts of rare earth oxide; the opaque glaze is prepared from the following chemical components in percentage by weight: 57.2 percent to 60.5 percent of SiO2, 9 percent to 12.8 percent of Al2O3, 8 percent to 12.5 percent of CaO, 5.5 percent to 9.0 percent of MgO, 2.2 percent to 4.2 percent of K2O, 1.5 percent to 3.0 percent of Na2O, 6 percent to 11.0 percent of ZrO2, 1.6 percent to 4.5 percent of SrO and 2.1 percent to 4.3 percent of BaO. The glaze surface of a ceramic product prepared from the ceramic glaze has lasting wear resistance, the effect is stable for a long time, the process of the product is simple, and the ceramic glaze can be used for large-scale production in factories.
一种陶瓷釉料、陶瓷产品及其制备方法，其中，所述陶瓷釉料，按重量计，包括如下组分：乳浊釉76份‑89份，液相调节剂10份‑21份，稀土氧化物1份‑3份；所述乳浊釉的化学组成，按重量百分比计，为：SiO2 57.2％‑60.5％、Al2O3 9％‑12.8％、CaO 8％‑12.5％、MgO 5.5％‑9.0％、K2O 2.2％‑4.2％、Na2O 1.5％‑3.0％、ZrO2 6％‑11.0％、SrO 1.6％‑4.5％、BaO 2.1％‑4.3％。采用所述陶瓷釉料制备的陶瓷产品的釉面具有持久耐磨性，并且该效果长期稳定，产品的工艺简单、可供工厂规模生产。
Ceramic glaze, ceramic product and preparation method thereof
一种陶瓷釉料、陶瓷产品及其制备方法
LIN XIAOFA (author) / LIN XIAOSHAN (author) / LAI MIN (author) / KUANG YONGJI (author) / CHENG XINTAO (author)
2024-03-01
Patent
Electronic Resource
Chinese
Ceramic glaze, preparation method and application thereof, and ceramic product
| European Patent Office | 2024
Transmutation glaze, transmutation glaze laterite ceramic product and preparation method thereof
| European Patent Office | 2022
Glaze composition, ceramic product and preparation method of ceramic product
| European Patent Office | 2023
| European Patent Office | 2023
White glaze ceramic product with black ground glaze and preparation method thereof
| European Patent Office | 2020