Opalescent porcelain and preparation method thereof
The invention provides opalescent porcelain and a preparation method thereof.The opalescent porcelain is prepared from 65-85 parts of zirconium oxide, 5-15 parts of loaded modified microporous zirconium oxide, 2-5 parts of yttrium oxide, 0.1-0.5 part of aluminum oxide and 0.01-0.1 part of pigment, the particle size of the raw materials is 0.1-0.5 micrometer, the loaded modified microporous zirconium oxide is microporous zirconium oxide loaded with silicate, and the pigment is a mixture of zirconium oxide and yttrium oxide. The microporous zirconium oxide loaded with silicate is added into the raw materials, so that the light transmittance and the refraction effect are improved, the transparent gradual change of the ceramic at the edge position is improved, and the ceramic has a good appearance effect.
本发明提出了一种乳光瓷及其制备方法，该乳光瓷，采用的原料包括氧化锆65‑85份、负载改性微孔氧化锆5‑15份、氧化钇2‑5份、氧化铝0.1‑0.5份和色料0.01‑0.1份，上述原料的粒度均为0.1‑0.5μm，所述负载改性微孔氧化锆为负载有硅酸盐的微孔氧化锆，通过在原料中加入负载有硅酸盐的微孔氧化锆，从而改善了透光性和折射效果，提高了瓷在边缘位置的透明渐变性，具有良好的外观效果。
Opalescent porcelain and preparation method thereof
The invention provides opalescent porcelain and a preparation method thereof.The opalescent porcelain is prepared from 65-85 parts of zirconium oxide, 5-15 parts of loaded modified microporous zirconium oxide, 2-5 parts of yttrium oxide, 0.1-0.5 part of aluminum oxide and 0.01-0.1 part of pigment, the particle size of the raw materials is 0.1-0.5 micrometer, the loaded modified microporous zirconium oxide is microporous zirconium oxide loaded with silicate, and the pigment is a mixture of zirconium oxide and yttrium oxide. The microporous zirconium oxide loaded with silicate is added into the raw materials, so that the light transmittance and the refraction effect are improved, the transparent gradual change of the ceramic at the edge position is improved, and the ceramic has a good appearance effect.
本发明提出了一种乳光瓷及其制备方法，该乳光瓷，采用的原料包括氧化锆65‑85份、负载改性微孔氧化锆5‑15份、氧化钇2‑5份、氧化铝0.1‑0.5份和色料0.01‑0.1份，上述原料的粒度均为0.1‑0.5μm，所述负载改性微孔氧化锆为负载有硅酸盐的微孔氧化锆，通过在原料中加入负载有硅酸盐的微孔氧化锆，从而改善了透光性和折射效果，提高了瓷在边缘位置的透明渐变性，具有良好的外观效果。
Opalescent porcelain and preparation method thereof
乳光瓷及其制备方法
WANG LING (author) / KE XILIN (author) / KE CHAOYANG (author)
2024-03-01
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Solid Opalescent Films Originating from Urethanes of Cellulose
| British Library Online Contents | 1997
Lisse et opalescent, Institut de recherche pluridisciplinaire
British Library Online Contents | 2008
Opalescent Cholesteric Networks from Chiral Polyisocyanates in Polystyrene
| British Library Online Contents | 1998
Porcelain clay, and porcelain and preparation method thereof
| European Patent Office | 2021
Alumina-based porcelain insulator porcelain body and preparation method thereof
| European Patent Office | 2024