Lead-free silver metal glaze and preparation method of lead-free silver metal glaze product
The invention discloses a lead-free silver metal glaze suitable for one-time rapid firing of a roller kiln. The glaze comprises the following components in percentage by weight: 30-50% of potassium feldspar, 5-10% of talc, 5-10% of calcite, 20-30% of calcium phosphate, 10-25% of ferric oxide, 3-8% of kaolin and 5-15% of frit powder, and the frit powder comprises the following components in percentage by weight: 10-20% of calcium phosphate, 10-20% of aluminum phosphate, 20-50% of sodium borate, 10-15% of quartz and 5-10% of lithium oxide. The boron-phosphorus equal phase-splitting accelerant is introduced to promote the formation and growth of metal split phases, and a large amount of silver metal split phases are generated in a short time to obtain a metal effect.
本发明公开了一种适合辊道窑一次快速烧成的无铅银色金属釉料。釉料组成成分按重量百分比计其组成如下:钾长石30~50%,滑石5~10%,方解石5~10%,磷酸钙20~30%,氧化铁10~25%,高岭土3~8%,熔块粉5~15%,所述熔块粉的组成按如下重量百分比计组成如下:磷酸钙10~20%,磷酸铝10~20%,硼酸钠20~50%,石英10~15%,氧化锂5~10%。本发明通过引入硼磷等分相促进剂促进金属分相的形成和增长,短时间内大量产生银色金属分相获得金属效果。
Lead-free silver metal glaze and preparation method of lead-free silver metal glaze product
The invention discloses a lead-free silver metal glaze suitable for one-time rapid firing of a roller kiln. The glaze comprises the following components in percentage by weight: 30-50% of potassium feldspar, 5-10% of talc, 5-10% of calcite, 20-30% of calcium phosphate, 10-25% of ferric oxide, 3-8% of kaolin and 5-15% of frit powder, and the frit powder comprises the following components in percentage by weight: 10-20% of calcium phosphate, 10-20% of aluminum phosphate, 20-50% of sodium borate, 10-15% of quartz and 5-10% of lithium oxide. The boron-phosphorus equal phase-splitting accelerant is introduced to promote the formation and growth of metal split phases, and a large amount of silver metal split phases are generated in a short time to obtain a metal effect.
本发明公开了一种适合辊道窑一次快速烧成的无铅银色金属釉料。釉料组成成分按重量百分比计其组成如下:钾长石30~50%,滑石5~10%,方解石5~10%,磷酸钙20~30%,氧化铁10~25%,高岭土3~8%,熔块粉5~15%,所述熔块粉的组成按如下重量百分比计组成如下:磷酸钙10~20%,磷酸铝10~20%,硼酸钠20~50%,石英10~15%,氧化锂5~10%。本发明通过引入硼磷等分相促进剂促进金属分相的形成和增长,短时间内大量产生银色金属分相获得金属效果。
Lead-free silver metal glaze and preparation method of lead-free silver metal glaze product
一种无铅银色金属釉料及其产品的制备方法
CHEN GUANGYUAN (author) / YUAN LI (author) / HU YINGZI (author) / YAO SHASHA (author)
2024-03-01
Patent
Electronic Resource
Chinese
Glaze mixture of metal glaze, metal glaze product and preparation process of metal glaze
European Patent Office | 2020
|European Patent Office | 2015
|Lead-free iron-based metallic glaze and preparation method thereof
European Patent Office | 2022
|European Patent Office | 2021
|Ceramic metal glaze powder, metal glaze and metal glazed tile
European Patent Office | 2022
|