Argil sintered brick and terrace manufacturing method
The invention belongs to the technical field of white spirit brewing, and relates to a preparation method of a pottery clay sintered brick, which comprises the following steps: crushing pottery clay into powder to obtain powder; taking part of the powder, adding equal volume of water, uniformly stirring, kneading into blocks, firing, forming and crushing to obtain aggregate; the particle size of the aggregate is 3.8-4.2 mm; taking the aggregate and the powder, adding water, mixing, uniformly stirring to prepare a green brick, and airing; the adding amount of the aggregate is 30%-50%, and the adding amount of the powder is 50%-70%; drying and firing: putting the air-dried green bricks into a drying room, drying and firing to obtain argil sintered bricks; wherein the drying parameters comprise that the temperature is gradually increased to 95-105 DEG C from the room temperature, the temperature increasing time is 2-4 days, and after the temperature is increased to 95-105 DEG C, drying continues to be conducted for 1-3 days; the firing parameters are as follows: firing is performed for 20-25 hours at the temperature of 900-1000 DEG C. The prepared argil sintered brick is high in water absorption and is combined with a gravel cushion layer to prepare a fermentation bin terrace, the koji-making fermentation temperature under the terrace is consistent with that of a concrete terrace, and the argil sintered brick is suitable for a high-temperature and high-humidity leaktight fermentation environment for koji-making.
本发明属于白酒酿制技术领域，涉及一种陶土烧结砖的制备方法，包括以下步骤：将陶泥粉碎成粉末状，得粉料；取部分粉料加入等体积水，翻拌均匀，捏制成块状，烧制成型，破碎，得骨料；骨料粒径为3.8‑4.2mm；取骨料和粉料加入水进行混合，搅匀，制成砖坯，晾干；骨料添加量为30％‑50％，粉料添加量占比为50％‑70％；烘干烧制：将晾干的砖坯放入烘房，进行烘干、烧制，得到陶土烧结砖；其中，烘干参数包括：由室温逐步上升至95‑105℃，升温时间为2‑4天，达到95‑105℃后，继续烘干1‑3天；烧制参数包括：在900‑1000℃温度下烧制20‑25小时。制得的陶土烧结砖吸水性较高，结合砂石垫层，制成发酵仓地坪，该地坪下的制曲发酵温度与三合土地坪一致，适用于制曲高温高湿的密闭性发酵环境。
Argil sintered brick and terrace manufacturing method
The invention belongs to the technical field of white spirit brewing, and relates to a preparation method of a pottery clay sintered brick, which comprises the following steps: crushing pottery clay into powder to obtain powder; taking part of the powder, adding equal volume of water, uniformly stirring, kneading into blocks, firing, forming and crushing to obtain aggregate; the particle size of the aggregate is 3.8-4.2 mm; taking the aggregate and the powder, adding water, mixing, uniformly stirring to prepare a green brick, and airing; the adding amount of the aggregate is 30%-50%, and the adding amount of the powder is 50%-70%; drying and firing: putting the air-dried green bricks into a drying room, drying and firing to obtain argil sintered bricks; wherein the drying parameters comprise that the temperature is gradually increased to 95-105 DEG C from the room temperature, the temperature increasing time is 2-4 days, and after the temperature is increased to 95-105 DEG C, drying continues to be conducted for 1-3 days; the firing parameters are as follows: firing is performed for 20-25 hours at the temperature of 900-1000 DEG C. The prepared argil sintered brick is high in water absorption and is combined with a gravel cushion layer to prepare a fermentation bin terrace, the koji-making fermentation temperature under the terrace is consistent with that of a concrete terrace, and the argil sintered brick is suitable for a high-temperature and high-humidity leaktight fermentation environment for koji-making.
本发明属于白酒酿制技术领域，涉及一种陶土烧结砖的制备方法，包括以下步骤：将陶泥粉碎成粉末状，得粉料；取部分粉料加入等体积水，翻拌均匀，捏制成块状，烧制成型，破碎，得骨料；骨料粒径为3.8‑4.2mm；取骨料和粉料加入水进行混合，搅匀，制成砖坯，晾干；骨料添加量为30％‑50％，粉料添加量占比为50％‑70％；烘干烧制：将晾干的砖坯放入烘房，进行烘干、烧制，得到陶土烧结砖；其中，烘干参数包括：由室温逐步上升至95‑105℃，升温时间为2‑4天，达到95‑105℃后，继续烘干1‑3天；烧制参数包括：在900‑1000℃温度下烧制20‑25小时。制得的陶土烧结砖吸水性较高，结合砂石垫层，制成发酵仓地坪，该地坪下的制曲发酵温度与三合土地坪一致，适用于制曲高温高湿的密闭性发酵环境。
Argil sintered brick and terrace manufacturing method
一种陶土烧结砖及地坪制作方法
YAO CUIPING (author) / LIU SHENG (author) / YANG ZHIBO (author) / LIANG YALI (author) / CHEN SHUN (author) / CHENG YANBO (author) / LI DAPENG (author) / LIU LIPING (author) / JIAO FU (author) / LI DAIXIN (author)
2024-04-09
Patent
Electronic Resource
Chinese
Method for quickly building hollowed-out argil brick curtain wall
| European Patent Office | 2024
Lightweight argil and shale perforated ganged brick and production method
| European Patent Office | 2015
Sun-shading inhaul cable argil plate brick curtain wall structure
| European Patent Office | 2021