Multi-element rare earth doped modified bismuth ferrite-based ceramic and preparation method thereof
The invention relates to the technical field of dielectric materials, in particular to a multi-element rare earth doped modified bismuth ferrite-based ceramic and a preparation method thereof, a standard solid-phase reaction sintering method is adopted, and the process comprises the steps of material drying, weighing according to a correct stoichiometric ratio, burdening, ball milling, drying, sieving, tabletting to obtain a BiFeO3-based ceramic green body, and finally sintering at the high temperature of 900 DEG C to obtain the ceramic. The ceramic shows good ferroelectricity and magnetism and has excellent magnetoelectric coupling, meanwhile, the preparation method is easy to implement, and mass production can be achieved.
本发明涉及电介质材料技术领域，具体涉及一种多元稀土掺杂改性铁酸铋基陶瓷及其制备方法，采用标准固相反应烧结法，其过程包括烘料、按照正确的化学计量比称重、配料、球磨、烘干、过筛、压片，得到BiFeO3基陶瓷生坯，最后在900℃的高温烧结成瓷。该陶瓷表现出良好的铁电性、磁性，且具有优异的磁电耦合，同时该制备方法实施简单、可大批量制作。
Multi-element rare earth doped modified bismuth ferrite-based ceramic and preparation method thereof
The invention relates to the technical field of dielectric materials, in particular to a multi-element rare earth doped modified bismuth ferrite-based ceramic and a preparation method thereof, a standard solid-phase reaction sintering method is adopted, and the process comprises the steps of material drying, weighing according to a correct stoichiometric ratio, burdening, ball milling, drying, sieving, tabletting to obtain a BiFeO3-based ceramic green body, and finally sintering at the high temperature of 900 DEG C to obtain the ceramic. The ceramic shows good ferroelectricity and magnetism and has excellent magnetoelectric coupling, meanwhile, the preparation method is easy to implement, and mass production can be achieved.
本发明涉及电介质材料技术领域，具体涉及一种多元稀土掺杂改性铁酸铋基陶瓷及其制备方法，采用标准固相反应烧结法，其过程包括烘料、按照正确的化学计量比称重、配料、球磨、烘干、过筛、压片，得到BiFeO3基陶瓷生坯，最后在900℃的高温烧结成瓷。该陶瓷表现出良好的铁电性、磁性，且具有优异的磁电耦合，同时该制备方法实施简单、可大批量制作。
Multi-element rare earth doped modified bismuth ferrite-based ceramic and preparation method thereof
一种多元稀土掺杂改性铁酸铋基陶瓷及其制备方法
2024-05-17
Patent
Electronic Resource
Chinese
IPC:
C04B
Kalk
,
LIME
Rare earth element doped Z-type ferrite material and preparation method thereof
| European Patent Office | 2023
Bismuth lanthanum ferrite ceramic and preparation method thereof
| European Patent Office | 2015
Bismuth ferrite-based leadless piezoelectric ceramic material and preparation method thereof
| European Patent Office | 2023
Lead-free bismuth ferrite-based ceramic material and preparation method thereof
| European Patent Office | 2020
| European Patent Office | 2020