Glass rubber non-autoclaved aerated concrete wall material and preparation method thereof
The invention relates to the technical field of building materials, in particular to a glass rubber non-autoclaved aerated concrete wall material and a preparation method thereof. The wall material provided by the invention comprises the following components in parts by weight: 270-360 parts of a siliceous material; 210 to 300 parts of a calcium material; 12 to 30 parts of gypsum; 3 to 24 parts of rubber particles; 1.8 to 5.4 parts of fiber; 0.6 to 3.0 parts of a gas forming agent; 0.48 to 5.0 parts of a foam stabilizer; 0.18 to 5.7 parts of an early strength agent; 1.2 to 3.6 parts of a waterproof agent; and 264 to 312 parts of water. The glass-rubber non-autoclaved aerated concrete is a homogeneous single wall material prepared from the waste glass and the waste rubber under the synergistic effect of all the raw materials, a composite insulation board is not needed, the problems that the construction process is tedious, and the insulation board falls off are solved, and the glass-rubber non-autoclaved aerated concrete is light in weight, high in strength and excellent in insulation performance. The glass rubber non-autoclaved aerated concrete wall material adopts a non-autoclaved curing process, the equipment and energy investment is low, the preparation process is simple, and the preparation efficiency is high.
本发明涉及建筑材料技术领域，具体涉及一种玻橡免蒸压加气混凝土墙体材料及其制备方法。本发明提供的墙体材料包括按重量份数计的以下组分：硅质材料：270~360份；钙质材料210~300份；石膏：12~30份；橡胶颗粒：3~24份；纤维：1.8~5.4份；发气剂：0.6~3.0份；稳泡剂：0.48~5.0份；早强剂0.18~5.7份；防水剂：1.2~3.6份；水：264~312份。本发明中所述玻橡免蒸压加气混凝土是利用废玻璃和废橡胶，各原料协同作用下制备得到的均质单一墙体材料，无需复合保温板，避免了施工工艺繁琐、保温板脱落等问题，并且轻质高强、保温性能优异。本发明中所述玻橡免蒸压加气混凝土墙体材料采用免蒸压养护工艺，设备与能源投资较低，制备工艺简单、制备效率高。
Glass rubber non-autoclaved aerated concrete wall material and preparation method thereof
The invention relates to the technical field of building materials, in particular to a glass rubber non-autoclaved aerated concrete wall material and a preparation method thereof. The wall material provided by the invention comprises the following components in parts by weight: 270-360 parts of a siliceous material; 210 to 300 parts of a calcium material; 12 to 30 parts of gypsum; 3 to 24 parts of rubber particles; 1.8 to 5.4 parts of fiber; 0.6 to 3.0 parts of a gas forming agent; 0.48 to 5.0 parts of a foam stabilizer; 0.18 to 5.7 parts of an early strength agent; 1.2 to 3.6 parts of a waterproof agent; and 264 to 312 parts of water. The glass-rubber non-autoclaved aerated concrete is a homogeneous single wall material prepared from the waste glass and the waste rubber under the synergistic effect of all the raw materials, a composite insulation board is not needed, the problems that the construction process is tedious, and the insulation board falls off are solved, and the glass-rubber non-autoclaved aerated concrete is light in weight, high in strength and excellent in insulation performance. The glass rubber non-autoclaved aerated concrete wall material adopts a non-autoclaved curing process, the equipment and energy investment is low, the preparation process is simple, and the preparation efficiency is high.
本发明涉及建筑材料技术领域，具体涉及一种玻橡免蒸压加气混凝土墙体材料及其制备方法。本发明提供的墙体材料包括按重量份数计的以下组分：硅质材料：270~360份；钙质材料210~300份；石膏：12~30份；橡胶颗粒：3~24份；纤维：1.8~5.4份；发气剂：0.6~3.0份；稳泡剂：0.48~5.0份；早强剂0.18~5.7份；防水剂：1.2~3.6份；水：264~312份。本发明中所述玻橡免蒸压加气混凝土是利用废玻璃和废橡胶，各原料协同作用下制备得到的均质单一墙体材料，无需复合保温板，避免了施工工艺繁琐、保温板脱落等问题，并且轻质高强、保温性能优异。本发明中所述玻橡免蒸压加气混凝土墙体材料采用免蒸压养护工艺，设备与能源投资较低，制备工艺简单、制备效率高。
Glass rubber non-autoclaved aerated concrete wall material and preparation method thereof
一种玻橡免蒸压加气混凝土墙体材料及其制备方法
PENG XIAOTONG (author) / LI MIN (author) / WANG JUNPENG (author) / LIN CHEN (author) / LIU XIAOHUI (author) / ZHANG YAO (author)
2024-08-09
Patent
Electronic Resource
Chinese
Autoclaved aerated concrete, autoclaved aerated concrete slab and preparation method thereof
| European Patent Office | 2020
Autoclaved aerated concrete material and preparation method thereof
| European Patent Office | 2024
| European Patent Office | 2023
Autoclaved aerated concrete material and preparation method thereof
| European Patent Office | 2024
Glass fiber autoclaved aerated concrete and preparation method thereof
| European Patent Office | 2015