Ice crack glaze, ice crack glaze, preparation method of ice crack glaze and ice crack ceramic
The invention relates to the field of ceramic preparation, and discloses ice crack glaze, ice crack glaze, a preparation method of the ice crack glaze and ice crack ceramic. The ice crack glaze material is prepared from the following components in percentage by weight: 55 to 72 percent of SiO2, 8.0 to 23 percent of Al2O3, 1.5 to 10 percent of Na2O, 4.0 to 6.0 percent of K2O, 4.0 to 8.5 percent of CaO, 0 to 2.0 percent of TiO2, 0 to 3.5 percent of ZnO and 0 to 6.0 percent of BaO; wherein the total content of SiO2 and Al2O3 is less than or equal to 81wt%, and the total content of Na2O and K2O is less than or equal to 14wt%. The ice crack glaze can be used for preparing an ice crack plate with accurate size, the ice crack glaze is not easy to crack or delaminate, and under the preferable condition, the ice crack glaze has more fine cracks, more laminations, strong layering sense, good ice crack effect and more bubbles. In addition, the firing temperature of the ice crack glaze is lower and is less than or equal to 1200 DEG C.
本发明涉及陶瓷制备领域，公开了冰裂纹釉料、冰裂纹釉及其制备方法和冰裂纹陶瓷。该冰裂纹釉料包括55‑72wt％的SiO2、8.0‑23wt％的Al2O3、1.5‑10wt％的Na2O、4.0‑6.0wt％的K2O、4.0‑8.5wt％的CaO、0‑2.0wt％的TiO2、0‑3.5wt％的ZnO和0‑6.0wt％的BaO；其中，SiO2和Al2O3的总含量≤81wt％，Na2O和K2O的总含量≤14wt％。该冰裂纹釉料能够制备尺寸精确的冰裂纹板，冰裂纹釉不易破裂或者脱层，并且在优选情况下，冰裂纹釉的细碎裂纹多，层叠多，层次感强，冰裂效果好，气泡多。此外，冰裂纹釉的烧成温度也更低，≤1200℃。
Ice crack glaze, ice crack glaze, preparation method of ice crack glaze and ice crack ceramic
The invention relates to the field of ceramic preparation, and discloses ice crack glaze, ice crack glaze, a preparation method of the ice crack glaze and ice crack ceramic. The ice crack glaze material is prepared from the following components in percentage by weight: 55 to 72 percent of SiO2, 8.0 to 23 percent of Al2O3, 1.5 to 10 percent of Na2O, 4.0 to 6.0 percent of K2O, 4.0 to 8.5 percent of CaO, 0 to 2.0 percent of TiO2, 0 to 3.5 percent of ZnO and 0 to 6.0 percent of BaO; wherein the total content of SiO2 and Al2O3 is less than or equal to 81wt%, and the total content of Na2O and K2O is less than or equal to 14wt%. The ice crack glaze can be used for preparing an ice crack plate with accurate size, the ice crack glaze is not easy to crack or delaminate, and under the preferable condition, the ice crack glaze has more fine cracks, more laminations, strong layering sense, good ice crack effect and more bubbles. In addition, the firing temperature of the ice crack glaze is lower and is less than or equal to 1200 DEG C.
本发明涉及陶瓷制备领域，公开了冰裂纹釉料、冰裂纹釉及其制备方法和冰裂纹陶瓷。该冰裂纹釉料包括55‑72wt％的SiO2、8.0‑23wt％的Al2O3、1.5‑10wt％的Na2O、4.0‑6.0wt％的K2O、4.0‑8.5wt％的CaO、0‑2.0wt％的TiO2、0‑3.5wt％的ZnO和0‑6.0wt％的BaO；其中，SiO2和Al2O3的总含量≤81wt％，Na2O和K2O的总含量≤14wt％。该冰裂纹釉料能够制备尺寸精确的冰裂纹板，冰裂纹釉不易破裂或者脱层，并且在优选情况下，冰裂纹釉的细碎裂纹多，层叠多，层次感强，冰裂效果好，气泡多。此外，冰裂纹釉的烧成温度也更低，≤1200℃。
Ice crack glaze, ice crack glaze, preparation method of ice crack glaze and ice crack ceramic
冰裂纹釉料、冰裂纹釉及其制备方法和冰裂纹陶瓷
LIN JIAFU (author) / ZHANG CAN (author) / HUANG FENG (author) / LI MAOFENG (author) / YANG PAN WEN (author)
2024-08-13
Patent
Electronic Resource
Chinese
Watermelon crack glaze with crack effect and preparation method thereof
| European Patent Office | 2023
Spherical crown crack ceramic art glaze and preparation method thereof
| European Patent Office | 2023