High-strength stone-like brick and preparation method thereof
The invention relates to the technical field of textile equipment, in particular to a high-strength stone-like brick and a preparation method thereof.The stone-like brick is prepared from, by mass, 10-20 parts of cement, 20-40 parts of ball clay, 15-20 parts of stone powder, 10-15 parts of coarse aggregate, 8-10 parts of fine aggregate, 5-10 parts of fiber additive and 10-20 parts of water; the anti-corrosion coating comprises the following components in parts by weight: 5-10 parts of feldspar, 5-10 parts of quartz, 10-15 parts of kaolin, 5-8 parts of moissanite, 5-8 parts of an oxidation additive, 3-7 parts of a metal additive, 2-4 parts of calcium carbonate, 2-3 parts of epoxy resin and 5-10 parts of water. According to the high-strength stone-like brick, the preparation method thereof and the glaze surface of the stone-like brick, through the metal additive and the oxidation additive, the strength of the glaze body on the surface of the stone-like brick is effectively improved, so that the surface strength of the stone-like brick is improved, the problem that the stone-like brick is broken due to long-term use or external force is reduced, the strength of the stone-like brick is improved, and the service life of the stone-like brick is prolonged.
本发明涉及纺织设备技术领域，尤其为一种高强度仿石砖及其制备方法，仿石砖包括按质量份数计包括以下原料，水泥10—20份、球土20—40份、石粉15—20份、粗骨料10—15份、细骨料8—10份、纤维添加物5—10份和水10—20份，长石5—10份、石英5—10份、高岭土10—15份、莫桑石5—8份、氧化添加剂5—8份、金属添加物3—7份、碳酸钙2—4份、环氧树脂2—3份和水5—10份。该高强度仿石砖及其制备方法，仿石砖的釉面通过金属添加物和氧化添加剂，有效地提升仿石砖表面釉体的强度，使得仿石砖的表面的强度得到提升，减少仿石砖长期使用或是受外力出现碎裂的问题，提升仿石砖的强度和使用寿命。
High-strength stone-like brick and preparation method thereof
The invention relates to the technical field of textile equipment, in particular to a high-strength stone-like brick and a preparation method thereof.The stone-like brick is prepared from, by mass, 10-20 parts of cement, 20-40 parts of ball clay, 15-20 parts of stone powder, 10-15 parts of coarse aggregate, 8-10 parts of fine aggregate, 5-10 parts of fiber additive and 10-20 parts of water; the anti-corrosion coating comprises the following components in parts by weight: 5-10 parts of feldspar, 5-10 parts of quartz, 10-15 parts of kaolin, 5-8 parts of moissanite, 5-8 parts of an oxidation additive, 3-7 parts of a metal additive, 2-4 parts of calcium carbonate, 2-3 parts of epoxy resin and 5-10 parts of water. According to the high-strength stone-like brick, the preparation method thereof and the glaze surface of the stone-like brick, through the metal additive and the oxidation additive, the strength of the glaze body on the surface of the stone-like brick is effectively improved, so that the surface strength of the stone-like brick is improved, the problem that the stone-like brick is broken due to long-term use or external force is reduced, the strength of the stone-like brick is improved, and the service life of the stone-like brick is prolonged.
本发明涉及纺织设备技术领域，尤其为一种高强度仿石砖及其制备方法，仿石砖包括按质量份数计包括以下原料，水泥10—20份、球土20—40份、石粉15—20份、粗骨料10—15份、细骨料8—10份、纤维添加物5—10份和水10—20份，长石5—10份、石英5—10份、高岭土10—15份、莫桑石5—8份、氧化添加剂5—8份、金属添加物3—7份、碳酸钙2—4份、环氧树脂2—3份和水5—10份。该高强度仿石砖及其制备方法，仿石砖的釉面通过金属添加物和氧化添加剂，有效地提升仿石砖表面釉体的强度，使得仿石砖的表面的强度得到提升，减少仿石砖长期使用或是受外力出现碎裂的问题，提升仿石砖的强度和使用寿命。
High-strength stone-like brick and preparation method thereof
一种高强度仿石砖及其制备方法
CHEN HAIYA (author) / GAO XUEXIANG (author)
2024-11-19
Patent
Electronic Resource
Chinese
High-strength stone-like brick and preparation method thereof
| European Patent Office | 2024
High-strength stone-like water permeable brick and preparation method thereof
| European Patent Office | 2022
High-strength stone-imitating brick and preparation method thereof
| European Patent Office | 2020
Glutenite stone-like brick and preparation method thereof
| European Patent Office | 2020