CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR
PROBLEM TO BE SOLVED: To provide a cement composition having high flowability (e.g. flow value (zero placement) 250 mm or more) before curing and exhibiting high compressive strength (e.g. 250 N/mmor more) after curing.SOLUTION: There is provided a cement composition containing a polishing treated article of moderate heat portland cement or low heat portland cement and silica fume having BET specific surface area of 10 to 25 m/g. The cement composition preferably contains an inorganic powder having 50% weight cumulative particle diameter of 0.8 to 5 μm. Also the polishing treated article of the moderate heat portland cement or the low heat portland cement contains preferably coarse particles with particle diameter of 20 μm or more by deforming a shape from angular surface part to round by a polishing treatment of particles constituting the moderate heat portland cement or the low heat portland cement and fine particles with particle diameter of less than 20 μm generated by the polishing treatment.SELECTED DRAWING: Figure 1
【課題】硬化前には高い流動性（例えば、フロー値（０打ち）が２５０ｍｍ以上）を有し、かつ硬化後には高い圧縮強度（例えば、２５０Ｎ／ｍｍ２以上）を発現するセメント組成物を提供する。【解決手段】中庸熱ポルトランドセメント又は低熱ポルトランドセメントの研磨処理物、及び、ＢＥＴ比表面積が１０〜２５ｍ２／ｇのシリカフュームを含むセメント組成物。セメント組成物は、好ましくは、５０％重量累積粒径が０．８〜５μｍの無機粉末を含む。また、中庸熱ポルトランドセメント又は低熱ポルトラドセメントの研磨処理物は、好ましくは、中庸熱ポルトランドセメント又は低熱ポルトランドセメントを構成する粒子を研磨処理してなる、角張った表面部分を丸みを帯びた形状に変形させてなる粒径２０μｍ以上の粗粒子、及び、研磨処理によって生じる粒径２０μｍ未満の微粒子を含む。【選択図】図１
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR
PROBLEM TO BE SOLVED: To provide a cement composition having high flowability (e.g. flow value (zero placement) 250 mm or more) before curing and exhibiting high compressive strength (e.g. 250 N/mmor more) after curing.SOLUTION: There is provided a cement composition containing a polishing treated article of moderate heat portland cement or low heat portland cement and silica fume having BET specific surface area of 10 to 25 m/g. The cement composition preferably contains an inorganic powder having 50% weight cumulative particle diameter of 0.8 to 5 μm. Also the polishing treated article of the moderate heat portland cement or the low heat portland cement contains preferably coarse particles with particle diameter of 20 μm or more by deforming a shape from angular surface part to round by a polishing treatment of particles constituting the moderate heat portland cement or the low heat portland cement and fine particles with particle diameter of less than 20 μm generated by the polishing treatment.SELECTED DRAWING: Figure 1
【課題】硬化前には高い流動性（例えば、フロー値（０打ち）が２５０ｍｍ以上）を有し、かつ硬化後には高い圧縮強度（例えば、２５０Ｎ／ｍｍ２以上）を発現するセメント組成物を提供する。【解決手段】中庸熱ポルトランドセメント又は低熱ポルトランドセメントの研磨処理物、及び、ＢＥＴ比表面積が１０〜２５ｍ２／ｇのシリカフュームを含むセメント組成物。セメント組成物は、好ましくは、５０％重量累積粒径が０．８〜５μｍの無機粉末を含む。また、中庸熱ポルトランドセメント又は低熱ポルトラドセメントの研磨処理物は、好ましくは、中庸熱ポルトランドセメント又は低熱ポルトランドセメントを構成する粒子を研磨処理してなる、角張った表面部分を丸みを帯びた形状に変形させてなる粒径２０μｍ以上の粗粒子、及び、研磨処理によって生じる粒径２０μｍ未満の微粒子を含む。【選択図】図１
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREFOR
セメント組成物及びその製造方法
NAKAYAMA RISA (author) / KONO KATSUYA (author) / TADA KATSUHIKO (author) / MORI HIROAKI (author) / SUGIYAMA SHINGO (author) / MAEHORI SHINPEI (author)