LINING FOR REFRACTORY CRUCIBLE FOR REFINING SILICONE MELT, AND METHOD FOR REFINING SILICONE MELT USING THE CRUCIBLE
PROBLEM TO BE SOLVED: To provide a refractory crucible preventing the intrusion of boron and phosphorous contaminants when a silicon melt is recrystallized to perform the refining of silicone.SOLUTION: Provided is a crucible for containing a molten silicon mixture, having: at least one alumina-containing refractory material being at least one refractory material having at least one inside face prescribing the inside for receiving a molten silicon mixture; and a lining with a thickness of 2 to 10 mm being a dried lining for forming a lining formed of a mixture of silicon carbide grains mixed into colloidal alumina vapor-deposited on the inside face and including silicon carbide grains at the substantially solid alumina binder. The colloidal alumina includes alumina grains suspended in water, and the alumina grains have a size of 20 to 50 nm.SELECTED DRAWING: Figure 1
【課題】シリコン溶融物を再結晶化させて、シリコンの精製を行う際に、ホウ素、リン汚染物の混入を防止する耐火性るつぼ提供。【解決手段】溶融シリコン混合物を受け入れるための内部を規定する少なくとも１つの内面を有する少なくとも１つの耐火性材料であって、アルミナを含む、少なくとも１つの耐火性材料と、内面上に蒸着したコロイド状アルミナ中に混合したシリコンカーバイド粒子の混合物から形成され、実質的に固体のアルミナバインダー内にシリコンカーバイド粒子を含むライニングを形成するために乾燥させたライニングであって、２〜１０ｍｍの厚さを有する、ライニングとを含む、溶融シリコン混合物を含有するためのるつぼ。コロイド状アルミナが、水に懸濁されたアルミナ粒子を含み、アルミナ粒子が、２０〜５０ｎｍのサイズを有する、るつぼ。【選択図】図１
LINING FOR REFRACTORY CRUCIBLE FOR REFINING SILICONE MELT, AND METHOD FOR REFINING SILICONE MELT USING THE CRUCIBLE
PROBLEM TO BE SOLVED: To provide a refractory crucible preventing the intrusion of boron and phosphorous contaminants when a silicon melt is recrystallized to perform the refining of silicone.SOLUTION: Provided is a crucible for containing a molten silicon mixture, having: at least one alumina-containing refractory material being at least one refractory material having at least one inside face prescribing the inside for receiving a molten silicon mixture; and a lining with a thickness of 2 to 10 mm being a dried lining for forming a lining formed of a mixture of silicon carbide grains mixed into colloidal alumina vapor-deposited on the inside face and including silicon carbide grains at the substantially solid alumina binder. The colloidal alumina includes alumina grains suspended in water, and the alumina grains have a size of 20 to 50 nm.SELECTED DRAWING: Figure 1
【課題】シリコン溶融物を再結晶化させて、シリコンの精製を行う際に、ホウ素、リン汚染物の混入を防止する耐火性るつぼ提供。【解決手段】溶融シリコン混合物を受け入れるための内部を規定する少なくとも１つの内面を有する少なくとも１つの耐火性材料であって、アルミナを含む、少なくとも１つの耐火性材料と、内面上に蒸着したコロイド状アルミナ中に混合したシリコンカーバイド粒子の混合物から形成され、実質的に固体のアルミナバインダー内にシリコンカーバイド粒子を含むライニングを形成するために乾燥させたライニングであって、２〜１０ｍｍの厚さを有する、ライニングとを含む、溶融シリコン混合物を含有するためのるつぼ。コロイド状アルミナが、水に懸濁されたアルミナ粒子を含み、アルミナ粒子が、２０〜５０ｎｍのサイズを有する、るつぼ。【選択図】図１
LINING FOR REFRACTORY CRUCIBLE FOR REFINING SILICONE MELT, AND METHOD FOR REFINING SILICONE MELT USING THE CRUCIBLE
シリコン溶融物の精製のための耐火性るつぼの表面のためのライニングおよび当該るつぼを使用するシリコン溶融物の精製方法
ALAIN TURENNE (author) / CHRISTAIN ALFRED (author)
2017-01-05
Patent
Electronic Resource
Japanese
Nitridation of crucible skulls from melt refining
| TIBKAT | 1960
Preparation method of disposable lining crucible and disposable lining crucible
| European Patent Office | 2023
Desulphurization during VIM Refining Ni-base Superalloy using CaO Crucible
| British Library Online Contents | 2003
Denitrogenation during vacuum induction melting refining Ni base superalloy using CaO crucible
| British Library Online Contents | 2002