SLAG POWDER AND MANUFACTURING METHOD OF SLAG POWDER
PROBLEM TO BE SOLVED: To provide a slag powder capable of suppressing reduction of reaction activity of the slag powder and being used for a blast furnace cement having suppressed reduction of compressive strength of a cured article regardless of presence or absence of a deteriorated raw material slag and a manufacturing method of the slag powder.SOLUTION: This invention relates to a slag powder having a Blaine specific surface area of 4000-7000 cm/g, a 24 μm sieve residual component measured by a laser diffraction type particle size distribution measurement method of 30 vol.% or less. There is provided a manufacturing method of the slag powder including a process of preparing a raw material slag with a Blaine specific surface area of 4000 cm/g, a 24 μm sieve residual component measured by a laser diffraction type particle size distribution measurement method of 30 vol.% or less to obtain the slag powder.SELECTED DRAWING: None
【課題】原料スラグの劣化の有無に関わらず、スラグ粉の反応活性の低下を抑制することができ、硬化物の圧縮強度の低下を抑制した高炉セメントに使用し得るスラグ粉及びスラグ粉の製造方法を提供する。【解決手段】本発明は、ブレーン比表面積が４０００〜７０００ｃｍ２／ｇであり、レーザー回折式粒度分布測定法によって測定された２４μｍ篩残分が３０体積％以下である、スラグ粉に関する。また、本発明は、原料スラグを、ブレーン比表面積４０００ｃｍ２／ｇ、且つレーザー回折式粒度分布測定法によって測定される２４μｍ篩残分が３０体積％以下となるように調製してスラグ粉を得る工程を含む、スラグ粉の製造方法に関する。【選択図】なし
SLAG POWDER AND MANUFACTURING METHOD OF SLAG POWDER
PROBLEM TO BE SOLVED: To provide a slag powder capable of suppressing reduction of reaction activity of the slag powder and being used for a blast furnace cement having suppressed reduction of compressive strength of a cured article regardless of presence or absence of a deteriorated raw material slag and a manufacturing method of the slag powder.SOLUTION: This invention relates to a slag powder having a Blaine specific surface area of 4000-7000 cm/g, a 24 μm sieve residual component measured by a laser diffraction type particle size distribution measurement method of 30 vol.% or less. There is provided a manufacturing method of the slag powder including a process of preparing a raw material slag with a Blaine specific surface area of 4000 cm/g, a 24 μm sieve residual component measured by a laser diffraction type particle size distribution measurement method of 30 vol.% or less to obtain the slag powder.SELECTED DRAWING: None
【課題】原料スラグの劣化の有無に関わらず、スラグ粉の反応活性の低下を抑制することができ、硬化物の圧縮強度の低下を抑制した高炉セメントに使用し得るスラグ粉及びスラグ粉の製造方法を提供する。【解決手段】本発明は、ブレーン比表面積が４０００〜７０００ｃｍ２／ｇであり、レーザー回折式粒度分布測定法によって測定された２４μｍ篩残分が３０体積％以下である、スラグ粉に関する。また、本発明は、原料スラグを、ブレーン比表面積４０００ｃｍ２／ｇ、且つレーザー回折式粒度分布測定法によって測定される２４μｍ篩残分が３０体積％以下となるように調製してスラグ粉を得る工程を含む、スラグ粉の製造方法に関する。【選択図】なし
SLAG POWDER AND MANUFACTURING METHOD OF SLAG POWDER
スラグ粉及びスラグ粉の製造方法
MIYAWAKI KENJI (author)
2017-06-22
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
/
C21B
Gewinnung von Eisen oder Stahl
,
MANUFACTURE OF IRON OR STEEL
/
F27D
Einzelheiten oder Zubehör für Industrieöfen, Schachtöfen, Brennöfen oder Retorten, soweit sie nicht auf eine Ofenart eingeschränkt sind
,
DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS, OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
| European Patent Office | 2022
Slag mineral powder grinding aid and slag mineral powder grinding method
| European Patent Office | 2022
Paving stone concrete prepared from steel slag powder and mineral slag powder
| European Patent Office | 2015
Steel slag powder-ferromanganese slag powder composite admixture and preparation process thereof
| European Patent Office | 2020