PROBLEM TO BE SOLVED: To provide a cement-based self leveling mortar suitable for application with ultrathin application thickness, for example 5 mm or less.SOLUTION: There is provided a self leveling mortar containing Portland cement of 100 pts.mass, a cellulose derivative with viscosity at 20°C of 1500 to 15000 mPa s of 0.2 to 0.5 pt.mass, a fiber with length of 1 to 5 mm of 0.1 to 0.3 pt.mass, a water reducing agent of 0.5 to 1.0 pt.mass, an expansive admixture of 4.0 to 12.0 pts.mass, a dry shrinkage reduction agent of 0.5 to 1.5 pts.mass and limestone fine aggregate with particle diameter of over 150 μm (α) and limestone fine aggregate with particle diameter of 150 μm or less (β) of 150 to 220 pts.mass with mass ratio (β)/(α) of 0.7 to 2.0.SELECTED DRAWING: None
【課題】 例えば5mm以下の極薄の施工厚みでの施工に適したセメント系のセルフレベリング性モルタルの提供を課題とする。【解決手段】 ポルトランドセメント100質量部、20℃の粘性が1500〜15000mPa・sのセルロース誘導体0.2〜0.5質量部、長さ1〜5mmの繊維0.1〜0.3質量部、減水剤0.5〜1.0質量部、膨張材4.0〜12.0質量部、乾燥収縮低減剤0.5〜1.5質量部、粒子径150μmを超える石灰石細骨材(α)及び粒子径150μm以下の石灰石細骨材(β)を150〜220質量部含有し、質量比で(β)/(α)が0.7〜2.0であることを特徴とするセルフレベリング性モルタル。【選択図】 なし
PROBLEM TO BE SOLVED: To provide a cement-based self leveling mortar suitable for application with ultrathin application thickness, for example 5 mm or less.SOLUTION: There is provided a self leveling mortar containing Portland cement of 100 pts.mass, a cellulose derivative with viscosity at 20°C of 1500 to 15000 mPa s of 0.2 to 0.5 pt.mass, a fiber with length of 1 to 5 mm of 0.1 to 0.3 pt.mass, a water reducing agent of 0.5 to 1.0 pt.mass, an expansive admixture of 4.0 to 12.0 pts.mass, a dry shrinkage reduction agent of 0.5 to 1.5 pts.mass and limestone fine aggregate with particle diameter of over 150 μm (α) and limestone fine aggregate with particle diameter of 150 μm or less (β) of 150 to 220 pts.mass with mass ratio (β)/(α) of 0.7 to 2.0.SELECTED DRAWING: None
【課題】 例えば5mm以下の極薄の施工厚みでの施工に適したセメント系のセルフレベリング性モルタルの提供を課題とする。【解決手段】 ポルトランドセメント100質量部、20℃の粘性が1500〜15000mPa・sのセルロース誘導体0.2〜0.5質量部、長さ1〜5mmの繊維0.1〜0.3質量部、減水剤0.5〜1.0質量部、膨張材4.0〜12.0質量部、乾燥収縮低減剤0.5〜1.5質量部、粒子径150μmを超える石灰石細骨材(α)及び粒子径150μm以下の石灰石細骨材(β)を150〜220質量部含有し、質量比で(β)/(α)が0.7〜2.0であることを特徴とするセルフレベリング性モルタル。【選択図】 なし
SELF LEVELING MORTAR
セルフレベリング性モルタル