CASTABLE REFRACTORY FOR COKE OVEN
PROBLEM TO BE SOLVED: To provide a method for obtaining a castable refractory, used as a door block for a coke oven lid, in which: cracks are prevented from progressing; and longer life span is achieved by improving thermal spalling resistance.SOLUTION: A cordierite sintered compact having a porosity of 20-30% is obtained by calcinating, as raw materials: 20-90 mass% of a cordierite material; an alumina material; an alumina-silica material; silica fine powder; and a hardener, at 1,000-1,350°C for 50 hours or longer. A method for producing a cordierite castable refractory containing 20-90 mass% of ground material of the cordierite sintered compact includes grinding and refining the cordierite sintered compact. The cordierite castable refractory comprises: 20-90 mass% of the cordierite material; the alumina material; the alumina-silica material; the silica fine powder; and the hardener, while containing the raw materials in the cordierite sintered compact.SELECTED DRAWING: None
【課題】亀裂の進展を抑え、耐熱スポーリング性向上による長寿命化が可能なコークス炉炉蓋のドアブロックとして使用するキャスタブル耐火物を得る方法。【解決手段】コーディエライト質原料を２０〜９０質量％とアルミナ質原料、アルミナ-シリカ質原料、シリカ微粉、硬化剤を原料とし、当該原料を１０００℃〜１３５０℃で５０時間以上焼成して気孔率２０〜３０％のコーディエライト質焼結体を得る。次いで、前記コーディエライト質焼結体を粉砕・調粒して、前記コーディエライト質焼結体の粉砕原料を２０〜９０質量％配合するコーディエライト質キャスタブル耐火物の製造方法である。前記コーディエライト質キャスタブル耐火物は、前記コーディエライト質焼結体中の原料を含めて、コーディエライト質原料２０〜９０質量％、アルミナ質原料、アルミナ-シリカ質原料、シリカ微粉、硬化剤からなる。【選択図】 なし
CASTABLE REFRACTORY FOR COKE OVEN
PROBLEM TO BE SOLVED: To provide a method for obtaining a castable refractory, used as a door block for a coke oven lid, in which: cracks are prevented from progressing; and longer life span is achieved by improving thermal spalling resistance.SOLUTION: A cordierite sintered compact having a porosity of 20-30% is obtained by calcinating, as raw materials: 20-90 mass% of a cordierite material; an alumina material; an alumina-silica material; silica fine powder; and a hardener, at 1,000-1,350°C for 50 hours or longer. A method for producing a cordierite castable refractory containing 20-90 mass% of ground material of the cordierite sintered compact includes grinding and refining the cordierite sintered compact. The cordierite castable refractory comprises: 20-90 mass% of the cordierite material; the alumina material; the alumina-silica material; the silica fine powder; and the hardener, while containing the raw materials in the cordierite sintered compact.SELECTED DRAWING: None
【課題】亀裂の進展を抑え、耐熱スポーリング性向上による長寿命化が可能なコークス炉炉蓋のドアブロックとして使用するキャスタブル耐火物を得る方法。【解決手段】コーディエライト質原料を２０〜９０質量％とアルミナ質原料、アルミナ-シリカ質原料、シリカ微粉、硬化剤を原料とし、当該原料を１０００℃〜１３５０℃で５０時間以上焼成して気孔率２０〜３０％のコーディエライト質焼結体を得る。次いで、前記コーディエライト質焼結体を粉砕・調粒して、前記コーディエライト質焼結体の粉砕原料を２０〜９０質量％配合するコーディエライト質キャスタブル耐火物の製造方法である。前記コーディエライト質キャスタブル耐火物は、前記コーディエライト質焼結体中の原料を含めて、コーディエライト質原料２０〜９０質量％、アルミナ質原料、アルミナ-シリカ質原料、シリカ微粉、硬化剤からなる。【選択図】 なし
CASTABLE REFRACTORY FOR COKE OVEN
コークス炉用キャスタブル耐火物
NISHIDA SHIGEFUMI (author) / HIGASHIKAWA NATSUMI (author)
2018-04-05
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
/
C10B
Zersetzende Destillation von kohlenstoffhaltigen Stoffen zur Erzeugung von Gas, Koks, Teer oder ähnlichen Stoffen
,
DESTRUCTIVE DISTILLATION OF CARBONACEOUS MATERIALS FOR PRODUCTION OF GAS, COKE, TAR, OR SIMILAR MATERIALS
/
F27D
Einzelheiten oder Zubehör für Industrieöfen, Schachtöfen, Brennöfen oder Retorten, soweit sie nicht auf eine Ofenart eingeschränkt sind
,
DETAILS OR ACCESSORIES OF FURNACES, KILNS, OVENS, OR RETORTS, IN SO FAR AS THEY ARE OF KINDS OCCURRING IN MORE THAN ONE KIND OF FURNACE
CASTABLE REFRACTORY COMPOSITION, CASTABLE REFRACTORY, AND METHOD OF PRODUCING CASTABLE REFRACTORY
| European Patent Office | 2022