DECORATIVE SHEET AND DECORATIVE MEMBER
PROBLEM TO BE SOLVED: To provide a decorative sheet and a decorative member having excellent processing performance and solvent resistance in a bent part of a decorative sheet and having excellent incombustibility.SOLUTION: There is provided a decorative sheet which uses a polyolefin-based resin film on a substrate and comprises a printed layer, a heat seal agent layer, an acrylic resin layer and a fluororesin layer in this order, wherein the heat seal agent layer is constituted by blending an isocyanate-based curing agent in acryl/vinyl acetate chloride/polyester=1/1/1, the acrylic resin layer and a laminate part of the fluororesin layer have an elongation rate of 120% or more and 140% or less when a No. 1 dumbbell-shaped test piece prepared according to JIS K 6251 is elongated to break at a pulling rate of 50 mm/min in a vertical direction to the formation direction under 5°C atmosphere and a primer layer is provided on the back face of the polyolefin-based resin film.SELECTED DRAWING: Figure 1
【課題】化粧シートの、折り曲げ部における加工性能、耐溶剤性能に優れ、かつ不燃性能を備えた、化粧シート及び化粧部材を提供することを課題とする。【解決手段】化粧シートであって、基材にポリオレフィン系樹脂フィルムを用い、印刷層、ヒートシール剤層、アクリル樹脂層、フッ素樹脂層とが、この順に備えられており、ヒートシール剤層は、アクリル／塩化酢酸ビニル／ポリエステル＝１／１／１にイソシアネート系硬化剤が配合されて構成されており、アクリル樹脂層と、フッ素樹脂層の積層体部分は、ＪＩＳ Ｋ ６２５１に準拠して作成した１号ダンベル形状の試験片を、５℃雰囲気下で成形方向に対して垂直方向に、引っ張り速度５０ｍｍ／分で破断するまで延伸した際の延伸率が、１２０％以上、１４０％以下であり、ポリオレフィン系樹脂フィルムの裏面には、プライマー層が備えられていることを特徴とする化粧シート。【選択図】図１
DECORATIVE SHEET AND DECORATIVE MEMBER
PROBLEM TO BE SOLVED: To provide a decorative sheet and a decorative member having excellent processing performance and solvent resistance in a bent part of a decorative sheet and having excellent incombustibility.SOLUTION: There is provided a decorative sheet which uses a polyolefin-based resin film on a substrate and comprises a printed layer, a heat seal agent layer, an acrylic resin layer and a fluororesin layer in this order, wherein the heat seal agent layer is constituted by blending an isocyanate-based curing agent in acryl/vinyl acetate chloride/polyester=1/1/1, the acrylic resin layer and a laminate part of the fluororesin layer have an elongation rate of 120% or more and 140% or less when a No. 1 dumbbell-shaped test piece prepared according to JIS K 6251 is elongated to break at a pulling rate of 50 mm/min in a vertical direction to the formation direction under 5°C atmosphere and a primer layer is provided on the back face of the polyolefin-based resin film.SELECTED DRAWING: Figure 1
【課題】化粧シートの、折り曲げ部における加工性能、耐溶剤性能に優れ、かつ不燃性能を備えた、化粧シート及び化粧部材を提供することを課題とする。【解決手段】化粧シートであって、基材にポリオレフィン系樹脂フィルムを用い、印刷層、ヒートシール剤層、アクリル樹脂層、フッ素樹脂層とが、この順に備えられており、ヒートシール剤層は、アクリル／塩化酢酸ビニル／ポリエステル＝１／１／１にイソシアネート系硬化剤が配合されて構成されており、アクリル樹脂層と、フッ素樹脂層の積層体部分は、ＪＩＳ Ｋ ６２５１に準拠して作成した１号ダンベル形状の試験片を、５℃雰囲気下で成形方向に対して垂直方向に、引っ張り速度５０ｍｍ／分で破断するまで延伸した際の延伸率が、１２０％以上、１４０％以下であり、ポリオレフィン系樹脂フィルムの裏面には、プライマー層が備えられていることを特徴とする化粧シート。【選択図】図１
DECORATIVE SHEET AND DECORATIVE MEMBER
化粧シート及び化粧部材
ORIHARA TAKASHI (author) / TOMINAGA TAKASHI (author)
2018-08-23
Patent
Electronic Resource
Japanese
IPC:
B32B
LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
,
Schichtkörper, d.h. aus Ebenen oder gewölbten Schichten, z.B. mit zell- oder wabenförmiger Form, aufgebaute Erzeugnisse
/
C09J
ADHESIVES
,
Klebstoffe
/
E04F
FINISHING WORK ON BUILDINGS, e.g. STAIRS, FLOORS
,
Ausbau von Bauwerken, z.B. Treppen, Fußböden