REPAIR METHOD OF SALT-SHIELDING MORTAR
To provide a repair method of salt-shielding mortar capable of exhibiting little initial length change in association with its curing and forming a mortar hardened body with salt-shielding upon being integrated with a concrete structural body.SOLUTION: A repairing method of salt-shielding mortar comprises: a construction step of constructing mortar on a concrete structural body; and a forming step of forming a mortar cured body through curing the mortar, wherein the mortar is a mixture of an alumina cement composition of salt-shielding mortar and water. The alumina cement composition of the salt-shielding mortar includes the alumina cement and gypsum hemihydrate, the alumina cement including 55 mass% to 75 mass% of CA, 5 mass% to 8 mass% of C12A7, 10 mass% to 28 mass% of C4AF, and 2 mass% to 6 mass% of C2AS. A Blaine specific surface area of the alumina cement is from 2,000 cm2/g to 4,000 cm2/g, and a Blaine specific surface area of the gypsum hemihydrate is from 3,000 cm2/g to 6,000 cm2/g. A content of the gypsum hemihydrate is from 10 pts.mass to 24 pts.mass relative to 100 pts.mass of the alumina cement.SELECTED DRAWING: None
【課題】硬化に伴う初期の長さ変化量が小さく、コンクリート構造体と一体化したときに優れた遮塩性を有するモルタル硬化体を形成することが可能な、遮塩性モルタルの補修方法を提供すること。【解決手段】コンクリート構造体にモルタルを施工する施工工程と、上記モルタルを硬化させることによってモルタル硬化体を形成する形成工程と、を有する遮塩性モルタルの補修方法であって、上記モルタルが、遮塩性モルタル用アルミナセメント組成物と水との混合物であり、上記遮塩性モルタル用アルミナセメント組成物が、アルミナセメント及び半水石膏を含み、上記アルミナセメントが、ＣＡを５５質量％〜７５質量％、Ｃ１２Ａ７を５質量％〜８質量％、Ｃ４ＡＦを１０質量％〜２８質量％、及びＣ２ＡＳを２質量％〜６質量％含み、上記アルミナセメントのブレーン比表面積が、２０００ｃｍ２／ｇ〜４０００ｃｍ２／ｇであり、上記半水石膏のブレーン比表面積が、３０００ｃｍ２／ｇ〜６０００ｃｍ２／ｇであり、上記半水石膏の含有量が、上記アルミナセメント１００質量部に対して、１０質量部〜２４質量部である、遮塩性モルタルの補修方法を提供する。【選択図】なし
REPAIR METHOD OF SALT-SHIELDING MORTAR
To provide a repair method of salt-shielding mortar capable of exhibiting little initial length change in association with its curing and forming a mortar hardened body with salt-shielding upon being integrated with a concrete structural body.SOLUTION: A repairing method of salt-shielding mortar comprises: a construction step of constructing mortar on a concrete structural body; and a forming step of forming a mortar cured body through curing the mortar, wherein the mortar is a mixture of an alumina cement composition of salt-shielding mortar and water. The alumina cement composition of the salt-shielding mortar includes the alumina cement and gypsum hemihydrate, the alumina cement including 55 mass% to 75 mass% of CA, 5 mass% to 8 mass% of C12A7, 10 mass% to 28 mass% of C4AF, and 2 mass% to 6 mass% of C2AS. A Blaine specific surface area of the alumina cement is from 2,000 cm2/g to 4,000 cm2/g, and a Blaine specific surface area of the gypsum hemihydrate is from 3,000 cm2/g to 6,000 cm2/g. A content of the gypsum hemihydrate is from 10 pts.mass to 24 pts.mass relative to 100 pts.mass of the alumina cement.SELECTED DRAWING: None
【課題】硬化に伴う初期の長さ変化量が小さく、コンクリート構造体と一体化したときに優れた遮塩性を有するモルタル硬化体を形成することが可能な、遮塩性モルタルの補修方法を提供すること。【解決手段】コンクリート構造体にモルタルを施工する施工工程と、上記モルタルを硬化させることによってモルタル硬化体を形成する形成工程と、を有する遮塩性モルタルの補修方法であって、上記モルタルが、遮塩性モルタル用アルミナセメント組成物と水との混合物であり、上記遮塩性モルタル用アルミナセメント組成物が、アルミナセメント及び半水石膏を含み、上記アルミナセメントが、ＣＡを５５質量％〜７５質量％、Ｃ１２Ａ７を５質量％〜８質量％、Ｃ４ＡＦを１０質量％〜２８質量％、及びＣ２ＡＳを２質量％〜６質量％含み、上記アルミナセメントのブレーン比表面積が、２０００ｃｍ２／ｇ〜４０００ｃｍ２／ｇであり、上記半水石膏のブレーン比表面積が、３０００ｃｍ２／ｇ〜６０００ｃｍ２／ｇであり、上記半水石膏の含有量が、上記アルミナセメント１００質量部に対して、１０質量部〜２４質量部である、遮塩性モルタルの補修方法を提供する。【選択図】なし
REPAIR METHOD OF SALT-SHIELDING MORTAR
遮塩性モルタルの補修方法
KATAGIRI TOMOKI (author) / NUKITA MAKOTO (author) / TODA YASUHIKO (author)
2020-07-09
Patent
Electronic Resource
Japanese