ZIRCONIA-CARBON REFRACTORY MATERIAL, IMMERSION NOZZLE, AND METHOD FOR PRODUCING ZIRCONIA-CARBON REFRACTORY MATERIAL
To improve the corrosion resistance of a zirconia-carbon refractory material compared with a conventional technique.SOLUTION: There is provided a zirconia-carbon refractory material containing 70 mass% or more and 98 mass% or less of a zirconia raw material and 2 mass% or more and 30 mass% or less of a carbon raw material, wherein the zirconia raw material contains a first part which cannot pass through a sieve with a nominal aperture of 106 μm and a second part which can pass through the sieve, the first part has a median diameter of 150 μm or more and 500 μm or less, the second part has a median diameter of 1 μm or more and 30 μm or less and the ratio W1/W2 of the weight W1 of the first part to the weight W2 of the second pat is 2.0 or more and 6.0 or less.SELECTED DRAWING: None
【課題】ジルコニア－カーボン質耐火材料の耐食性を従来技術に比べて向上させる。【解決手段】ジルコニア原料７０重量％以上９８重量％以下と、カーボン原料２重量％以上３０重量％以下と、を含むジルコニア－カーボン質耐火材料であって、ジルコニア原料は、公称目開き１０６μｍのふるいを通過できない第一部分と、当該ふるいを通過できる第二部分と、を含み、第一部分のメジアン径は、１５０μｍ以上５００μｍ以下であり、第二部分のメジアン径は、１μｍ以上３０μｍ以下であり、第一部分の重量Ｗ１と第二部分の重量Ｗ２との比Ｗ１／Ｗ２は、２．０以上６．０以下である。【選択図】なし
ZIRCONIA-CARBON REFRACTORY MATERIAL, IMMERSION NOZZLE, AND METHOD FOR PRODUCING ZIRCONIA-CARBON REFRACTORY MATERIAL
To improve the corrosion resistance of a zirconia-carbon refractory material compared with a conventional technique.SOLUTION: There is provided a zirconia-carbon refractory material containing 70 mass% or more and 98 mass% or less of a zirconia raw material and 2 mass% or more and 30 mass% or less of a carbon raw material, wherein the zirconia raw material contains a first part which cannot pass through a sieve with a nominal aperture of 106 μm and a second part which can pass through the sieve, the first part has a median diameter of 150 μm or more and 500 μm or less, the second part has a median diameter of 1 μm or more and 30 μm or less and the ratio W1/W2 of the weight W1 of the first part to the weight W2 of the second pat is 2.0 or more and 6.0 or less.SELECTED DRAWING: None
【課題】ジルコニア－カーボン質耐火材料の耐食性を従来技術に比べて向上させる。【解決手段】ジルコニア原料７０重量％以上９８重量％以下と、カーボン原料２重量％以上３０重量％以下と、を含むジルコニア－カーボン質耐火材料であって、ジルコニア原料は、公称目開き１０６μｍのふるいを通過できない第一部分と、当該ふるいを通過できる第二部分と、を含み、第一部分のメジアン径は、１５０μｍ以上５００μｍ以下であり、第二部分のメジアン径は、１μｍ以上３０μｍ以下であり、第一部分の重量Ｗ１と第二部分の重量Ｗ２との比Ｗ１／Ｗ２は、２．０以上６．０以下である。【選択図】なし
ZIRCONIA-CARBON REFRACTORY MATERIAL, IMMERSION NOZZLE, AND METHOD FOR PRODUCING ZIRCONIA-CARBON REFRACTORY MATERIAL
ジルコニア－カーボン質耐火材料、浸漬ノズル、およびジルコニア－カーボン質耐火材料の製造方法
HAYASHI I (author) / FUJITA KEIGO (author) / MATSUNAGA TAKAYUKI (author)
2023-02-09
Patent
Electronic Resource
Japanese
Zirconia refractory material and preparation method thereof
| European Patent Office | 2015