CRACK SUPPRESSED CONSTRUCTION METHOD OF MASS CONCRETE
To provide a construction method that is highly effective in suppressing crack caused by inner and outer temperature difference through hydration reaction of mass concrete.SOLUTION: Phase change material in temperature control mats 20-1, 20-2 changes in phase according to environmental temperature to keep temperature of a surface and a center of mass concrete C or to suppress temperature change thereof. More specifically, when the environmental temperature changes to higher temperature than a fusion point of the phase change material (for example, when the environment changes from nighttime to daytime), temperature increase is suppressed through realizing heat absorption effect by melting the phase change material. In the graph of Fig 3, for example, when the environmental temperature changes and rises as a curve t1, the temperature change of the phase change material becomes a curve t2. This suppresses the change in temperature rise even when a whole or a part of a surface of the mass concrete C rises in temperature through heat of hydration in the mass concrete C. Therefore, suppression of temperature drop of the surface allows generation of acute temperature gradient between the surface and the center part to be suppressed.SELECTED DRAWING: Figure 1
【課題】マスコンクリートの水和反応による内外温度差に起因するひび割れの抑制効果が高い工法を提供する。【解決手段】温度制御マット２０－１，２０－２内の相変化材料が環境温度に応じて相変化することで、マスコンクリートＣの表面及び中心部を保温し、又は温度変化を抑制する。より具体的には、相変化材料の融点よりも高い環境温度へと変化する場合（例えば夜間から日中に移行する場合）、相変化材料が融解することで吸熱効果を発揮して温度上昇を抑制する。例えば図３のグラフにおいて、環境温度の上昇変化が曲線ｔ１のとき、相変化材料の温度変化は曲線ｔ２となる。よって、マスコンクリートＣ内の水和熱によってそのマスコンクリートＣの表面の全部又は一部において温度上昇が生じたとしても、その温度上昇の変化が抑制される。これにより、表面の温度低下が抑制されることにより、表面と中心部間の急激な温度勾配の発生を抑えることができる。【選択図】図１
CRACK SUPPRESSED CONSTRUCTION METHOD OF MASS CONCRETE
To provide a construction method that is highly effective in suppressing crack caused by inner and outer temperature difference through hydration reaction of mass concrete.SOLUTION: Phase change material in temperature control mats 20-1, 20-2 changes in phase according to environmental temperature to keep temperature of a surface and a center of mass concrete C or to suppress temperature change thereof. More specifically, when the environmental temperature changes to higher temperature than a fusion point of the phase change material (for example, when the environment changes from nighttime to daytime), temperature increase is suppressed through realizing heat absorption effect by melting the phase change material. In the graph of Fig 3, for example, when the environmental temperature changes and rises as a curve t1, the temperature change of the phase change material becomes a curve t2. This suppresses the change in temperature rise even when a whole or a part of a surface of the mass concrete C rises in temperature through heat of hydration in the mass concrete C. Therefore, suppression of temperature drop of the surface allows generation of acute temperature gradient between the surface and the center part to be suppressed.SELECTED DRAWING: Figure 1
【課題】マスコンクリートの水和反応による内外温度差に起因するひび割れの抑制効果が高い工法を提供する。【解決手段】温度制御マット２０－１，２０－２内の相変化材料が環境温度に応じて相変化することで、マスコンクリートＣの表面及び中心部を保温し、又は温度変化を抑制する。より具体的には、相変化材料の融点よりも高い環境温度へと変化する場合（例えば夜間から日中に移行する場合）、相変化材料が融解することで吸熱効果を発揮して温度上昇を抑制する。例えば図３のグラフにおいて、環境温度の上昇変化が曲線ｔ１のとき、相変化材料の温度変化は曲線ｔ２となる。よって、マスコンクリートＣ内の水和熱によってそのマスコンクリートＣの表面の全部又は一部において温度上昇が生じたとしても、その温度上昇の変化が抑制される。これにより、表面の温度低下が抑制されることにより、表面と中心部間の急激な温度勾配の発生を抑えることができる。【選択図】図１
CRACK SUPPRESSED CONSTRUCTION METHOD OF MASS CONCRETE
マスコンクリートのひび割れ抑制工法
SAKAI TAKAHIRO (author)
2024-09-09
Patent
Electronic Resource
Japanese
IPC:
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
E04G
SCAFFOLDING
,
Baugerüste
/
C04B
Kalk
,
LIME
Construction method for controlling mass concrete crack formation
| European Patent Office | 2016
Construction method for mass concrete temperature crack control
| European Patent Office | 2020