CEMENT COMPOSITION AND MANUFACTURING METHOD THEREOF
To provide a cement composition which can contribute to a greater reduction of carbon dioxide emissions compared to when using limestone and exhibits reduced yield stress and viscosity, and a manufacturing method thereof.SOLUTION: A cement composition includes light calcium carbonate, Portland cement clinker, and gypsum. The light calcium carbonate has a volume standard cumulative 50% particle size of 10 μm or over and 35 μm or under, 1-μm passage fraction on volume standard of 3.0% or under, and 35-μm residue on volume standard of 5.0% or over and 50.0% or under. When the cement composition is 100 mass%, the content of light calcium carbonate is 1 mass% or over and 20 mass% or under, and the combined total of the content of Portland cement clinker and the content of gypsum is 80 mass% or over and 99 mass% or under.SELECTED DRAWING: Figure 3
【課題】石灰石を使用した場合よりも二酸化炭素の排出量の低減に寄与することが可能であり、且つ降伏応力及び粘性が低減されたセメント組成物、及びその製造方法を提供すること。【解決手段】セメント組成物は、軽質炭酸カルシウムと、ポルトランドセメントクリンカと、石膏と、を含む。軽質炭酸カルシウムは、その体積基準累積５０％粒子径が１０μｍ以上３５μｍ以下であり、１μｍ通過分が体積基準で３．０％以下であり、且つ、３５μｍ残分が体積基準で５．０％以上５０．０％以下である。セメント組成物を１００質量％とした場合、軽質炭酸カルシウムの含有量が１質量％以上２０質量％以下であり、且つ、ポルトランドセメントクリンカの含有量及び石膏の含有量の合計量が８０質量％以上９９質量％以下である。【選択図】図３
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREOF
To provide a cement composition which can contribute to a greater reduction of carbon dioxide emissions compared to when using limestone and exhibits reduced yield stress and viscosity, and a manufacturing method thereof.SOLUTION: A cement composition includes light calcium carbonate, Portland cement clinker, and gypsum. The light calcium carbonate has a volume standard cumulative 50% particle size of 10 μm or over and 35 μm or under, 1-μm passage fraction on volume standard of 3.0% or under, and 35-μm residue on volume standard of 5.0% or over and 50.0% or under. When the cement composition is 100 mass%, the content of light calcium carbonate is 1 mass% or over and 20 mass% or under, and the combined total of the content of Portland cement clinker and the content of gypsum is 80 mass% or over and 99 mass% or under.SELECTED DRAWING: Figure 3
【課題】石灰石を使用した場合よりも二酸化炭素の排出量の低減に寄与することが可能であり、且つ降伏応力及び粘性が低減されたセメント組成物、及びその製造方法を提供すること。【解決手段】セメント組成物は、軽質炭酸カルシウムと、ポルトランドセメントクリンカと、石膏と、を含む。軽質炭酸カルシウムは、その体積基準累積５０％粒子径が１０μｍ以上３５μｍ以下であり、１μｍ通過分が体積基準で３．０％以下であり、且つ、３５μｍ残分が体積基準で５．０％以上５０．０％以下である。セメント組成物を１００質量％とした場合、軽質炭酸カルシウムの含有量が１質量％以上２０質量％以下であり、且つ、ポルトランドセメントクリンカの含有量及び石膏の含有量の合計量が８０質量％以上９９質量％以下である。【選択図】図３
CEMENT COMPOSITION AND MANUFACTURING METHOD THEREOF
セメント組成物及びその製造方法
GOTO TAKU (author) / OSAKI MASAFUMI (author)
2024-10-31
Patent
Electronic Resource
Japanese
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2018
MIXTURE COMPOSITION, CEMENT COMPOSITION, AND MANUFACTURING METHOD THEREOF
| European Patent Office | 2022
MIXED CEMENT COMPOSITION AND MANUFACTURING METHOD THEREOF
| European Patent Office | 2022