REFRACTORY COMPOSITION AND SLIDE GATE PLATE FOR STEEL CASTING BY USING IT
The present invention relates to a refractory composition and to a slide gate plate for steel casting manufactured with the same. A slide gate plate having a refractory material formed by sintering, which contains multiple components, contains a main component forming a base composition, wherein the main component contains 43 wt% or more and 77 wt% or less of electrofused magnesia; 10 wt% or more and 40 wt% or less of CaO stabilized zirconia; and 5 wt% or more and 10 wt% or less of carbon. The slide gate plate having a refractory material is manufactured to obtain a refractory composition with improved corrosion resistance and spalling resistance, thereby increasing resistance to chemically molten iron as for special steel casting like Nb, Mn, and Cr-added high oxygen steel. Therefore, the costs and time for maintenance of refractory material of a slide gate plate. Also, delay of casting work caused by unnecessary repair is controlled to improve productivity.
본 발명은 내화 조성물 및 이로 제작된 강 주조용 슬라이드 게이트 플레이트에 관한 것으로서, 복수의 성분을 포함하고 기본 조성을 이루는 주성분을 포함하고, 주성분은 중량%로, 전융 마그네시아 : 43wt% 이상 내지 77wt% 이하, CaO 안정화 지르코니아 : 10wt% 이상 내지 40wt% 이하, 카본 : 5wt% 이상 내지 10wt% 이하를 포함하여, 소성에 의해 성형되는 내화물을 갖는 강 주조용 슬라이드 게이트 플레이트를 제작함으로써, 내식성 및 내스폴링성이 증가 된 내화 조성물을 획득할 수 있어, Nb, Mn, Cr첨가의 고산소강과 같은 특수강의 주조용으로써 화학적 용선에 대한 저항성을 증가시킬 수 있다. 따라서, 슬라이드 게이트 플레이트 내화물의 유지보수에 따른 비용 및 시간을 절감할 수 있다. 또한, 불필요한 보수에 따른 주조 조업 지연을 억제하여 생산성을 향상시킬 수 있다.
REFRACTORY COMPOSITION AND SLIDE GATE PLATE FOR STEEL CASTING BY USING IT
The present invention relates to a refractory composition and to a slide gate plate for steel casting manufactured with the same. A slide gate plate having a refractory material formed by sintering, which contains multiple components, contains a main component forming a base composition, wherein the main component contains 43 wt% or more and 77 wt% or less of electrofused magnesia; 10 wt% or more and 40 wt% or less of CaO stabilized zirconia; and 5 wt% or more and 10 wt% or less of carbon. The slide gate plate having a refractory material is manufactured to obtain a refractory composition with improved corrosion resistance and spalling resistance, thereby increasing resistance to chemically molten iron as for special steel casting like Nb, Mn, and Cr-added high oxygen steel. Therefore, the costs and time for maintenance of refractory material of a slide gate plate. Also, delay of casting work caused by unnecessary repair is controlled to improve productivity.
본 발명은 내화 조성물 및 이로 제작된 강 주조용 슬라이드 게이트 플레이트에 관한 것으로서, 복수의 성분을 포함하고 기본 조성을 이루는 주성분을 포함하고, 주성분은 중량%로, 전융 마그네시아 : 43wt% 이상 내지 77wt% 이하, CaO 안정화 지르코니아 : 10wt% 이상 내지 40wt% 이하, 카본 : 5wt% 이상 내지 10wt% 이하를 포함하여, 소성에 의해 성형되는 내화물을 갖는 강 주조용 슬라이드 게이트 플레이트를 제작함으로써, 내식성 및 내스폴링성이 증가 된 내화 조성물을 획득할 수 있어, Nb, Mn, Cr첨가의 고산소강과 같은 특수강의 주조용으로써 화학적 용선에 대한 저항성을 증가시킬 수 있다. 따라서, 슬라이드 게이트 플레이트 내화물의 유지보수에 따른 비용 및 시간을 절감할 수 있다. 또한, 불필요한 보수에 따른 주조 조업 지연을 억제하여 생산성을 향상시킬 수 있다.
REFRACTORY COMPOSITION AND SLIDE GATE PLATE FOR STEEL CASTING BY USING IT
내화 조성물 및 이로 제작된 강 주조용 슬라이드 게이트 플레이트
JEONG DOO HOA (author)
2015-06-30
Patent
Electronic Resource
Korean
REFRACTORY COMPOSITION AND SLIDE GATE PLATE FOR STEEL CASTING BY USING IT
| European Patent Office | 2015
Refractory composition and slide gate plate for steel casting by using it
European Patent Office | 2015
| European Patent Office | 2020