MANUFACTURING METHODE OF LIQUID SELF WATERPROOFING ADMIXTURE, COMPOSITION AND METHODE OF CONSTRUCTION USING THE SAME
The method for manufacturing a liquefied self waterproofing admixture comprises: a first step of mixing 100 parts by weight of water, 15-20 parts by weight of stearic acid amide, 15-20 parts by weight of oleic acid, 40-50 parts by weight of sulfonated naphthalene formaldehyde condensate, 1-2 parts by weight of sodium naphthionate, 5-10 parts by weight of ammonia aqueous solution and 0.5-1 parts by weight of surfactant, and stirring the mixture at temperature of 80-90°C for 15 minutes to manufacture a water repellent mixed solution; a second step of mixing 100 parts by weight of water (dispersion medium), 2-3 parts by weight of silica fume, 20-30 parts by weight of active silica, 3-5 parts by weight of diatomite and 10-15 parts by weight of water soluble latex, and stirring the mixture at temperature of 70-90°C for 15 minutes to manufacture an inorganic particle filled dispersion solution; a third step of mixing the water repellent mixed solution with the inorganic particle filled dispersion solution at the weight ratio of 1:0.5-1:0.8 and stirring the mixture at temperature of 70-80°C for 10 minutes to manufacture a self waterproofing base solution; a fourth step of mixing 1-2 parts by weight of sodium lauryl sulfate and 1-2 parts by weight of sodium benzoate with respect to 100 parts by weight of the self waterproofing base solution and stirring the mixture at 70-80°C for 10 minutes to manufacture a self waterproofing solution; and a fifth step of mixing 0.5-1 parts by weight of hydro gel particles with the 100 parts by weight of the self waterproofing solution and stirring the mixture at room temperature for 10 minutes while applying ultrasonic waves to the mixture.
본 발명의 액상 구체방수제의 제조방법은 물 100중량부, 스테아린산 아마이드 15 내지 20중량부, 올래인산 15 내지 20중량부, 술포네이티드 나프탈렌 포름알데하이드 축합물 40 내지 50중량부, 나프티온산 나트륨 1 내지 2중량부, 암모니아 수용액 5 내지 10중량부 및 계면활성제 0.5 내지 1중량부를 혼합하고, 80 내지 90℃의 온도에서 15분간 교반하여 발수성부여 혼합용액을 제조하는 제1단계와, 물 100중량부(분산매), 실리카 퓸 2 내지 3중량부, 활성실리카 20 내지 30중량부, 규조토 3 내지 5중량부 및 수용성 라텍스 10 내지 15중량부를 혼합하고, 70 내지 90℃의 온도에서 15분간 교반하여 무기입자충전 분산용액을 제조하는 제2단계와, 상기 발수성부여 혼합용액과 무기입자충전 분산용액을 1:0.5 내지 1:0.8의 중량비로 혼합하고, 70 내지 80℃의 온도에서 10분간 교반하여 구체방수 기초용액을 제조하는 제3단계와, 상기 구체방수 기초용액 100중량부에 나트륨 라우릴 황산염 1 내지 2중량부, 소듐 벤조에이트 1 내지 2중량부를 혼합하고, 70 내지 80℃의 온도에서 10분간 교반하여 구체방수액을 제조하는 제4단계와, 상기 구체방수액 100중량부에 하이드로 겔 입자 0.5 내지 1중량부를 혼합하고, 초음파를 가하면서 상온에서 10분간 교반하는 제5단계를 포함한다.
MANUFACTURING METHODE OF LIQUID SELF WATERPROOFING ADMIXTURE, COMPOSITION AND METHODE OF CONSTRUCTION USING THE SAME
The method for manufacturing a liquefied self waterproofing admixture comprises: a first step of mixing 100 parts by weight of water, 15-20 parts by weight of stearic acid amide, 15-20 parts by weight of oleic acid, 40-50 parts by weight of sulfonated naphthalene formaldehyde condensate, 1-2 parts by weight of sodium naphthionate, 5-10 parts by weight of ammonia aqueous solution and 0.5-1 parts by weight of surfactant, and stirring the mixture at temperature of 80-90°C for 15 minutes to manufacture a water repellent mixed solution; a second step of mixing 100 parts by weight of water (dispersion medium), 2-3 parts by weight of silica fume, 20-30 parts by weight of active silica, 3-5 parts by weight of diatomite and 10-15 parts by weight of water soluble latex, and stirring the mixture at temperature of 70-90°C for 15 minutes to manufacture an inorganic particle filled dispersion solution; a third step of mixing the water repellent mixed solution with the inorganic particle filled dispersion solution at the weight ratio of 1:0.5-1:0.8 and stirring the mixture at temperature of 70-80°C for 10 minutes to manufacture a self waterproofing base solution; a fourth step of mixing 1-2 parts by weight of sodium lauryl sulfate and 1-2 parts by weight of sodium benzoate with respect to 100 parts by weight of the self waterproofing base solution and stirring the mixture at 70-80°C for 10 minutes to manufacture a self waterproofing solution; and a fifth step of mixing 0.5-1 parts by weight of hydro gel particles with the 100 parts by weight of the self waterproofing solution and stirring the mixture at room temperature for 10 minutes while applying ultrasonic waves to the mixture.
본 발명의 액상 구체방수제의 제조방법은 물 100중량부, 스테아린산 아마이드 15 내지 20중량부, 올래인산 15 내지 20중량부, 술포네이티드 나프탈렌 포름알데하이드 축합물 40 내지 50중량부, 나프티온산 나트륨 1 내지 2중량부, 암모니아 수용액 5 내지 10중량부 및 계면활성제 0.5 내지 1중량부를 혼합하고, 80 내지 90℃의 온도에서 15분간 교반하여 발수성부여 혼합용액을 제조하는 제1단계와, 물 100중량부(분산매), 실리카 퓸 2 내지 3중량부, 활성실리카 20 내지 30중량부, 규조토 3 내지 5중량부 및 수용성 라텍스 10 내지 15중량부를 혼합하고, 70 내지 90℃의 온도에서 15분간 교반하여 무기입자충전 분산용액을 제조하는 제2단계와, 상기 발수성부여 혼합용액과 무기입자충전 분산용액을 1:0.5 내지 1:0.8의 중량비로 혼합하고, 70 내지 80℃의 온도에서 10분간 교반하여 구체방수 기초용액을 제조하는 제3단계와, 상기 구체방수 기초용액 100중량부에 나트륨 라우릴 황산염 1 내지 2중량부, 소듐 벤조에이트 1 내지 2중량부를 혼합하고, 70 내지 80℃의 온도에서 10분간 교반하여 구체방수액을 제조하는 제4단계와, 상기 구체방수액 100중량부에 하이드로 겔 입자 0.5 내지 1중량부를 혼합하고, 초음파를 가하면서 상온에서 10분간 교반하는 제5단계를 포함한다.
MANUFACTURING METHODE OF LIQUID SELF WATERPROOFING ADMIXTURE, COMPOSITION AND METHODE OF CONSTRUCTION USING THE SAME
액상 구체방수제의 제조방법, 이에 의하여 제조된 구체방수제 조성물 및 이를 이용한 시공방법
IM MYUNG SOO (author) / KIM MEONG JI (author)
2015-12-24
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
| European Patent Office | 2015
| European Patent Office | 2016
| European Patent Office | 2020
| European Patent Office | 2015