STONE MASTIC ASPHALT MIXTURE
The present invention relates to a stone mastic asphalt (SMA) modified binder composition with improved an anti-freezing function and durability, comprising: 10 to 90 wt% of calcium chloride or sodium chloride; 2 to 25 wt% of sodium sulfate; 2 to 25 wt% of calcium oxide; 2 to 25 wt% of a vitrified; 2 to 25 wt% of ethylene propylene rubber; 0.01 to 10 wt% of a fiber reinforcing agent; 0.01 to 10 wt% of furfuryl alcohol; and 0.01 to 10 wt% of bismaleimide, and to a method for preparing an SMA mixture using the same. According to the present invention, an anti-freezing agent added during the manufacturing of asphalt concrete can maintain a high ice-making function, thereby preventing accidents in slippery snow-covered road and deterioration of a road facility. In addition, since the ratio and physical conditions of initial components are changed, it is possible to prepare a composition which has a long-term freeze-suppression effect, prevents repeated icing when a surrounding temperature is decreased, is not harmful to an environment, and is not corrosive to metal. By improving strength and adhesion, plastic deformation resistance and low temperature fatigue cracking are remarkably improved and removed, and accordingly, it is possible to prepare the SMA mixture capable of preventing damage to a pavement surface due to plastic deformation and low temperature cracking, which general asphalt pavement has, and securing slip resistance, thereby improving durability of pavement even in terms of economy. Therefore, the present invention has direct and indirect economic effects such as reduction of maintenance costs, reduction of human and physical loss due to congestion and waiting generated during maintenance of road, and the like.
본 발명의 쇄석 매스틱 아스팔트(SMA, STONE MASTIC ASPHALT) 개질 결합재 조성물은 염화칼슘 또는 염화나트륨 10~90중량%, 황산나트륨 2~25중량%, 산화칼슘 2~25중량%, 비트리파이드 2~25중량%, 에틸렌프로필렌고무 2~25중량%, 섬유보강재 0.01∼10중량%, 푸르푸릴알코올 0.01~10중량% 및 비스말레이미드 0.01~10중량%를 포함하는 것을 특징으로 하는 결빙 방지 기능 및 내구성이 개선된 SMA 개질 결합재 조성물 및 이를 이용한 SMA 혼합물 제조방법에 관한 것이다. 본 발명에 의하면, 아스팔트 콘크리트 제조 시 첨가되는 결빙 방지제가 높은 제빙 기능을 유지할 수 있어 눈길 미끄럼 사고 및 도로시설물의 열화를 방지할 수 있다. 또한, 초기 성분의 비율 및 물리적 조건을 변화시키기 때문에, 장기간의 동결억제 효과를 가지며, 주변 온도가 떨어지면 반복적인 착빙을 막으며, 환경에 유해하지 않고, 금속에 대한 부식성이 없는 조성물을 만드는 것이 가능하다. 강도 및 접착력 개선을 통하여 소성변형 저항성 및 저온 피로 균열성이 현저히 개선되었으며, 따라서 일반 아스팔트 포장이 가지는 소성변형, 저온균열성에 의한 포장면의 파손을 방지하고, 미끄럼 저항성을 확보할 수 있는 SMA 혼합물을 제조할 수 있어 경제적인 면에서도 포장의 내구성이 향상되어 유지보수 비용의 절감 및 도로유지 보수 시 발생하는 정체, 대기로 인한 인적 물적 손실 감소 등 직간접적인 경제적 효과가 있다.
STONE MASTIC ASPHALT MIXTURE
The present invention relates to a stone mastic asphalt (SMA) modified binder composition with improved an anti-freezing function and durability, comprising: 10 to 90 wt% of calcium chloride or sodium chloride; 2 to 25 wt% of sodium sulfate; 2 to 25 wt% of calcium oxide; 2 to 25 wt% of a vitrified; 2 to 25 wt% of ethylene propylene rubber; 0.01 to 10 wt% of a fiber reinforcing agent; 0.01 to 10 wt% of furfuryl alcohol; and 0.01 to 10 wt% of bismaleimide, and to a method for preparing an SMA mixture using the same. According to the present invention, an anti-freezing agent added during the manufacturing of asphalt concrete can maintain a high ice-making function, thereby preventing accidents in slippery snow-covered road and deterioration of a road facility. In addition, since the ratio and physical conditions of initial components are changed, it is possible to prepare a composition which has a long-term freeze-suppression effect, prevents repeated icing when a surrounding temperature is decreased, is not harmful to an environment, and is not corrosive to metal. By improving strength and adhesion, plastic deformation resistance and low temperature fatigue cracking are remarkably improved and removed, and accordingly, it is possible to prepare the SMA mixture capable of preventing damage to a pavement surface due to plastic deformation and low temperature cracking, which general asphalt pavement has, and securing slip resistance, thereby improving durability of pavement even in terms of economy. Therefore, the present invention has direct and indirect economic effects such as reduction of maintenance costs, reduction of human and physical loss due to congestion and waiting generated during maintenance of road, and the like.
본 발명의 쇄석 매스틱 아스팔트(SMA, STONE MASTIC ASPHALT) 개질 결합재 조성물은 염화칼슘 또는 염화나트륨 10~90중량%, 황산나트륨 2~25중량%, 산화칼슘 2~25중량%, 비트리파이드 2~25중량%, 에틸렌프로필렌고무 2~25중량%, 섬유보강재 0.01∼10중량%, 푸르푸릴알코올 0.01~10중량% 및 비스말레이미드 0.01~10중량%를 포함하는 것을 특징으로 하는 결빙 방지 기능 및 내구성이 개선된 SMA 개질 결합재 조성물 및 이를 이용한 SMA 혼합물 제조방법에 관한 것이다. 본 발명에 의하면, 아스팔트 콘크리트 제조 시 첨가되는 결빙 방지제가 높은 제빙 기능을 유지할 수 있어 눈길 미끄럼 사고 및 도로시설물의 열화를 방지할 수 있다. 또한, 초기 성분의 비율 및 물리적 조건을 변화시키기 때문에, 장기간의 동결억제 효과를 가지며, 주변 온도가 떨어지면 반복적인 착빙을 막으며, 환경에 유해하지 않고, 금속에 대한 부식성이 없는 조성물을 만드는 것이 가능하다. 강도 및 접착력 개선을 통하여 소성변형 저항성 및 저온 피로 균열성이 현저히 개선되었으며, 따라서 일반 아스팔트 포장이 가지는 소성변형, 저온균열성에 의한 포장면의 파손을 방지하고, 미끄럼 저항성을 확보할 수 있는 SMA 혼합물을 제조할 수 있어 경제적인 면에서도 포장의 내구성이 향상되어 유지보수 비용의 절감 및 도로유지 보수 시 발생하는 정체, 대기로 인한 인적 물적 손실 감소 등 직간접적인 경제적 효과가 있다.
STONE MASTIC ASPHALT MIXTURE
쇄석 매스틱 아스팔트 혼합물
SHIN HYEON KUK (author) / CHOI JONG YUN (author)
2019-03-06
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Heavy duty stone mastic asphalt
| British Library Conference Proceedings | 1996
Stone Mastic Asphalt In Colorado
| NTIS | 2001
Free mix type modified asphalt composition for warm stone mastic asphalt mixture
| European Patent Office | 2021
Evaluation of Stone Mastic Asphalt Performance
| British Library Conference Proceedings | 1997