The present invention relates to a warm stone mastic asphalt mixture comprising: with respect to 100 parts by weight of the mixed aggregate, 60 to 80 wt% of coarse aggregate having a maximum diameter of 5 mm or more, 15 to 30 wt% of fine aggregate having a maximum diameter of less than 5 mm, and 5 to 10 wt% of mastic; with respect to 100 parts by weight of asphalt, 5-10 parts by weight of the porous nylon hollow fiber (10) which has a diameter of 50 to 500㎛ and a hollow part (12) in a longitudinal direction in a center of a main body (11), and in which micropores (13) allowing an outer surface of the main body (11) to communicate with the hollow part (12) are irregularly formed; with respect to 100 parts by weight of a polyamide-based polymer compound, 5 to 10 parts by weight of a modifier in which 10 to 30 parts by weight of a low-density polyethylene resin, 35 to 150 parts by weight of process oil, 10 to 15 parts by weight of organic polymer compatibilizer, and 10 to 20 parts by weight of a corrosion inhibitor are mixed; and 0.5 to 3 parts by weight of cellulose fiber. As the warm stone mastic asphalt (SMA) mixture of the present invention has high consistency and high bonding strength, the pre-mix type modified asphalt composition minimizes the plastic deformation (wheel dent) of the warm stone mastic asphalt (SMA) mixture (ascon) manufactured using the same, lowers the construction temperature of the asphalt pavement to reduce energy consumption during asphalt pavement construction, reduces CO_2 generation, and improves workability and compaction. Because the pre-mix type modified asphalt composition has low dynamic viscosity, excellent workability and compaction properties can be provided.
본 발명은 [A] 최대직경이 5㎜ 이상인 굵은골재 60~80중량%와 최대직경이 5㎜ 미만인 잔골재 15~30중량%와 채움재(Mastic) 5~10중량부로 이루어진 혼합골재 100중량부에 대하여, [B] (ⅰ) 아스팔트 100 중량부에 대하여 (ⅱ) 직경이 50~500㎛이고, 본체(11)의 중앙 내부에 길이방향을 따라 중공부(12)가 형성되어 있고, 본체(11)의 외표면과 상기 중공부(12)를 연통시켜주는 미세공(13)들이 불규칙으로 형성되어 있는 다공성 나일론 중공섬유(10) 5~10중량부 및 (ⅲ) 폴리아미드계 고분자 화합물 100중량부 대비 저밀도 폴리에틸렌 수지 10~30중량부, 프로세스 오일 35~150중량부, 유기 고분자 상용화제 10~15중량% 및 부식 방지제 10~20중량부가 혼합된 조성을 갖는 개질제 5~10중량부와 [C] 셀룰로오스 섬유 0.5~3중량부가 혼합되어 있는 것을 특징으로 한다. 본 발명의 중온 쇄석 마스틱 아스팔트(SMA) 혼합물은 고응집력(High consistency)과 고결합성(High Bonding Strength)을 구비하기 때문에 소성 변형(차바퀴 패임) 현상을 최소화시켜 주고, 아스팔트 포장체의 시공온도를 낮추어 아스팔트 포장체 시공시 에너지 사용량을 절감하고 CO2 발생을 감소시키고 시공성과 다짐성을 개선시켜 준다. 낮은 동점도(Dynamic Viscosity)를 갖기 때문에 시공성과 다짐성이 뛰어나다.
The present invention relates to a warm stone mastic asphalt mixture comprising: with respect to 100 parts by weight of the mixed aggregate, 60 to 80 wt% of coarse aggregate having a maximum diameter of 5 mm or more, 15 to 30 wt% of fine aggregate having a maximum diameter of less than 5 mm, and 5 to 10 wt% of mastic; with respect to 100 parts by weight of asphalt, 5-10 parts by weight of the porous nylon hollow fiber (10) which has a diameter of 50 to 500㎛ and a hollow part (12) in a longitudinal direction in a center of a main body (11), and in which micropores (13) allowing an outer surface of the main body (11) to communicate with the hollow part (12) are irregularly formed; with respect to 100 parts by weight of a polyamide-based polymer compound, 5 to 10 parts by weight of a modifier in which 10 to 30 parts by weight of a low-density polyethylene resin, 35 to 150 parts by weight of process oil, 10 to 15 parts by weight of organic polymer compatibilizer, and 10 to 20 parts by weight of a corrosion inhibitor are mixed; and 0.5 to 3 parts by weight of cellulose fiber. As the warm stone mastic asphalt (SMA) mixture of the present invention has high consistency and high bonding strength, the pre-mix type modified asphalt composition minimizes the plastic deformation (wheel dent) of the warm stone mastic asphalt (SMA) mixture (ascon) manufactured using the same, lowers the construction temperature of the asphalt pavement to reduce energy consumption during asphalt pavement construction, reduces CO_2 generation, and improves workability and compaction. Because the pre-mix type modified asphalt composition has low dynamic viscosity, excellent workability and compaction properties can be provided.
본 발명은 [A] 최대직경이 5㎜ 이상인 굵은골재 60~80중량%와 최대직경이 5㎜ 미만인 잔골재 15~30중량%와 채움재(Mastic) 5~10중량부로 이루어진 혼합골재 100중량부에 대하여, [B] (ⅰ) 아스팔트 100 중량부에 대하여 (ⅱ) 직경이 50~500㎛이고, 본체(11)의 중앙 내부에 길이방향을 따라 중공부(12)가 형성되어 있고, 본체(11)의 외표면과 상기 중공부(12)를 연통시켜주는 미세공(13)들이 불규칙으로 형성되어 있는 다공성 나일론 중공섬유(10) 5~10중량부 및 (ⅲ) 폴리아미드계 고분자 화합물 100중량부 대비 저밀도 폴리에틸렌 수지 10~30중량부, 프로세스 오일 35~150중량부, 유기 고분자 상용화제 10~15중량% 및 부식 방지제 10~20중량부가 혼합된 조성을 갖는 개질제 5~10중량부와 [C] 셀룰로오스 섬유 0.5~3중량부가 혼합되어 있는 것을 특징으로 한다. 본 발명의 중온 쇄석 마스틱 아스팔트(SMA) 혼합물은 고응집력(High consistency)과 고결합성(High Bonding Strength)을 구비하기 때문에 소성 변형(차바퀴 패임) 현상을 최소화시켜 주고, 아스팔트 포장체의 시공온도를 낮추어 아스팔트 포장체 시공시 에너지 사용량을 절감하고 CO2 발생을 감소시키고 시공성과 다짐성을 개선시켜 준다. 낮은 동점도(Dynamic Viscosity)를 갖기 때문에 시공성과 다짐성이 뛰어나다.
Warm stone mastic asphalt mixture
중온 쇄석 마스틱 아스팔트（ＳＭＡ）혼합물
KIM DONG YEON (author)
2021-08-20
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Free mix type modified asphalt composition for warm stone mastic asphalt mixture
| European Patent Office | 2021
Characterization of Shredded Waste Plastic on Warm Stone Mastic Asphalt
| Springer Verlag | 2021
Heavy duty stone mastic asphalt
| British Library Conference Proceedings | 1996
Stone Mastic Asphalt In Colorado
| NTIS | 2001