Modifier for warm asphalt mixture and mehtod of manufacturing warn asphalt mixture thereby
According to the present invention, a modifier for a middle temperature asphalt mixture is mixed to have particles of SiO_2, Al_2_O_3, CaO, MgO, Na_2O_3, K_2O and Fe_2O_3, which have 100-200 μm of an average particle diameter and 0.3-0.5 μm of pores to have 24-32% of porosity, and contain silicon (Si) 4.8 to 5.4 times more than aluminum (Al). The modifier has 0.7-2.0 mol/kg of an ion exchange capacity and comprises aluminum-silicate hydrates of alkaline metals and alkaline earth metals, having 0.1-6% of water content at 105°C. When an asphalt mixture is manufactured by mixing aggregates and asphalt, the present invention adds and mixes, with respect to 100 parts by weight of the asphalt, the modifier for a middle temperature asphalt mixture, the aluminum-silicate hydrate of alkaline metals and alkaline earth metals, to manufacture a middle temperature asphalt mixture. The present invention greatly lowers a mixing temperature of aggregates and asphalt when manufacturing a middle temperature asphalt mixture and a compacting temperature when constructing a middle temperature asphalt packaging body to reduce a construction period, and cuts energy consumptions while minimizing carbon dioxide emissions occurring the environmental pollution.
본 발명에 따른 중온 아스팔트 혼합물용 개질제는 평군입자 직경이 100~200㎛이며, 0.3~0.5㎛의 기공들이 형성되어 기공도가 24~32%인 SiO입자, AlO입자, CaO 입자, MgO 입자, NaO입자, KO 입자 및 FeO입자 들이 알루미늄(Al) 성분보다 규소(Si) 성분이 4.8~5.4배 더 많이 함유되도록 혼합되어 있고, 이온교환능(Ion exchange capacity)이 0.7~2.0 mol/kg이고, 105℃에서 수분 함유량이 0.1~6%인 알칼리금속 및 알칼리토금속의 알루미늄-실리케이트 수화물로 구성된다. 본 발명에서는 골재와 아스팔트를 배합하여 아스팔트 혼합물을 제조할 때 상기 아스팔트 100중량부에 대하여 상기의 알칼리금속 및 알칼리토금속의 알루미늄-실리케이트 수화물인 중온 아스팔트 혼합물용 개질제를 첨가, 혼합하여 중온 아스팔트 혼합물을 제조한다. 본 발명은 중온 아스팔트 혼합물 제조시 골재와 아스팔트의 혼합온도와 중온 아스팔트 포장체를 시공시 다짐 온도를 크게 낮출수 있어서 공사기간을 단축하고, 에너지 소모량을 절감함과 동시에 환경 오염을 일으키는 이산화탄소 발생을 최소화 시켜준다.
Modifier for warm asphalt mixture and mehtod of manufacturing warn asphalt mixture thereby
According to the present invention, a modifier for a middle temperature asphalt mixture is mixed to have particles of SiO_2, Al_2_O_3, CaO, MgO, Na_2O_3, K_2O and Fe_2O_3, which have 100-200 μm of an average particle diameter and 0.3-0.5 μm of pores to have 24-32% of porosity, and contain silicon (Si) 4.8 to 5.4 times more than aluminum (Al). The modifier has 0.7-2.0 mol/kg of an ion exchange capacity and comprises aluminum-silicate hydrates of alkaline metals and alkaline earth metals, having 0.1-6% of water content at 105°C. When an asphalt mixture is manufactured by mixing aggregates and asphalt, the present invention adds and mixes, with respect to 100 parts by weight of the asphalt, the modifier for a middle temperature asphalt mixture, the aluminum-silicate hydrate of alkaline metals and alkaline earth metals, to manufacture a middle temperature asphalt mixture. The present invention greatly lowers a mixing temperature of aggregates and asphalt when manufacturing a middle temperature asphalt mixture and a compacting temperature when constructing a middle temperature asphalt packaging body to reduce a construction period, and cuts energy consumptions while minimizing carbon dioxide emissions occurring the environmental pollution.
본 발명에 따른 중온 아스팔트 혼합물용 개질제는 평군입자 직경이 100~200㎛이며, 0.3~0.5㎛의 기공들이 형성되어 기공도가 24~32%인 SiO입자, AlO입자, CaO 입자, MgO 입자, NaO입자, KO 입자 및 FeO입자 들이 알루미늄(Al) 성분보다 규소(Si) 성분이 4.8~5.4배 더 많이 함유되도록 혼합되어 있고, 이온교환능(Ion exchange capacity)이 0.7~2.0 mol/kg이고, 105℃에서 수분 함유량이 0.1~6%인 알칼리금속 및 알칼리토금속의 알루미늄-실리케이트 수화물로 구성된다. 본 발명에서는 골재와 아스팔트를 배합하여 아스팔트 혼합물을 제조할 때 상기 아스팔트 100중량부에 대하여 상기의 알칼리금속 및 알칼리토금속의 알루미늄-실리케이트 수화물인 중온 아스팔트 혼합물용 개질제를 첨가, 혼합하여 중온 아스팔트 혼합물을 제조한다. 본 발명은 중온 아스팔트 혼합물 제조시 골재와 아스팔트의 혼합온도와 중온 아스팔트 포장체를 시공시 다짐 온도를 크게 낮출수 있어서 공사기간을 단축하고, 에너지 소모량을 절감함과 동시에 환경 오염을 일으키는 이산화탄소 발생을 최소화 시켜준다.
Modifier for warm asphalt mixture and mehtod of manufacturing warn asphalt mixture thereby
중온 아스팔트 혼합물용 개질제 및 이를 이용한 중온 아스팔트 혼합물의 제조방법
KIM DONG YEON (author)
2020-02-18
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
/
C08K
Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe
,
USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
/
C08L
COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
,
Massen auf Basis makromolekularer Verbindungen
Asphalt modifier, asphalt mixture and preparing methods of asphalt modifier and asphalt mixture
| European Patent Office | 2015
Warm temperature asphalt modifier and asphalt mixture using the same
| European Patent Office | 2017
| European Patent Office | 2016
ASPHALT MODIFIER FOR ASPHALT MIXTURE AND ASPHALT MIXTURE COMPRISING SAME
| European Patent Office | 2022