Mortar composition for repair and reinforcement of concrete structure and repair and reinforcement method of concrete structure using same
The present invention relates to a mortar composition for repairing and reinforcing a concrete structure to facilitate construction and a concrete structure repair and reinforcement method using the same. According to the present invention, the mortar composition comprises: 8-30 wt% of cement; 40-83 wt% of fine aggregate; 2-20 wt% of fine blast furnace slag powder; 1.5-15 wt% of amorphous calcium aluminate; 0.5-10 wt% of titanium oxide; 0.5-15 wt% of gypsum; 0.1-5 wt% of copper oxide; 0.1-5 wt% of sepiolite; 0.1-5 wt% of beryllium oxide; 1-5 wt% of an acryl-modified powder resin; 0.1-5 wt% of polyvinyl acetate; 0.1-5 wt% of polyethylene glycol; 0.1-5 wt% of polyvinyl fluoride; 0.1-5 wt% of polydopamine; 0.1-5 wt% of silica fume; 0.1-5 wt% of a polycarboxylic acid-base fluidizer; 0.1-5.0 wt% of reinforcement fiber; and 0.1-5 wt% of a fluorine-based grade IV alkyl ammonium salt.
본 발명은 시멘트 8 내지 30 중량%; 잔골재 40 내지 83 중량%; 고로슬래그 미분말 2 내지 20 중량%; 비정질 칼슘알루미네이트 1.5 내지 15 중량%; 산화타이타늄 0.5 내지 10 중량%; 석고 0.5 내지 15 중량%; 산화구리 0.1 내지 5 중량%; 세피올라이트 0.1 내지 5 중량%; 산화베릴륨 0.1 내지 5 중량%; 아크릴 개질 분말수지 1 내지 5 중량%; 폴리비닐아세테이트 0.1 내지 5 중량%; 폴리에틸렌 글리콜 0.1 내지 5 중량%; 폴리비닐플루오라이드 0.1 내지 5 중량%; 폴리도파민 0.1 내지 5 중량%; 실리카 흄 0.1 내지 5 중량%; 폴리카르복실산계 유동화제 0.1 내지 5 중량%; 섬유보강재 0.1 내지 5.0 중량%; 및 불소계 4급 알킬암모늄염 0.1 내지 5 중량%를 포함하는 콘크리트 구조물의 보수 및 보강용 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수 및 보강공법에 관한 것이다.
Mortar composition for repair and reinforcement of concrete structure and repair and reinforcement method of concrete structure using same
The present invention relates to a mortar composition for repairing and reinforcing a concrete structure to facilitate construction and a concrete structure repair and reinforcement method using the same. According to the present invention, the mortar composition comprises: 8-30 wt% of cement; 40-83 wt% of fine aggregate; 2-20 wt% of fine blast furnace slag powder; 1.5-15 wt% of amorphous calcium aluminate; 0.5-10 wt% of titanium oxide; 0.5-15 wt% of gypsum; 0.1-5 wt% of copper oxide; 0.1-5 wt% of sepiolite; 0.1-5 wt% of beryllium oxide; 1-5 wt% of an acryl-modified powder resin; 0.1-5 wt% of polyvinyl acetate; 0.1-5 wt% of polyethylene glycol; 0.1-5 wt% of polyvinyl fluoride; 0.1-5 wt% of polydopamine; 0.1-5 wt% of silica fume; 0.1-5 wt% of a polycarboxylic acid-base fluidizer; 0.1-5.0 wt% of reinforcement fiber; and 0.1-5 wt% of a fluorine-based grade IV alkyl ammonium salt.
본 발명은 시멘트 8 내지 30 중량%; 잔골재 40 내지 83 중량%; 고로슬래그 미분말 2 내지 20 중량%; 비정질 칼슘알루미네이트 1.5 내지 15 중량%; 산화타이타늄 0.5 내지 10 중량%; 석고 0.5 내지 15 중량%; 산화구리 0.1 내지 5 중량%; 세피올라이트 0.1 내지 5 중량%; 산화베릴륨 0.1 내지 5 중량%; 아크릴 개질 분말수지 1 내지 5 중량%; 폴리비닐아세테이트 0.1 내지 5 중량%; 폴리에틸렌 글리콜 0.1 내지 5 중량%; 폴리비닐플루오라이드 0.1 내지 5 중량%; 폴리도파민 0.1 내지 5 중량%; 실리카 흄 0.1 내지 5 중량%; 폴리카르복실산계 유동화제 0.1 내지 5 중량%; 섬유보강재 0.1 내지 5.0 중량%; 및 불소계 4급 알킬암모늄염 0.1 내지 5 중량%를 포함하는 콘크리트 구조물의 보수 및 보강용 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수 및 보강공법에 관한 것이다.
Mortar composition for repair and reinforcement of concrete structure and repair and reinforcement method of concrete structure using same
콘크리트 구조물의 보수 및 보강용 모르타르 조성물 및 이를 이용한 콘크리트 구조물의 보수 및 보강 공법
KIM JONG CHEUL (author)
2020-09-23
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
Repair-reinforcement mortar of concrete structure and repair-reinforcement method using thereof
| European Patent Office | 2020
| European Patent Office | 2023
| European Patent Office | 2020
| European Patent Office | 2020
| European Patent Office | 2019