The present invention relates to a crack repair method of a concrete structure using dedicated equipment for injecting crack repair materials, which comprises: a structure crack part examination and background treatment step to measure the crack part of the aged concrete structure by using a crack measuring gauge, and if the crack part is measured to be 0.3 mm or greater, to remove deteriorated surfaces and foreign substances by using a power tool; a surface drying and heating step to use an indirect or direct heater, which generates a temperature of 60℃ or higher, to dry the surface of the crack part of the structure, and let a sealing material and the injected crack repair materials be adsorbed in and attached to the surface; a sealing treatment and dedicated sealing equipment installation step to install the sealing material and the dedicated equipment for injecting crack repair materials on the surface of the crack part, to harden the sealing material, and prevent the crack repair materials from being discharged to the outside in order to prevent the crack repair materials injected into the crack part of the structure from being exposed to the outside; a crack repair materials mixing step to transfer and mix a main agent stored in a storage container a of the dedicated equipment for injecting the crack repair materials and a hardening agent stored in a storage container b by using the mixing apparatus; a crack repair materials injection step to transfer the crack repair materials transferred and mixed by the mixing apparatus through an air compressor and to inject the crack repair materials into the crack part of the structure; an injection status checking and hardening step to check the hardened status of the crack repair materials in 12 to 24 hours; and a crack repair completion step. As such, the present invention is able to store and minimize the loss of crack repair materials by using the dedicated equipment for injecting the crack repair materials, leave no residue after use, prevent environmental pollution, completely fill even a rear surface of the structure with the crack repair materials, and simply clean the dedicated equipment for injecting the crack repair materials even after the crack part of the structure is repaired.

본 발명은 노후화된 콘크리트 구조물의 균열부를 균열측정게이지를 이용하여 0.3㎜ 이상시 동력공구를 이용하여 열화된 표면 및 이물질을 제거하는 구조물의 균열부 조사 및 바탕처리 단계; 60℃의 이상의 온도를 생성하는 간접가열 또는 직접가열기를 이용하여 구조물 균열부의 표면을 건조시켜 씰링재 및 주입되는 균열 보수재가 표면에 흡착 및 부착되도록 하는 표면건조 가열단계; 구조물의 균열부에 주입되는 균열 보수재가 외부로 노출되는 것을 방지하기 위하여 균열부 표면에 씰링재와 균열 보수재 주입전용장비를 설치하고 씰링재를 경화시켜 균열 보수재가 외부로 토출되는 것을 방지하는 씰링처리 및 주입전용장비 설치단계; 상기 균열 보수재 주입전용장비의 저장용기a에 보관된 주제와 저장용기b에 보관된 경화제를 혼합장치로 이송하여 혼합하는 균열 보수재혼합단계; 혼합장치로 이송되어 혼합된 균열 보수재를 공기압축기를 통하여 구조물의 균열부로 이송시켜 주입시키는 균열 보수재 주입단계; 12~24시간 이후 균열 보수재의 경화상태를 확인하는 주입상태 확인 및 경화단계; 및 균열보수 완료단계로 이루어지는 균열 보수재 주입 전용 장비를 이용한 콘크리트 구조물의 균열 보수 공법에 관한 것이다. 이러한 본 발명은 균열 보수재 주입전용장비를 이용하여 균열 보수재의 저장 및 손실을 최소화할 수 있고, 사용후 잔여물이 존재하지 않아 환경오염을 방지할 수 있으며, 구조물 배면까지 균열 보수재의 완벽한 충진이 가능하고, 구조물의 균열부 보수 후에도 균열 보수재 주입전용장비의 청소가 간단하게 이루어지는 효과가 있다.