The present invention relates to a high-functionality quick-hardening cement concrete composition for road pavement repair, comprising: 3 to 55 wt% of a quick hardening binder, 5 to 70 wt% of fine aggregate, 3 to 60 wt% of coarse aggregate, 0.01 to 30 wt% of a high-functional modifier, and 0.1 to 30 wt% of water. The quick hardening binder, based on 100 parts by weight of crude Portland cement, comprises: 50 to 70 parts by weight of aluminum sulfate, 20 to 40 parts by weight of lithium oxide, 20 to 40 parts by weight of boron nitride, 20 to 40 parts by weight of modified sulfur, 10 to 30 parts by weight of seaweed powder, 10 to 30 parts by weight of potassium phosphate, 10 to 30 parts by weight of gypsum, 10 to 30 parts by weight of calcium sulfoaluminate, 1 to 10 parts by weight of calcite and 1 to 10 parts by weight of chlorite. The high-functionality modifier, based on 100 parts by weight of the vinyl acetate-butyl acrylate copolymer, comprises: 50 to 70 parts by weight of polyphosphorylcholine glycol acrylate, 50 to 70 parts by weight of siloxane, 20 to 40 parts by weight of poly(3,4-dialkoxythiophene), 10 to 30 parts by weight of para-aminobenzene sulfonacetamide, 10 to 30 parts by weight of phenothiazine, 1 to 10 parts by weight of methacryloxypropyl tris(trimethylsiloxy)silane and 1 to 10 parts by weight of butylated hydroxyanisole. The present invention relates to a high-functionality quick-hardening cement concrete composition for road pavement repair with excellent strength and durability while dramatically reducing vehicle control time and construction cost by quickly repairing damaged parts of a concrete road, and to a road pavement repair method using the same.

본 발명은 도로포장 보수용 고기능성 초속경 시멘트 콘크리트 조성물로서, 초속경형 결합재 3 내지 55 중량%, 잔골재 5 내지 70 중량%, 굵은골재 3 내지 60 중량%, 고기능성 개질제 0.01 내지 30 중량% 및 물 0.1 내지 30 중량%를 포함하고, 상기 초속경형 결합재는 조강 포틀랜드 시멘트 100 중량부에 대하여, 황산알루미늄 50 내지 70 중량부, 산화리튬 20 내지 40 중량부, 질화붕소 20 내지 40 중량부, 개질유황 20 내지 40 중량부, 해조류 분말 10 내지 30 중량부, 인산칼륨 10 내지 30 중량부, 석고 10 내지 30 중량부, 칼슘설포알루미네이트 10 내지 30 중량부, 방해석 1 내지 10 중량부 및 크로라이트 1 내지 10 중량부를 포함하고; 상기 고기능성 개질제는 비닐 아세테이트-부틸 아크릴레이트 공중합체 100 중량부에 대하여, 폴리포스포릴콜린글라이콜 아크릴레이트 50 내지 70 중량부, 실록산 50 내지 70 중량부, 폴리(3,4-디알콕시티오펜) 20 내지 40 중량부, 파라아미노벤젠술폰아세트아미드 10 내지 30 중량부, 페노티아진 10 내지 30 중량부, 메타크릴옥시프로필트리스(트리메틸실록시)실란 1 내지 10 중량부 및 부틸레이티드 하이드록시아니솔 1 내지 10 중량부를 포함하여; 신속하게 콘크리트 도로의 파손부위를 복구함으로써 차량 통제 시간 및 시공 비용을 획기적으로 절감함과 동시에 강도 및 내구성 우수한 도로포장 보수용 고기능성 초속경 시멘트 콘크리트 조성물 및 이를 이용한 도로포장 보수 시공방법에 관한 것이다.