CRACK RESISTANT WATERPROOF SHEET AND WATERPROOFING METHOD USED THEREOF
The present invention relates to a crack-resistant waterproof sheet and a composite waterproofing method using the same. More specifically, the crack-resistant waterproof sheet comprises: a compound layer composed of 55-72 wt% of asphalt, 5-20 wt% of calcium carbonate, 7-15 wt% of styrene butadiene styrene (SBS) rubber, 0.1-13 wt% of silicon oxide, 0.1-8 wt% of polyethylene, 0.1-3 wt% of a curing accelerator which is an organotin compound, 0.2-2 wt% of SB latex, 0.1-8 wt% of process oil, and 5-10 wt% of polyethylene terephthalate; a nonwoven layer attached to the lower surface of the compound layer and composed of non-compressed nonwoven fabric; and a surface layer sanded with sands or silica sands on the upper surface of the compound layer. Therefore, provided are a crack-resistant waterproof sheet and a composite waterproofing method using the same, wherein waterproofing construction is performed at low or high temperatures using the waterproof sheet having excellent low-temperature flexibility, crack resistance, fatigue resistance, shear bonding strength, and tensile bonding strength to prevent the cracks, tears and breaks of the waterproof sheet even if a weighted body presses the waterproof sheet, e.g., a worker walks or a working vehicle drives on the constructed waterproof sheet before pressed concrete is cast, so a waterproof layer and a film layer can be protected stably to obtain a waterproof layer and a film layer ensured even after the construction of pressed concrete.
본 발명은 내균열성 방수시트 및 이를 이용한 복합방수공법에 관한 것으로, 더욱 상세하게는, 아스팔트 55 ~ 72 중량%, 탄산칼슘 5 ~ 20중량%, SBS고무(styrene butadiene styrene rubber) 7 ~ 15 중량%, 산화규소 0.1 ~ 13 중량%, 폴리에틸렌(Polyethylene) 0.1 ~ 8 중량%, 유기주석 화합물인 경화촉진제 0.1 ~ 3 중량%, SB LATEX 0.2 ~ 2 중량%, 프로세스오일 0.1 ~ 8 중량%, 폴리에틸렌 테레프탈레이트 5 ~ 10 중량%로 조성된 컴파운드층과; 상기 컴파운드층 하부면에 부착 형성되는 비압축 부직포로 이루어진 부직포층과; 상기 컴파운드층의 상부면에 모래 또는 규사로 샌딩처리된 표면층을 포함한다. 따라서, 저온 굴곡성, 내균열성, 내피로성, 전단 접착 강도, 인장 접착 강도가 우수한 방수시트로 저온 또는 고온에서 방수시공이 이루어지게 하여 누름콘크리트를 타설하기 전단계에서 시공된 방수시트 상부로 작업자가가 보행하거나 작업차량이 운행되는 등 중량체가 방수시트를 가압하더라도 방수시트의 균열, 찢김, 파단 현상이 방지되어 방수층 및 도막층이 안정적으로 보호될 수 있게 함으로써, 누름콘크리트 시공 후에도 보장된 방수층과 도막층을 얻을 수 있게 하는 내균열성 방수시트 및 이를 이용한 복합방수공법을 제공한다.
CRACK RESISTANT WATERPROOF SHEET AND WATERPROOFING METHOD USED THEREOF
The present invention relates to a crack-resistant waterproof sheet and a composite waterproofing method using the same. More specifically, the crack-resistant waterproof sheet comprises: a compound layer composed of 55-72 wt% of asphalt, 5-20 wt% of calcium carbonate, 7-15 wt% of styrene butadiene styrene (SBS) rubber, 0.1-13 wt% of silicon oxide, 0.1-8 wt% of polyethylene, 0.1-3 wt% of a curing accelerator which is an organotin compound, 0.2-2 wt% of SB latex, 0.1-8 wt% of process oil, and 5-10 wt% of polyethylene terephthalate; a nonwoven layer attached to the lower surface of the compound layer and composed of non-compressed nonwoven fabric; and a surface layer sanded with sands or silica sands on the upper surface of the compound layer. Therefore, provided are a crack-resistant waterproof sheet and a composite waterproofing method using the same, wherein waterproofing construction is performed at low or high temperatures using the waterproof sheet having excellent low-temperature flexibility, crack resistance, fatigue resistance, shear bonding strength, and tensile bonding strength to prevent the cracks, tears and breaks of the waterproof sheet even if a weighted body presses the waterproof sheet, e.g., a worker walks or a working vehicle drives on the constructed waterproof sheet before pressed concrete is cast, so a waterproof layer and a film layer can be protected stably to obtain a waterproof layer and a film layer ensured even after the construction of pressed concrete.
본 발명은 내균열성 방수시트 및 이를 이용한 복합방수공법에 관한 것으로, 더욱 상세하게는, 아스팔트 55 ~ 72 중량%, 탄산칼슘 5 ~ 20중량%, SBS고무(styrene butadiene styrene rubber) 7 ~ 15 중량%, 산화규소 0.1 ~ 13 중량%, 폴리에틸렌(Polyethylene) 0.1 ~ 8 중량%, 유기주석 화합물인 경화촉진제 0.1 ~ 3 중량%, SB LATEX 0.2 ~ 2 중량%, 프로세스오일 0.1 ~ 8 중량%, 폴리에틸렌 테레프탈레이트 5 ~ 10 중량%로 조성된 컴파운드층과; 상기 컴파운드층 하부면에 부착 형성되는 비압축 부직포로 이루어진 부직포층과; 상기 컴파운드층의 상부면에 모래 또는 규사로 샌딩처리된 표면층을 포함한다. 따라서, 저온 굴곡성, 내균열성, 내피로성, 전단 접착 강도, 인장 접착 강도가 우수한 방수시트로 저온 또는 고온에서 방수시공이 이루어지게 하여 누름콘크리트를 타설하기 전단계에서 시공된 방수시트 상부로 작업자가가 보행하거나 작업차량이 운행되는 등 중량체가 방수시트를 가압하더라도 방수시트의 균열, 찢김, 파단 현상이 방지되어 방수층 및 도막층이 안정적으로 보호될 수 있게 함으로써, 누름콘크리트 시공 후에도 보장된 방수층과 도막층을 얻을 수 있게 하는 내균열성 방수시트 및 이를 이용한 복합방수공법을 제공한다.
CRACK RESISTANT WATERPROOF SHEET AND WATERPROOFING METHOD USED THEREOF
내균열성 방수시트 및 이를 이용한 복합방수공법
HWANG VO GILE (author)
2021-10-07
Patent
Electronic Resource
Korean
COMPLEX WATERPROOF SHEET AND WATERPROOFING METHOD USED THEREOF
| European Patent Office | 2019
NORI WATERPROOF SHEET AND TRIPLE-LAYERD WATERPROOFING METHOD USED THEREOF
| European Patent Office | 2017
Waterproof structure, waterproof sheet and waterproofing method
| European Patent Office | 2019
WATERPROOF STRUCTURE, WATERPROOF SHEET AND WATERPROOFING METHOD
| European Patent Office | 2019
WATERPROOFING CONSTRUCTION METHOD AND COMPOSITE WATERPROOF SHEET USED THEREFOR
| European Patent Office | 2024