AN INORGANIC CERAMIC FOAM COMPOSITION WHICH CAN BE CURED AT NORMAL TEMPERATURE AND METHOD OF PREPARING THE SAME.
The present invention relates to an inorganic room-temperature-curing foam ceramic composition, and a production method thereof. The production method of the present invention includes the following steps: (1) weighing an inorganic bonding material composition comprising: 5-20 wt% of an inorganic filler, 5-20 wt% of a lightweight aggregate, 10-20 wt% of activated carbon, 40-80 wt% of an inorganic magnesium phosphate bonding material, and 0.5-10 wt% of a carbonate; (2) inserting, into a mixer, the lightweight aggregate, the activated carbon, the inorganic filler, and inorganic magnesium phosphate bonding material in sequence; (3) mixing the powder inserted in the mixer; (4) processing into slurry after adding 30-50 parts by weight of water with respect to 100 parts by weight of a uniformly mixed composition and then mixing the same thereafter; (5) inserting 0.5-11 parts by weight of the carbonate with respect to 100 parts by weight of the produced slurry; (6) injecting and generating bubbles in water while stirring the slurry mixed with the carbonate; (7) filling the material into a molding frame; (8) applying vibration onto the filled raw material for one to two seconds; (9) hardening the molded article filled in the molding frame; (10) removing the hardened and molded foam ceramic article from the molding frame; and (11) finishing the inorganic room-temperature-curing foam ceramic by curing the removed molded article.
본 발명은 마그네슘인산 시멘트를 기본 조성물로 하는 무기질 상온경화형 발포세라믹 조성물 및 그 제조방법에 관한 것으로, 본 발명의 제조방법은 아래의 단계로 구성된다. 1) 무기질 필러 5~20 중량%, 경량골재 5~20 중량%, 활성탄 10~20 중량%, 무기질 인산마그네슘 결합재 40 내지 80 중량%, 탄산염 0.5 내지 10 중량%로 구성되는 무기결합재 조성물을 각각의 용기에 저울을 이용하여 칭량하는 단계; 2) 각각 칭량된 분상원료를 경량골재→활성탄→무기질 필러→무기질인산마그네슘 결합재의 순으로 믹서기에 투입하는 단계; 3) 믹서기에 투입된 분말상을 혼합하는 단계; 4) 균일 혼합된 분말상의 조성물 100중량부에 대하여 30 내지 50중량부의 물을 투입하고 혼합하여 슬러리상으로 제조하는 단계; 5) 제조된 슬러리 100 중량부에 대하여 탄산염 0.5 내지 11 중량부를 투입하는 단계; 6) 탄산염이 혼합된 슬러리를 급격하게 교반하면서 물속에 기포를 주입하고, 탄산염이 MgO 와 PO이온과 반응하면서 초기 형태를 잃어버리고 M나 M(M=Na, K, NH, M=Ca, Mg, Ba 등) 및 CO의 형태로 분리되면서 CO가스에 의해 기포를 발생시키는 단계; 7) 발생된 기포가 소포되지 않도록 교반을 멈추고 이를 성형틀에 충진하는 단계; 8) 충진한 원료가 성형틀 곳곳에 잘 스며들 수 있도록 1~2초간 진동을 가하는 단계; 9) 성형틀에 채워진 성형물이 5~20분 이내에 경화하는 단계; 10) 경화된 발포세라믹 성형체는 30~60분의 자연경화시간 경과 후에 탈형하는 단계; 11) 탈형된 성형품을 양생하여 무기질 상온경화형 발포 세라믹을 완성하는 단계 [색인어] 발포 세라믹, 무기질, 상온경화, 마그네슘인산 시멘트, 탄산가스, 활성탄
AN INORGANIC CERAMIC FOAM COMPOSITION WHICH CAN BE CURED AT NORMAL TEMPERATURE AND METHOD OF PREPARING THE SAME.
The present invention relates to an inorganic room-temperature-curing foam ceramic composition, and a production method thereof. The production method of the present invention includes the following steps: (1) weighing an inorganic bonding material composition comprising: 5-20 wt% of an inorganic filler, 5-20 wt% of a lightweight aggregate, 10-20 wt% of activated carbon, 40-80 wt% of an inorganic magnesium phosphate bonding material, and 0.5-10 wt% of a carbonate; (2) inserting, into a mixer, the lightweight aggregate, the activated carbon, the inorganic filler, and inorganic magnesium phosphate bonding material in sequence; (3) mixing the powder inserted in the mixer; (4) processing into slurry after adding 30-50 parts by weight of water with respect to 100 parts by weight of a uniformly mixed composition and then mixing the same thereafter; (5) inserting 0.5-11 parts by weight of the carbonate with respect to 100 parts by weight of the produced slurry; (6) injecting and generating bubbles in water while stirring the slurry mixed with the carbonate; (7) filling the material into a molding frame; (8) applying vibration onto the filled raw material for one to two seconds; (9) hardening the molded article filled in the molding frame; (10) removing the hardened and molded foam ceramic article from the molding frame; and (11) finishing the inorganic room-temperature-curing foam ceramic by curing the removed molded article.
본 발명은 마그네슘인산 시멘트를 기본 조성물로 하는 무기질 상온경화형 발포세라믹 조성물 및 그 제조방법에 관한 것으로, 본 발명의 제조방법은 아래의 단계로 구성된다. 1) 무기질 필러 5~20 중량%, 경량골재 5~20 중량%, 활성탄 10~20 중량%, 무기질 인산마그네슘 결합재 40 내지 80 중량%, 탄산염 0.5 내지 10 중량%로 구성되는 무기결합재 조성물을 각각의 용기에 저울을 이용하여 칭량하는 단계; 2) 각각 칭량된 분상원료를 경량골재→활성탄→무기질 필러→무기질인산마그네슘 결합재의 순으로 믹서기에 투입하는 단계; 3) 믹서기에 투입된 분말상을 혼합하는 단계; 4) 균일 혼합된 분말상의 조성물 100중량부에 대하여 30 내지 50중량부의 물을 투입하고 혼합하여 슬러리상으로 제조하는 단계; 5) 제조된 슬러리 100 중량부에 대하여 탄산염 0.5 내지 11 중량부를 투입하는 단계; 6) 탄산염이 혼합된 슬러리를 급격하게 교반하면서 물속에 기포를 주입하고, 탄산염이 MgO 와 PO이온과 반응하면서 초기 형태를 잃어버리고 M나 M(M=Na, K, NH, M=Ca, Mg, Ba 등) 및 CO의 형태로 분리되면서 CO가스에 의해 기포를 발생시키는 단계; 7) 발생된 기포가 소포되지 않도록 교반을 멈추고 이를 성형틀에 충진하는 단계; 8) 충진한 원료가 성형틀 곳곳에 잘 스며들 수 있도록 1~2초간 진동을 가하는 단계; 9) 성형틀에 채워진 성형물이 5~20분 이내에 경화하는 단계; 10) 경화된 발포세라믹 성형체는 30~60분의 자연경화시간 경과 후에 탈형하는 단계; 11) 탈형된 성형품을 양생하여 무기질 상온경화형 발포 세라믹을 완성하는 단계 [색인어] 발포 세라믹, 무기질, 상온경화, 마그네슘인산 시멘트, 탄산가스, 활성탄
AN INORGANIC CERAMIC FOAM COMPOSITION WHICH CAN BE CURED AT NORMAL TEMPERATURE AND METHOD OF PREPARING THE SAME.
무기질 상온경화형 발포세라믹 조성물 및 그 제조방법
KIM YOUNG DO (author) / KWON EUN JA (author) / SON SE GU (author)
2015-12-02
Patent
Electronic Resource
Korean
European Patent Office | 2016
| European Patent Office | 2022
Inorganic intumescent cured foam material and preparation method thereof
| European Patent Office | 2024
A fiber-reinforced inorganic insulation foam preparing method
| European Patent Office | 2016