EXOTHERMIC GLAZE AND VESSEL SPED IT ON THE SURFACE
The present invention relates to an exothermic glaze composition for ceramics. The composition is added and mixed with 40 to 70 parts by weight of water in 100 parts by weight of a mixture mixed with 15 to 50 wt% of silicon carbide (SiC), 2 to 25 wt% of carbon, 10 to 50 wt% of petalite, 5 to 30 wt% of feldspar, 5 to 30 wt% of clay, and 2 to 7 wt% of limestone. The exothermic glaze composition has effects in manufacturing an exothermic container having excellent exothermic time for elevating the temperature and exothermic properties, for rapidly converting the same to the heat energy by applying and plasticizing the same to a heat resistant container, and absorbing the high frequency.
본 발명은 도자기용 발열 유약 조성물에 관한 것으로, 그 구성은 탄화규소(Silicon carbide, SiC) 15 내지 50중량%, 카본(Carbon) 2 내지 25중량%, 엽장석(葉長石:Petalite) 10 내지 50중량%, 장석(Feldspar) 5 내지 30중량%, 점토(Clay) 5 내지 30중량% 및 석회석(limestone) 2 내지 7중량%가 혼합된 혼합물 100중량부에 물 40 내지 70중량부를 첨가 혼합하여 조성되는 것을 특징으로 하는 것으로서, 엽장석(petalite:페타라이트), 장석, 점토, 석회석 및 도전손실 재료인 탄소계열의 탄화규소와 카본을 혼합 첨가하여 발열 유약을 조성하고, 그 발열 유약을 내열 용기에 도포 소성하여 전자 레인지에서 발산되는 고주파(2.45GHz)를 흡수하여 신속하게 열 에너지로 변환하는 우수한 발열 승온시간 및 발열 특성을 갖는 발열 용기를 제작할 수 있는 효과가 있다. 또한, 철산화물이 첨가되어 소성시 융점을 하락시켜 용기의 열충격성 및 내열특성을 저하시키는 페라이트(ferrite)를 사용하지 않고 열패창계수가 낮은 엽장석을 사용함으로, 유약이 도포 소성되는 발열 용기의 열 충격성 및 내열 특성을 강화할 수 있는 효과가 있다. 또한, 본 발명의 도자기용 발열 유약 조성물은 기존의 내열 용기를 소성하기 전에 소지의 성형품에 도포 소성하여 간편히 발열 용기로 제작할 수 있어 제품의 제작편의성뿐만 아니라, 고가 재료의 사용이 최소화되어 제품의 단가를 절감하여 제품의 가격경쟁력을 확보할 수 있는 효과가 있다.
EXOTHERMIC GLAZE AND VESSEL SPED IT ON THE SURFACE
The present invention relates to an exothermic glaze composition for ceramics. The composition is added and mixed with 40 to 70 parts by weight of water in 100 parts by weight of a mixture mixed with 15 to 50 wt% of silicon carbide (SiC), 2 to 25 wt% of carbon, 10 to 50 wt% of petalite, 5 to 30 wt% of feldspar, 5 to 30 wt% of clay, and 2 to 7 wt% of limestone. The exothermic glaze composition has effects in manufacturing an exothermic container having excellent exothermic time for elevating the temperature and exothermic properties, for rapidly converting the same to the heat energy by applying and plasticizing the same to a heat resistant container, and absorbing the high frequency.
본 발명은 도자기용 발열 유약 조성물에 관한 것으로, 그 구성은 탄화규소(Silicon carbide, SiC) 15 내지 50중량%, 카본(Carbon) 2 내지 25중량%, 엽장석(葉長石:Petalite) 10 내지 50중량%, 장석(Feldspar) 5 내지 30중량%, 점토(Clay) 5 내지 30중량% 및 석회석(limestone) 2 내지 7중량%가 혼합된 혼합물 100중량부에 물 40 내지 70중량부를 첨가 혼합하여 조성되는 것을 특징으로 하는 것으로서, 엽장석(petalite:페타라이트), 장석, 점토, 석회석 및 도전손실 재료인 탄소계열의 탄화규소와 카본을 혼합 첨가하여 발열 유약을 조성하고, 그 발열 유약을 내열 용기에 도포 소성하여 전자 레인지에서 발산되는 고주파(2.45GHz)를 흡수하여 신속하게 열 에너지로 변환하는 우수한 발열 승온시간 및 발열 특성을 갖는 발열 용기를 제작할 수 있는 효과가 있다. 또한, 철산화물이 첨가되어 소성시 융점을 하락시켜 용기의 열충격성 및 내열특성을 저하시키는 페라이트(ferrite)를 사용하지 않고 열패창계수가 낮은 엽장석을 사용함으로, 유약이 도포 소성되는 발열 용기의 열 충격성 및 내열 특성을 강화할 수 있는 효과가 있다. 또한, 본 발명의 도자기용 발열 유약 조성물은 기존의 내열 용기를 소성하기 전에 소지의 성형품에 도포 소성하여 간편히 발열 용기로 제작할 수 있어 제품의 제작편의성뿐만 아니라, 고가 재료의 사용이 최소화되어 제품의 단가를 절감하여 제품의 가격경쟁력을 확보할 수 있는 효과가 있다.
EXOTHERMIC GLAZE AND VESSEL SPED IT ON THE SURFACE
도자기용 발열 유약 조성물
PARK WON HYUN (author) / LEE YOUNG GU (author)
2016-03-03
Patent
Electronic Resource
Korean
IPC:
C04B
Kalk
,
LIME
BETONGELEMENTENS POTENTIALER: SPED MED FÖRUTSÄTTNINGAR - Kommentar
| Online Contents | 2002
Surface glaze of tableware porcelain and preparation method of surface glaze
| European Patent Office | 2024
Glaze making method capable of increasing smoothness of glaze surface
| European Patent Office | 2021