The present invention relates to a pile grouting composition comprising, based on Type 3 blast furnace slag cement, 10-100 parts by weight of ferro-nickel slag micropowder and 10-100 parts by weight of calcined dolomite. According to the present invention, free CaO and SiO_2 ingredients of ferro-nickel slag micropowder and calcined dolomite micropowder are activated by the stimulation of alkali and sulfate produced during the hydration of Type 3 blast furnace slag cement, thereby providing strength at least equal to the strength of Type 1 general cement. In addition, MgO ingredient contained in ferro-nickel slag micropowder and calcined dolomite micropowder each in an amount of 30 wt% or more is combined with compounding water (H_2O) so that it is converted into Mg(OH)_2 to realize strength while undergoing expansion. Such a volumetric expansion action is used to grout the voids in perforated ground and natural ground and prevents loss of a grouting solution caused by ground water that may exist between a perforation hole and an embedded pile. Thus, it is possible to significantly improve the tip supporting power and circumferential surface frictional force of the embedded pile as compared to the conventional grouting solution.
본 발명은 제3종 고로슬래그 시멘트 100중량부에 대하여 페로니켈 슬래그 미분말 10~100중량부와 경소백운석 미분말 10~100중량부를 포함하는 것을 특징으로 하는 말뚝 주입재 조성물에 관한 것이다. 본 발명에 따르면, 페로니켈 슬래그 미분말과 경소백운석 미분말의 유리화된 CaO, SiO성분들이 3종 고로슬래그 시멘트의 수화반응시 생성되는 알칼리 및 황산염의 자극에 의해 활성화되어 1종 보통시멘트와 동등 이상의 강도를 발현할 수 있다. 또한, 페로니켈 슬래그 미분말과 경소백운석 미분말에 각각 30중량% 이상 함유된 MgO 성분이 배합수(HO)와 만나 Mg(OH)로 전이되면서 강도를 발현하는 동시에 팽창하는 체적 팽창작용을 이용하여 천공지반과 원지반의 간극을 채워주며 천공구멍과 매입말뚝 사이에 존재할 수 있는 지하수에 의한 주입액의 유실을 방지하여 매입 말뚝의 선단지지력 및 주면마찰력을 기존 시멘트 주입액에 비하여 크게 향상시킬 수 있는 효과가 있다.
The present invention relates to a pile grouting composition comprising, based on Type 3 blast furnace slag cement, 10-100 parts by weight of ferro-nickel slag micropowder and 10-100 parts by weight of calcined dolomite. According to the present invention, free CaO and SiO_2 ingredients of ferro-nickel slag micropowder and calcined dolomite micropowder are activated by the stimulation of alkali and sulfate produced during the hydration of Type 3 blast furnace slag cement, thereby providing strength at least equal to the strength of Type 1 general cement. In addition, MgO ingredient contained in ferro-nickel slag micropowder and calcined dolomite micropowder each in an amount of 30 wt% or more is combined with compounding water (H_2O) so that it is converted into Mg(OH)_2 to realize strength while undergoing expansion. Such a volumetric expansion action is used to grout the voids in perforated ground and natural ground and prevents loss of a grouting solution caused by ground water that may exist between a perforation hole and an embedded pile. Thus, it is possible to significantly improve the tip supporting power and circumferential surface frictional force of the embedded pile as compared to the conventional grouting solution.
본 발명은 제3종 고로슬래그 시멘트 100중량부에 대하여 페로니켈 슬래그 미분말 10~100중량부와 경소백운석 미분말 10~100중량부를 포함하는 것을 특징으로 하는 말뚝 주입재 조성물에 관한 것이다. 본 발명에 따르면, 페로니켈 슬래그 미분말과 경소백운석 미분말의 유리화된 CaO, SiO성분들이 3종 고로슬래그 시멘트의 수화반응시 생성되는 알칼리 및 황산염의 자극에 의해 활성화되어 1종 보통시멘트와 동등 이상의 강도를 발현할 수 있다. 또한, 페로니켈 슬래그 미분말과 경소백운석 미분말에 각각 30중량% 이상 함유된 MgO 성분이 배합수(HO)와 만나 Mg(OH)로 전이되면서 강도를 발현하는 동시에 팽창하는 체적 팽창작용을 이용하여 천공지반과 원지반의 간극을 채워주며 천공구멍과 매입말뚝 사이에 존재할 수 있는 지하수에 의한 주입액의 유실을 방지하여 매입 말뚝의 선단지지력 및 주면마찰력을 기존 시멘트 주입액에 비하여 크게 향상시킬 수 있는 효과가 있다.
PILE GROUTING MATERIALS
말뚝 주입재 조성물
PARK WON CHUN (author)
2016-08-09
Patent
Electronic Resource
Korean
Pile bottom unscrewing grouting device of hollow pile and pile bottom grouting method
| European Patent Office | 2023
Post-grouting grouting device for bored pile and grouting method
| European Patent Office | 2022
| European Patent Office | 2015